The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite an...The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite and improve heat resistance.The effects of different calcine time on the macroscopical morphology,mass loss,phase evolution,microstructure and chemical bond evolution of MAS/BPF composites were characterized by XRD,XPS,and SEM analyses.The experimental results reveal that the increase of calcine time result in the fewer holes,relatively denser and smoother top layer of MAS/BPF composites and protect the interior from deeper decomposition.The final residues of composites are amorphous carbon and C-O-Si-Al-Mg ceramic.And MAS/BPF composites show excellent mass stability,low shrinkage and self-supporting features after 2 h holding compared with BPF composites without 40wt%of inorganic fillers.展开更多
Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） compos...Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.展开更多
基金Funded by the Joint Fund of Ministry of Education for Equipment Pre-research(Nos.6141A02022250 and SAST2018-067)。
文摘The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite and improve heat resistance.The effects of different calcine time on the macroscopical morphology,mass loss,phase evolution,microstructure and chemical bond evolution of MAS/BPF composites were characterized by XRD,XPS,and SEM analyses.The experimental results reveal that the increase of calcine time result in the fewer holes,relatively denser and smoother top layer of MAS/BPF composites and protect the interior from deeper decomposition.The final residues of composites are amorphous carbon and C-O-Si-Al-Mg ceramic.And MAS/BPF composites show excellent mass stability,low shrinkage and self-supporting features after 2 h holding compared with BPF composites without 40wt%of inorganic fillers.
文摘Fluxing agents of zinc borate, antimony oxide, galss frit A and glass frit B, with different melting or softening point temperatures, were added into MgO-Al_2O_3-SiO_2/boron phenol formaldehyde resin（MAS/BPF） composites to lower the formation temperature of eutectic liquid phase and promote the ceramification of ceramifiable composites. The effects of fluxing agents on the thermogravimetric properties, phase evolution, and microstructure evolution of MAS/BPF composites were characterized by TG-DSC, XRD and SEM analyses. The results reveal that the addition of a fluxing agent highly reduces the decomposition rate of MAS/BPF composites. Fluxing agents lower the formation temperatures of liquid phases of ceramifiable MAS/BPF composites obviously, and then promote the ceramification and densification process. The final residues of composites are ceramic surrounded by large amount of glass phases.