Chitosan is a natural biopolymer, derived from chitin, which is used for wood modification. Polyethylene glycol（PEG） was reacted with wood to provide possible fixation of the chitosan to wood. Wood blocks were treat...Chitosan is a natural biopolymer, derived from chitin, which is used for wood modification. Polyethylene glycol（PEG） was reacted with wood to provide possible fixation of the chitosan to wood. Wood blocks were treated with chitosan and PEG, as well as pre-treatment with the PEG at different temperatures and further reaction with the chitosan. The samples were soaked in water to study leaching of the chemicals, water absorption, swelling, as well as anti-swelling efficiency. Any prior reaction of the wood with PEG provided better reaction to the chitosan.Bulking was increased after the treatment of the wood with PEG. Swelling was reduced in the PEG-treated wood blocks as well as the pre-treated samples. Chitosan was not able to protect wood against water penetration： the treated samples showed more water absorption and swelling.However, pre-treatment of the samples decreased swelling in the wood, and the density was not noticeably affected by the treatments. Heating during the treatment caused more reduction in swelling for PEG–chitosan treated samples.展开更多
文摘Chitosan is a natural biopolymer, derived from chitin, which is used for wood modification. Polyethylene glycol（PEG） was reacted with wood to provide possible fixation of the chitosan to wood. Wood blocks were treated with chitosan and PEG, as well as pre-treatment with the PEG at different temperatures and further reaction with the chitosan. The samples were soaked in water to study leaching of the chemicals, water absorption, swelling, as well as anti-swelling efficiency. Any prior reaction of the wood with PEG provided better reaction to the chitosan.Bulking was increased after the treatment of the wood with PEG. Swelling was reduced in the PEG-treated wood blocks as well as the pre-treated samples. Chitosan was not able to protect wood against water penetration： the treated samples showed more water absorption and swelling.However, pre-treatment of the samples decreased swelling in the wood, and the density was not noticeably affected by the treatments. Heating during the treatment caused more reduction in swelling for PEG–chitosan treated samples.