In this paper,a new method combines chemical/physical crosslinking,and emulsification-foaming porogenic was adopted to prepare n-hydroxyapatite(n-HA)/polyvinyl alcohol(PVA)/chitosan(CS)porous composite hydrogel using ...In this paper,a new method combines chemical/physical crosslinking,and emulsification-foaming porogenic was adopted to prepare n-hydroxyapatite(n-HA)/polyvinyl alcohol(PVA)/chitosan(CS)porous composite hydrogel using artificial cornea scaffold materials.The fabricate conditions,including the type and amount of emulsification-foaming porogen,mixing time and speed etc.were researched.The results showed the optimal condition that the alkylphenol polyoxyethylene ether(OP)acted as emulsification-foaming porogen,with the ratio of WPVA/WOP as 3.75,and mixing 15 min with a stirring speed of 800 r·min-1.Additionally,the fabricated composite hydrogel scaffold materials possessed interconnected internal holes,a moisture content of above 65%,and tensile strength of above 6 MPa.In vitro cytotoxicity and acute systemic toxicity assay confirmed that the scaffolds did not show any cytotoxicity.The as-prepared hydrogel could be a promising candidate for artificial cornea scaffold material.展开更多
基金Supported by the Key Technology R&D Program of Shenzhen Municipal(JSGG20120614164013545)Basic Research Program of Shenzhen Municipal(JCYJ20130329102614715).
文摘In this paper,a new method combines chemical/physical crosslinking,and emulsification-foaming porogenic was adopted to prepare n-hydroxyapatite(n-HA)/polyvinyl alcohol(PVA)/chitosan(CS)porous composite hydrogel using artificial cornea scaffold materials.The fabricate conditions,including the type and amount of emulsification-foaming porogen,mixing time and speed etc.were researched.The results showed the optimal condition that the alkylphenol polyoxyethylene ether(OP)acted as emulsification-foaming porogen,with the ratio of WPVA/WOP as 3.75,and mixing 15 min with a stirring speed of 800 r·min-1.Additionally,the fabricated composite hydrogel scaffold materials possessed interconnected internal holes,a moisture content of above 65%,and tensile strength of above 6 MPa.In vitro cytotoxicity and acute systemic toxicity assay confirmed that the scaffolds did not show any cytotoxicity.The as-prepared hydrogel could be a promising candidate for artificial cornea scaffold material.