Strength and chloride resistance of blended Portland cement mortar containing palm oil fuel ash and fly ash

This paper presented a study on the strength and chloride resistance of mortars made with ternary blends of ordinary Portland cement （OPC）, ground palm oil fuel ash （POA）, and classified fly ash （FA）. The mortar mixtures were made with Portland cement type I containing 0-40wt% FA and POA. FA and POA with 1wt%-3wt% retained on a sieve No.325 were used. The compressive strength and rapid chloride penetration depth of mortars were determined. The results reveal that the use of ternary blended cements produces good strength mortars. The use of the blend of FA and POA also produces high strength mortars and excellent resistance to chloride penetration owing to the synergic effect of FA and POA. A mathematical analysis and two-parameter polynomial model were presented to predict the compressive strength. The mathematical model correlated well with the experimental results. The computer 3-D graphics of strength of the ternary blended mortars were also constructed and could be used to aid the understanding and the proportioning of the blended system.

Effect of Modification Treatment on Chloride Ions Permeability and Microstructure of Recycled Brick-mixed Aggregate Concrete

The modification methods of pozzolan slurry combined with sodium silicate and silicon-based additive were respectively adopted to treat recycled coarse brick-mixed aggregate(RCBA)in this study.The compressive strength and chloride permeability resistance of recycled aggregate concrete(RAC)before and after modification treatment were tested,and the microstructure of RAC was analyzed by mercury intrusion porosimetry(MIP)and scanning electron microscopy(SEM).The results show that the physical properties of RCBA strengthened by modification treatment are improved,and the compressive strength and chloride permeability resistance of treated RAC are also significantly improved.The modification treatment optimizes the pore size distribution of RAC,which increases the number of gel pores and transition pores,and decreases the number of capillary pores and macro pores.The surface fractal dimension shows a significant correlation with chloride diffusion coefficient,indicating that the variation of chloride permeability of treated RAC is consistent with the microstructure evolution.

Porosity,Pore Size Distribution and Chloride Permeability of Shotcrete Modified with Nano Particles at Early Age

Nano particles have been found to be effective in enhancing many properties of regular concretes. However, there is little information on the effect of nano particles on shotcrete. In fact, if similar positive effect of nano particles can also appear in shotcrete, they will greatly benefit the wide application of shotcrete in more and more repair and strengthening of structures in civil engineering, especially in corrosive environments. In this study, through experiments on 70 specimens, the effects of nano SiO2, CaCO3 and Al2O3 particles on the early-age porosity, pore size distribution, compressive strength and chloride permeability of shotcrete were investigated.Test results indicated that nano SiO2 particles significantly increased the compressive strength and chloride penetration resistance; nano Al2O3 and CaCO3 particles had slight enhancing effect on the compressive strength; nano CaCO3 particles were most effective in promoting the chloride penetration resistance of shotcrete. As a conclusion, nano SiO2 particles were recommended when both early age compressive strength and chloride penetration resistance were crucial, and nano CaCO3 particles were recommended when only chloride penetration resistance was concerned for their high cost-effectiveness.