Paper‑like Polyphenylene Sulfide/Aramid Fiber Electrode with Excellent Areal Capacitance and Flame‑Retardant Performance

In this paper,an aramid chopped fiber,so-called(ACF)/polyphenylene sulfide(PPS)composite,containing multi-walled carbon nanotubes(MWCNT),and in situ polymerized polypyrrole(PPy)was designed and fabricated,to be applied as a paper based electrode.The ACF/PPS/MWCNT-PPy electrode features highly porous paper-like structure with excel-lent electrochemical activity,rendering it a high areal capacitance of~3205 mF cm^(-2) at a current density of 5 mA cm^(-2).After 5000 charge-discharge cycles,the areal capacitance still maintains 93%and 70%at high current densities of 20 and 80 mA cm^(-2),respectively.Moreover,the ACF/PPS/MWCNT-PPy electrode displays over 50%the areal capacitance and maintains it's mechanical stability after annealing at 300℃.The UL-94 test reveals that the highest V-0 flame-retardant performance can be achieved.All these results suggest that the ACF/PPS/MWCNT-PPy composite is a promising material to be used as electrode for supercapacitor with high energy-storage capability and noninflammability.

Microstructural tailoring,mechanical and thermal properties of SiC composites fabricated by selective laser sintering and reactive melt infiltration

Poor flowability of printable powders and long preparation cycles are the main challenges in the selective laser sintering(SLS)of chopped carbon fiber(C_(f))reinforced silicon carbide(SiC)composites with complex structures.In this study,we develop an efficient and novel processing route in the fabrication of lightweight SiC composites via the SLS of phenolic resin(PR)and Cr powders with the addition of a-SiC particles combined with the one-step reactive melt infiltration(RMI).The effects of a-SiC addition on the microstructural evolution of the C_(f)/SiC/PR printed bodies,C_(f)/SiC/C green bodies,and derived SiC composites were investigated.The results indicate that the added a-SiC particles play an important role in enhancing the flowability of raw powders,reducing the porosity.increasing the reliability of the C/SiC/C green bodies,and contributing to improving the microstructure homogeneity and mechanical properties of the SiC composites.The maximum density,flexural strength,and fracture toughness(Kic)of the SiC composites are 2.749±0.006 g·cm^(3),266±5 MPa,and 3.30±0.06 MPa-m,respectively.The coefficient of thermal expansion(CTE,a)of the SiC composites is approximately 4.29×10^(-6)K^(-1)from room temperature(RT)to 900℃,and the thermal conductivity(x)is in the range of 80.15-92.48 W·m^(-1)·K^(-1)at RT.The high-temperature strength of the SiC composites increase to 287±18 MPa up to 1200℃.This study provides a novel as well as feasible tactic for the preparation of high-quality printable powders as well as lightweight,high-strength,and high-x SiC composites with complex structures by the SLS and RMI.