The ultra-fine chromic oxide powder was prepared by a novel gas-solid reduction reaction.Na2CrO4 was firstly reduced with hydrogen at 400-600 ℃.The obtained reduction products,mainly the mixture of NaCrO2 and sodium ...The ultra-fine chromic oxide powder was prepared by a novel gas-solid reduction reaction.Na2CrO4 was firstly reduced with hydrogen at 400-600 ℃.The obtained reduction products,mainly the mixture of NaCrO2 and sodium hydroxide（NaOH）,were converted into chromic oxide through hydrolysis followed by calcination.The obtained chromic oxide product was characterized by powder X-ray diffraction（XRD） and SEM.The results show that the hydrolysis process of sodium chromite is the key step and lower reduction temperature helps intensify the hydrolysis process.展开更多
基金Funded by the Key Program Project of the National Natural Science Foundation of China (No.50234040)the Major Project of the Knowledge Innovation Program of the Chinese Academy of Sciences (No.KCCX1-SW-22)
文摘The ultra-fine chromic oxide powder was prepared by a novel gas-solid reduction reaction.Na2CrO4 was firstly reduced with hydrogen at 400-600 ℃.The obtained reduction products,mainly the mixture of NaCrO2 and sodium hydroxide（NaOH）,were converted into chromic oxide through hydrolysis followed by calcination.The obtained chromic oxide product was characterized by powder X-ray diffraction（XRD） and SEM.The results show that the hydrolysis process of sodium chromite is the key step and lower reduction temperature helps intensify the hydrolysis process.