Marine structures are mostly made of metals and always experience complex random loading during their service periods. The fatigue crack growth behaviors of metal materials have been proved from laboratory tests to be...Marine structures are mostly made of metals and always experience complex random loading during their service periods. The fatigue crack growth behaviors of metal materials have been proved from laboratory tests to be sensitive to the loading sequence encountered. In order to take account of the loading sequence effect, fatigue life prediction should be based on fatigue crack propagation（FCP） theory rather than the currently used cumulative fatigue damage（CFD） theory. A unified fatigue life prediction（UFLP） method for marine structures has been proposed by the authors＇ group. In order to apply the UFLP method for newly designed structures, authorities such as the classification societies should provide a standardized load-time history（SLH） such as the TWIST and FALSTAFF sequences for transport and fighter aircraft. This paper mainly aims at proposing a procedure to generate the SLHs for marine structures based on a short-term loading sample and to provide an illustration on how to use the presented SLH to a typical tubular T-joint in an offshore platform based on the UFLP method.展开更多
A method for strengthening damaged tubular steel T-joints under axial compression by wrapping them with carbon fiber-reinforced polymer(CFRP)sheets was proposed and evaluated.The influence of the CFRP strengthening on...A method for strengthening damaged tubular steel T-joints under axial compression by wrapping them with carbon fiber-reinforced polymer(CFRP)sheets was proposed and evaluated.The influence of the CFRP strengthening on the failure mode and load capacity of T-joints with different degrees of damage was investigated using experiments and finite element analyses.Five T-joints were physically tested:one bare joint to obtain the peak load and corresponding displacement(D1m),two reinforced joints to provide a reference,and two pre-damaged then retrofitted joints to serve as the primary research objects.The ratio of the pre-loaded specimen chord displacement to the value of D1m was considered to be the degree of damage of the two retrofitted joints,and was set to 0.80 and 1.20.The results demonstrate that the maximum capacity of the retrofitted specimen was increased by 0.83%–15.06%over the corresponding unreinforced specimens.However,the capacity of the retrofitted specimen was 2.51%–22.77%lesser compared with that of the directly reinforced specimens.Next,111 numerical analysis models(0.63≤b≤0.76,9.70≤g≤16.92)were established to parametrically evaluate the effects of different geometric and strengthening parameters on the load capacity of strengthened tubular T-joints under different degrees of damage.The numerical analysis results revealed that the development of equivalent plastic strain at the selected measuring points was moderated by strengthening with CFRP wrapping,and indicated the optimal CFRP strengthening thickness and wrapping orientation according to tubular T-joint parameters.Finally,reasonable equations for calculating the load capacity of CFRP-strengthened joints were proposed and demonstrated to provide accurate results.The findings of this study can be used to inform improved CFRP strengthening of damaged tubular steel structures.展开更多
基金financially supported by the Fourth Term of"333 Engineering"Program of Jiangsu Province(Grant No.BRA2011116)Youth Foundation of Jiangsu Province(Grant No.BK2012095)Special Program for Hadal Science and Technology of Shanghai Ocean University(Grant No.HAST-T-2013-01)
文摘Marine structures are mostly made of metals and always experience complex random loading during their service periods. The fatigue crack growth behaviors of metal materials have been proved from laboratory tests to be sensitive to the loading sequence encountered. In order to take account of the loading sequence effect, fatigue life prediction should be based on fatigue crack propagation（FCP） theory rather than the currently used cumulative fatigue damage（CFD） theory. A unified fatigue life prediction（UFLP） method for marine structures has been proposed by the authors＇ group. In order to apply the UFLP method for newly designed structures, authorities such as the classification societies should provide a standardized load-time history（SLH） such as the TWIST and FALSTAFF sequences for transport and fighter aircraft. This paper mainly aims at proposing a procedure to generate the SLHs for marine structures based on a short-term loading sample and to provide an illustration on how to use the presented SLH to a typical tubular T-joint in an offshore platform based on the UFLP method.
基金This research work was supported and funded by Shandong Provincial Science and Technology Plan Project(No.J13LG05).
文摘A method for strengthening damaged tubular steel T-joints under axial compression by wrapping them with carbon fiber-reinforced polymer(CFRP)sheets was proposed and evaluated.The influence of the CFRP strengthening on the failure mode and load capacity of T-joints with different degrees of damage was investigated using experiments and finite element analyses.Five T-joints were physically tested:one bare joint to obtain the peak load and corresponding displacement(D1m),two reinforced joints to provide a reference,and two pre-damaged then retrofitted joints to serve as the primary research objects.The ratio of the pre-loaded specimen chord displacement to the value of D1m was considered to be the degree of damage of the two retrofitted joints,and was set to 0.80 and 1.20.The results demonstrate that the maximum capacity of the retrofitted specimen was increased by 0.83%–15.06%over the corresponding unreinforced specimens.However,the capacity of the retrofitted specimen was 2.51%–22.77%lesser compared with that of the directly reinforced specimens.Next,111 numerical analysis models(0.63≤b≤0.76,9.70≤g≤16.92)were established to parametrically evaluate the effects of different geometric and strengthening parameters on the load capacity of strengthened tubular T-joints under different degrees of damage.The numerical analysis results revealed that the development of equivalent plastic strain at the selected measuring points was moderated by strengthening with CFRP wrapping,and indicated the optimal CFRP strengthening thickness and wrapping orientation according to tubular T-joint parameters.Finally,reasonable equations for calculating the load capacity of CFRP-strengthened joints were proposed and demonstrated to provide accurate results.The findings of this study can be used to inform improved CFRP strengthening of damaged tubular steel structures.