Effects of Municipal Sewage Sludge on Fixation of Cr,Ni,Cu,and Zn during Co-processing of Heavy Metal-containing Waste in Cement Kilns

Cement raw meal with MSS and different heavy metals was blended to examine the fixation ratios, chemical species, and cement crystalline phases in clinkers. The results showed that blending MSS could decrease the fixation ratio of Cr, Ni, Cu, and Zn in the produced clinker by 5% to 25%. And Cr, Cu, and Zn were mainly incorporated into clinkers as metal silicates, Ni was mainly solubilized in Mg O to form magnesium nickel oxides, and the transition phases were mainly metal aluminum oxides as indicated by X-ray diffraction. The reduction of fixation ratios was likely attributed to the presence of impure elements, such as sodium and phosphorus in MSS. In addition, high concentrations（eg, 1.7 wt%） of chlorine in MSS led to metal chloride formation that could vaporize Cu, Cr, Ni, and Zn. To summarize, introducing MSS would decrease the fixation ratios of heavy metals due to the presence of impure elements, such as sodium and phosphorus and chlorine.

A Model for Predicting the Erosion Rate Induced by the Use of a Selective Catalytic Reduction Denitrification Technology in Cement Kilns Flue Gas

Selective catalytic reduction(SCR)is a technology by which nitrogen oxides are converted with the aid of a catalyst into diatomic nitrogen and water.It is known that the catalyst can be easily eroded if a cement kiln with a high-dust content is considered.To understand this process,numerical simulations have been carried out considering a single catalyst channel in order to study the collision and erosion of fly ash and catalysts at meso scale.Based on a response surface methodology,the effects of five factors on the erosion rate have been studied,namely,the catalyst particle velocity,the particle size,the particle concentration,the incidence angle and the catalyst porosity.The results show that the influence of particle velocity,particle size and particle concentration is statistically significant and the particle size and incidence angle have a significant effect on the erosion rate.A quadratic polynomial prediction model for the erosion rate of honeycomb catalysts in cement kiln SCR reactors is finally proposed to support the future optimization of these systems.

Plant Test of Industrial Waste Disposal in a Cement Kiln

Destruction of industrial waste in cement rotary kilns (CRKs) is an alternative technology for the treatment of certain types of industrial waste (IW). In this paper, three typical types of industrial wastes were co-incinerated in the CRK at Beijing Cement Plant to determine the effects of waste disposal (especially solid waste disposal) on the quality of clinker and the concentration of pollutants in air emission. Experimental results show that (1) waste disposal does not affect the quality of clinker and fly ash, and fly ash after the IW disposal can still be used in the cement production, (2) heavy metals from IW are immobilized and stabilized in the clinker and cement, and (3) concentration of pollutants in air emission is far below than the permitted values in the China National Standard-Air Pollutants Emission Standard (GB 16297-1996).

Increasing Plant Availability by Mechanical Checking of the Cement Rotary Kiln Axis

A periodic check of the cement rotary kiln axis is needed withinthe framework of preventive ma- intenance for maintaining high plantavailability. The fourth generation 'KAS-4' measuring system wasdevel- oped by Wuhan University of Technology in 1999. The system canbe carried out with rotating or stationary kiln plant. The same istrue of the measurement of tire and supporting roller diameters, theclearance of tires, the po- sition of rollers, the machining of tiresand rollers, the slops of roller surfaces, the deflection of gear,the axis of kiln. The system has been applied to the measurement for10 set of cement rotary kiln in China.

Improvement of geotechnical properties of sabkha soil utilizing cement kiln dust

Improvement of properties of weak soils in terms of strength,durability and cost is the key from engineering point of view.The weak soils could be stabilized using mechanical and/or chemical methods.Agents added during chemical stabilization could improve the engineering properties of treated soils.Stabilizers utilized have to satisfy noticeable performance,durability,low price,and can be easily implemented.Since cement kiln dust(CKD) is industrial by-product,it would be a noble task if this waste material could be utilized for stabilization of sabkha soil.This study investigates the feasibility of utilizing CKD for improving the properties of sabkha soil.Soil samples are prepared with 2% cement and 10%,20% or 30% CKD and are tested to determine their unconfined compressive strength(UCS),soaked California bearing ratio(CBR) and durability.Mechanism of stabilization is studied utilizing advanced techniques,such as the scanning electron microscope(SEM),energy dispersive X-ray analysis(EDX),backscattered electron image(BEI) and X-ray diffraction analysis(XRD).It is noted that the sabkha soil mixed with 2% cement and 30% CKD could be used as a sub-base material in rigid pavements.The incorporation of CKD leads to technical and economic benefits.

Present Synthesizing Situation and Application Mechanism of Hercynite in Cement Kilns

The magnesia -hercynite bricks offer a new lining to rotary cement kiln. They are well adopted and widely used in the high temperature zone of cement kiln, and have obtained good performance at rigorous and severe working conditions. The synthesis of hercynite requires a suitable atmosphere with proper O2 partial pressures which makes sure FeO can stably exist at the synthesizing temperature. Current industrial production of hercynite mainly adopts fused method. The other method, sinte- ring method, is not mature and needs further research. The magnesia - hercynite brick shows high hot toughhess, high adhesion strength to kiln crust, and good corrosion resistance to alkali salt in cement kilns. The mismatching of thermal expansion between magnesia and hercynite can improve the thermal shock resistance of the bricks, but the oxidation of partial Fe^2＋ , the high temperature solution, and low temperature exsolution of transgranular secondary spinel lead to cubical expansion, .formation of more cracks, and poor thermal shock resistance of the bricks.

A New Kind of Eco-Cement Made of Cement Kiln Dust and Granular Blast Furnace Slag

A research project wus conducted to manufacture eco-cement for sustainable development using cement kiln dust（ CKD ） and granular blast furnace slag（ GBFS ）. In the project, the burning process and minerul compositions of CKD dinker were investigated. Different minerulizers such as CaSO4 and CaF2 , sulfur and alkali corttent were coasidered. The strength of CKD and GBFS eco-cement were evaluated. The results indicate the CKD clinker can not only form ordinary cement clinker minerals such as C3 S, C2 S and C4 AF , but also form such high-reuctive minerals as C4 A3 S and C. A7 · CaF2 . The CKD and GBFS eco-cement will have the similar strength to the Portland cement grade 32.5 when blend proportion is properly applied.

Application of the Hand-instrument of Measurement of Tyre Gap and Diameter in Cement Rotary Kiln

This article is concerned with the cement rotary kiln, thehand-instrument of measurements of tyre gap and the outer diameter.The accuracy of measurements of tyre gap and diameter is less than ±1 mm. The hand-instrument wins two patents in China. It has beenapplied to the measurement for 16 sets of cement ro- Tary kiln inChina.

Modeling of Rotary Kiln in Cement Industry

Cement production is a highly energy-intensive process, and the rotary kiln is the most important part of the process. Having a comprehensive model of the kiln in order to reduce manufacturing costs, better performance can be created. In this paper, the influence processes in a simulated cement rotary kiln and operating parameters on the output of the study were to develop and validate the systems using the same batch. The followings were examined: solid phase, gas and coating temperature change in a rotary kiln.

Chrome-free Basic Refractories for Burning Zone of Cement Rotary Kiln

Based on the relevant phase diagrams of ternary system in MgO - CaO - ZrO2 - SiO2 quarternary systems, the phase diagram of Fe - O system and the condensed phase stability area diagram of iron oxides, the corrosion resistance of MgO - CaO - ZrO2 refractories to silicate cement, and the forming conditions and prepar- ing measures of hercynite are analyzed.

Hydrothermal Characteristics of Blended Cement Pastes Containing Silica Sand Using Cement Kiln Dust as an Activator

The hydrothermal reactivity of silica sand was studied using cement kiln dust (CKD) as an activator in addition to the Portland cement fraction of El-Karnak cement (a blend of ordinary Portland cement and ground sand). Autoclaved EI-Karnak cement pastes were studied at pressures of 0.507, 1.013 and 1.520 MPa of saturated steam with respect to their compressive strength, kinetics of hydrothermal reaction and the phase composition of the formed hydrates. The role of CKD in affecting the physicochemical and mechanical properties of EI-Karnak cement pastes was studied by autoclaving of several pastes containing 5, 7.5, 10 and 20% CKD at a pressure of 1.013 MPa of saturated steam. CKD was added either as a raw CKD (unwashed) or after washing with water (washed CKD). The results of these physicochemical studies obtained could be related as much as possible to the role of CKD (raw or washed) in affecting the hydrothermal reactivity of silica sand in EI-Karnak cement pastes.

A Short Communication on Refractories as Kiln Lining along Various Thermal Zones in Pre-calcining Cement Rotary Kiln

Modern cement rotary kiln is often large in size while rotating in high speed. Thermal condition within a rotary kiln is rather complex, exerting severe thermal and chemical attack on refractory of its kiln lining. In the present paper, the cause that leads to refractory failure was analyzed; requirements for refractory to overcome such failure was discussed. Composites and properties of different refractories most often used as kiln lining were assessed, including magnesia - chrome bricks, magnesia spinel bricks, dolomite bricks, silicon carbide muUite bricks and castables etc. Recommendation was made for refractories with suitable composites and properties to be used as kiln lining in each specific zone to best counteract the severe thermal conditions. A cost-effective configura- tion was presented to assemble kiln lining for rotary kiln＇s different zones in line with the regulation at JC/ T 2196-2013 ＂Specifications of refractory for cement rotary kiln＂. Chromite-free refractories with property of high endurance to thermal attack and corrosion are required to be used in modern Pre-calcining cement rotary kilns.

Corrosion of Disposing Urban Domestic Wastes on Refractories for Cement Rotary Kilns

Corrosion of burning urban domestic wastes to alkali-resistant bricks and spalling-resistant high alumina bricks was researched by static crucible method and SEM in order to choose refractories for cement rotary kilns for collaboratively disposing wastes. The result indicates that the main corrosion mechanism is slag permeation and corrosion ; the emitted high temperature gases containing alkali, sulfur and chlorine during burning the wastes re- act with refractories forming low melting point sulfate, chloride and compound salts, which metamorphose the refractories, and the loose metamorphic layer is easy to spall under thermal stress. So, corrosion resistance and spaUing resistance shall be taken into account when choosing refractories for cement rotary kilns for collaboratively disposing wastes. It is suggested that decomposition furnaces should adopt spaUing resistant high alumina bricks and anti-coating SiC castables, and preheating equipment should adopt high strength alkali-resistant bricks and castables.

Utilization of Cement Kiln Dust (CKD) with Silica Fume (SF) as a Partial Replacement of Cement in Concrete Production

This research aimed to clarify the role of by-product materials, such as CKD with SF as partial replacement by weight of cement in concrete manufacturing and inclusion on different characteristics of concrete. Concrete test specimens were mixed with 0%, 5%, 10%, 15%, 20% and 25% (CKD) with 15% (SF) as partial replacement by weight of Cement (CEM I-52.5N). Fresh concrete properties have been evaluated by workability measurement slump test. While hardened concrete properties have been evaluated by compressive, split tensile and flexural strengths tests at ages 7, 28 and 56 days, but evaluated for bond strength, modulus of elasticity and chemical composition measurement with X-Ray Fluorescence at age of 28 days. The test results have revealed that the increase of CKD amount with fixed amount of SF in concrete mixtures as partial replacement by weight of cement leads to gradual decrease of fresh concrete workability. In concrete mixtures, 20% CKD in the presence of 15% SF as partial replacement by the weight of cement are the optimum ratios which can be used without any negative effect on mechanical properties compressive, indirect tensile, flexural and bond strength at all the ages of concrete. Also modulus of elasticity and bond strength increased by 8.81% and 0.69% respectively at the age 28 days compared with control mixture.

A New Type of Cement Kiln——Annular Shaft Kiln

Annular shaft kiln invented by authors is an achievement in scientific research of Wuhan University of Technology. The invention-patent technology has been applyed recently to a φ2.2×7.7m circular shaft kiln of semi-mechnization in Tangshan National Cement Plant. The circular shaft kiln became an annular shaft kiln after a core tube was added in it as an inner annulation. This kiln has been proved to be successful in practice. It’s output after firing on 9th october 1989 has increased by 50%. The average clinker mark of over 525 has

Damage Mechanism of Silicon Carbidemullite Bricks for Transition Zone of Cement Rotary Kilns

In order to improve the service performance and explore the damage mechanism of silicon carbide-mullite bricks for the transition zone of cement rotary kilns,the phase composition and the microstructure of a used brick in the transition zone of a cement rotary kiln were analyzed by XRD,SEM and EDS.The results show that the liquid and alkali vapor phases generated by the reaction between cement materials and the silicon carbide-mullite brick mostly enter the silicon carbide-mullite brick through the pores;meanwhile,Ca+and K+in the cement penetrate through the liquid maintaining a high chemical potential energy to dissolve Al2O3 and SiO2 at the top of the liquid phase thus enhancing the phase penetration;with the decreasing temperature,crystals such as gehlenite,potassium feldspar and potassium chloride are precipitated,which destroy the original structure and increase the difference of thermal expansion coefficient between the high temperature dense end and the metamorphic layer thus resulting in cracks,spalling,and rupture.

Alkali Resistant Bricks for Cement Kiln

This standard specifies the classification, techni- cal requirements, test methods, inspection rules, marking, packing, transportation and storage of alkali resistant bricks.

Spalling Resistant Bauxite Based Bricks for Cement Kiln

1 Scope This standard specifies the term, definition, classification, labeling, technical requirements, test methods, inspection rules, packing, marking, transportation, storage, and quality certificate of spalling resistant bauxite based bricks for cement kiln.

水泥回转窑过渡带用尖晶石-方镁石-铝酸钙耐火材料的制备

水泥回转窑过渡带由于难以结窑皮和所用耐火材料热导率较高,使得窑体表面温度高,散热损失大。本工作以菱镁矿、白云石和煅烧氧化铝为原料合成了尖晶石-铝酸钙复相轻量骨料,以此为颗粒,以烧结镁砂细粉为基质制备出尖晶石-方镁石-铝酸钙耐火材料。借助扫描电子显微镜、X射线衍射仪等手段研究了合成原料物相组成对耐火材料常温物理性能、荷重软化温度和抗水泥物料侵蚀性能的影响,结果表明:利用菱镁矿、白云石和煅烧氧化铝为原料在1650℃保温4 h可以合成吸水率较低的尖晶石-铝酸钙复相轻量耐火原料。以合成尖晶石-铝酸钙复相材料为骨料可以制备出常温耐压强度较高的尖晶石-方镁石-铝酸钙耐火材料,其高强度得益于合成骨料与方镁石基质的良好结合。尖晶石-方镁石-铝酸钙耐火材料具有较好的抗水泥物料侵蚀性能,可用于水泥回转窑过渡带。