Preparation of Poly(o-toluidine)/Nano ZrO2/Epoxy Composite Coating and Its Application for Corrosion Protection of Steel

The main objective was to study the anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating.Poly（o-toluidine）/nano ZrO2 composite was prepared by in situ polymerization of o-toluidine monomer in the presence of nano ZrO2 particles.Fourier transformation infrared spectroscopy（FT-IR）,UV-visible spectroscopy（UV-vis）,X-ray diffraction（XRD）,Scanning electron microscopy（SEM）,and Thermogravimetric analysis（TGA） were used to characterize the composition and structure of the composite.Poly（o-toluidine）/nano ZrO2 composite was mixed with epoxy resin through a solution blending method and the three components poly（o-toluidine）/nano ZrO2/epoxy composite coating was coated onto the surface of steel sample by the brush coating method.The anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating on steel sample was studied by polarization curve and electrochemical impendence spectroscopy in 3.5% Na Cl solution as corrosion environment and also compared with that of poly（o-toluidine）/epoxy composite coating and pure epoxy coating.It was observed that the composite coating containing poly（otoluidine）/nano ZrO2 composite has got higher corrosion protection ability than that of poly（o-toluidine）.The electrochemical measurement results demonstrated that poly（o-toluidine） fillers improve the electrochemical anticorrosion performance of epoxy coating and the addition of nano ZrO2 particles increases the tortuosity of the diffusion pathway of corrosive substances.