Combining urea oxidation reaction(UOR) with hydrogen evolution reaction(HER) is an effective method for energy saving and highly efficient electrocatalytic hydrogen production. Herein, molybdenumincorporated cobalt ca...Combining urea oxidation reaction(UOR) with hydrogen evolution reaction(HER) is an effective method for energy saving and highly efficient electrocatalytic hydrogen production. Herein, molybdenumincorporated cobalt carbonate hydroxide nanoarrays(CoxMoyCH) are designed and synthesized as a bifunctional catalyst towards UOR and HER. Benefiting from the Mo doping, the dispersed nanoarray structure and redistributed electron density, the CoxMoyCH catalyst display outstanding catalytic performance and durability for both HER and UOR, affording the overpotential of 82 m V for HER and delivering a low potential of the 1.33 V for UOR(vs. reversible hydrogen electrode, RHE) to attain a current density of 10 m A cm^(-2), respectively. Remarkably, when CoxMoyCH was applied as bifunctional catalyst in a twoelectrode electrolyzer, a working voltage of 1.40 V is needed in urea-assisted water electrolysis at10 m A cm^(-2) and without apparent decline for 40 h, outperforming the working voltage of 1.51 V in conventional water electrolysis.展开更多
The precipitation of cobalt carbonate nanocrystals was achieved through the reaction of a pure and rich solution of cobalt sulphate (Co<sup>2+</sup>: 16.80 g/l) with a solution of carbonate solution (200 g...The precipitation of cobalt carbonate nanocrystals was achieved through the reaction of a pure and rich solution of cobalt sulphate (Co<sup>2+</sup>: 16.80 g/l) with a solution of carbonate solution (200 g/l). A surfactant was added to the reacting mixture in order to control the shape and size of generated crystallites. Two parameters were then varied <em>i.e.</em>, the weight of surfactant agent and the precipitation time in accordance with Taguchi’s L4 full experimental procedure (2<sup>2</sup>). Chemical and structural characterizations tests of the obtained precipitates were done through X-Rays Fluorescence (XRF), Scanning Electron Microscopy (SEM) and X-Rays Diffractometer (XRD);whereas the size of crystallites was assessed according to the Laue-Scherrer formula. The results obtained from the variance analysis (ANOVA) indicated an optimal size of cobalt carbonate’s crystallites of 13 nm with a cobalt content of 44.35% (equivalent to 89.45% of CoCO<sub>3</sub>) at ambient temperature under the following conditions: pH = 7;Mixing speed: 800 tr/min;Surfactant weight: 8 g;and a mixing time: 10 minutes. SEM images revealed an agglomeration of the obtained nanocrystals due to suspected drying conditions <em>i.e.</em>, drying temperature and drying atmosphere. It is suggested that the experiment should be conducted under neutral conditions at a temperature below that of cobalt carbonate’s decomposition (181.41℃).展开更多
Cobalt ferrite nanoparticles(CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition(TCVD). In this process, acetylene...Cobalt ferrite nanoparticles(CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition(TCVD). In this process, acetylene gas(C2H2) was used as a carbon source and the coating was carried out for 1, 2, or 3 h at 750℃. The Ar/C2H2 ratio was 10:1. Heating during the TCVD process resulted in a NP core size that approached 30 nm; the thickness of the shell was less than 10 nm. The composition, structure, and morphology of the fabricated composites were characterized using X-ray diffraction, simultaneous thermal analysis, transmission electron microscopy, high-resolution transmission electron microscopy, and selected-area diffraction. A vibrating sample magnetometer was used to survey the samples' magnetic properties. The deposited carbon shell substantially affected the growth and magnetic properties of the CFNPs. Micro-Raman spectroscopy was used to study the carbon coating and revealed that the deposited carbon comprised graphite, multiwalled carbon nanotubes, and diamond-like carbon. With an increase in coating time, the intensity ratio between the amorphous and ordered peaks in the Raman spectra decreased, which indicated an increase in crystallite size.展开更多
Double-exchange(DE) interaction plays an important role in electrocatalytic oxygen evolution reaction(OER).However,precise achievement of DE interaction often requires foreign dopants or vacancy engineering,leading to...Double-exchange(DE) interaction plays an important role in electrocatalytic oxygen evolution reaction(OER).However,precise achievement of DE interaction often requires foreign dopants or vacancy engineering,leading to destabilization of the catalysts and deterioration of performance.By contrast,the utilization of environmentally friendly,contactless,and continuously adjustable magnetic fields to study the OER process is profitable to avoid aforementioned interference factors and further elucidate the direct relationship_(0.5)between DE interaction and OER activity.Here,by using cobalt hydroxide carbonate(Co(OH)(CO_(3))·xH_(2)O,CoHC) nanostructures as a proof-of-concept study,external magnetic fields are carefully implemented to verify the role of DE interaction during water oxidation reaction.Detailed studies reveal that external magnetic fields effectively enhance the reaction rate of the catalyst,the overpotential decreases from 386 to 355 mV(100 mA·cm^(-2)),while Tafel slopes drastically decline from 93 to 67 mV·dec^(-1)(1.0 T).Moreover,magnetic field increment exhibits robust durability.Through in situ Raman and impedance measurements under external field,it can be found that magnetic field promotes the electron migration between Co^(2+) and Co^(3+) in the CoHC catalysts with the assistance of DE interactions,thus boosting the OER efficiency.展开更多
Mesoporous carbon-supported cobalt (Co-MC) catalysts are widely applied as electrode materials for bat- teries. Conversely, the development of Co-MC as bifunctional catalysts for application in organic catalytic rea...Mesoporous carbon-supported cobalt (Co-MC) catalysts are widely applied as electrode materials for bat- teries. Conversely, the development of Co-MC as bifunctional catalysts for application in organic catalytic reactions and degradation of water contaminants is slower. Herein, the catalyst displayed high activity in the selective oxidation of toluene to benzaldehyde under mild conditions, attaining a high selectivity of 92.3%. Factors influencing the catalytic reaction performance were also investigated. Additionally, Co-MC displayed remarkable catalytic activity in degrading dyes relative to the pure metal counterpart. Moreover, the catalyst exhibited excellent reusability, as determined by the cyclic catalytic experiments. The paper demonstrates the potential of Co-MC as a bifunctional catalyst for both toluene selective oxidation and water contaminant degradation.展开更多
CoCO_(3) with high theoretical capacity has been considered as a candidate anode for the next generation of lithium-ion batteries(LIBs).However,the electrochemical performance of CoCO_(3) itself,especially the cyclic ...CoCO_(3) with high theoretical capacity has been considered as a candidate anode for the next generation of lithium-ion batteries(LIBs).However,the electrochemical performance of CoCO_(3) itself,especially the cyclic stability at high current density,hinders its application.Herein,pure phase CoCO_(3) particles with different particle and pore sizes were prepared by adjusting the solvents(diethylene glycol,ethylene glycol,and deionized water).Among them,CoCO_(3) synthesized with diethylene glycol(DG-CC)as the solvent shows the best electrochemical performance owing to the smaller particle size and abundant mesoporous structure to maintain robust structural stability.A high specific capacity of 690.7 mAh/g after 1000 cycles was achieved,and an excellent capacity retention was presented.The capacity was contributed by diverse electrochemical reactions and the impedance of DG-CC under different cycles was further compared.Those results provide an important reference for the structural design and stable cycle performance of pure CoCO_(3).展开更多
An efficient sustainable and scalable strategy for the synthesis of porous cobalt/nitrogen co-doped carbons(Co@NCs) via pyrolysis of aniline-modified ZIFs,has been demonstrated.Aniline can coordinate and absorb on the...An efficient sustainable and scalable strategy for the synthesis of porous cobalt/nitrogen co-doped carbons(Co@NCs) via pyrolysis of aniline-modified ZIFs,has been demonstrated.Aniline can coordinate and absorb on the surface of ZIF(ZIF-CoZn3-PhA),accelerate the precipitation of ZIFs,thus resulting in smaller ZIF particle size.Meanwhile,the aniline on the surface of ZIF-CoZn3-PhA promotes the formation of the protective carbon shell and smaller Co nanoparticles,and increases nitrogen content of the catalyst.Because of these prope rties of Co@NC-PhA-3,the oxidative esterification of 5-hydroxymethylfurfural can be carried out under ambient conditions.According to our experimental and computational results,a synergistic catalytic effect between CoNx sites and Co nanoparticles has been established,in which both Co nanoparticles and CoNx can activate O2 while Co nanoparticles bind and oxidize HMF.Moreover,the formation and release of active oxygen species in CoNx sites are reinfo rced by the electronic interaction between Co nanoparticles and CoNx.展开更多
The catalytic hydrogenation of CO_(2) to multi-carbon compounds under mild conditions would not only provide value-added products, but also benefit for the reduction of CO_(2) emission if hydrogen derives from renewab...The catalytic hydrogenation of CO_(2) to multi-carbon compounds under mild conditions would not only provide value-added products, but also benefit for the reduction of CO_(2) emission if hydrogen derives from renewable energy sources. Herein, we report CoCO3 supported Ru and Pt nano-particles, which could catalyze hydrogenation of CO_(2)to produce higher hydrocarbons(C2-C26) and higher alcohols(C2OH-C6OH) at low temperatures of 80-130℃. The selectivity for C2+ compounds reached 81.1% at 80℃, which was the highest value reported so far. This work provides a promising catalyst for highly selective converting CO_(2)and H2 to C2+ compounds at low temperatures.展开更多
基金financially supported by the National Natural Science Foundation of China(52025013,22121005)the 111 Project(B12015)+1 种基金Haihe Laboratory of Sustainable Chemical Transformationsthe Fundamental Research Funds for the Central Universities。
文摘Combining urea oxidation reaction(UOR) with hydrogen evolution reaction(HER) is an effective method for energy saving and highly efficient electrocatalytic hydrogen production. Herein, molybdenumincorporated cobalt carbonate hydroxide nanoarrays(CoxMoyCH) are designed and synthesized as a bifunctional catalyst towards UOR and HER. Benefiting from the Mo doping, the dispersed nanoarray structure and redistributed electron density, the CoxMoyCH catalyst display outstanding catalytic performance and durability for both HER and UOR, affording the overpotential of 82 m V for HER and delivering a low potential of the 1.33 V for UOR(vs. reversible hydrogen electrode, RHE) to attain a current density of 10 m A cm^(-2), respectively. Remarkably, when CoxMoyCH was applied as bifunctional catalyst in a twoelectrode electrolyzer, a working voltage of 1.40 V is needed in urea-assisted water electrolysis at10 m A cm^(-2) and without apparent decline for 40 h, outperforming the working voltage of 1.51 V in conventional water electrolysis.
文摘The precipitation of cobalt carbonate nanocrystals was achieved through the reaction of a pure and rich solution of cobalt sulphate (Co<sup>2+</sup>: 16.80 g/l) with a solution of carbonate solution (200 g/l). A surfactant was added to the reacting mixture in order to control the shape and size of generated crystallites. Two parameters were then varied <em>i.e.</em>, the weight of surfactant agent and the precipitation time in accordance with Taguchi’s L4 full experimental procedure (2<sup>2</sup>). Chemical and structural characterizations tests of the obtained precipitates were done through X-Rays Fluorescence (XRF), Scanning Electron Microscopy (SEM) and X-Rays Diffractometer (XRD);whereas the size of crystallites was assessed according to the Laue-Scherrer formula. The results obtained from the variance analysis (ANOVA) indicated an optimal size of cobalt carbonate’s crystallites of 13 nm with a cobalt content of 44.35% (equivalent to 89.45% of CoCO<sub>3</sub>) at ambient temperature under the following conditions: pH = 7;Mixing speed: 800 tr/min;Surfactant weight: 8 g;and a mixing time: 10 minutes. SEM images revealed an agglomeration of the obtained nanocrystals due to suspected drying conditions <em>i.e.</em>, drying temperature and drying atmosphere. It is suggested that the experiment should be conducted under neutral conditions at a temperature below that of cobalt carbonate’s decomposition (181.41℃).
文摘Cobalt ferrite nanoparticles(CFNPs) were prepared via a reverse micelle method. The CFNPs were subsequently coated with carbon shells by means of thermal chemical vapor deposition(TCVD). In this process, acetylene gas(C2H2) was used as a carbon source and the coating was carried out for 1, 2, or 3 h at 750℃. The Ar/C2H2 ratio was 10:1. Heating during the TCVD process resulted in a NP core size that approached 30 nm; the thickness of the shell was less than 10 nm. The composition, structure, and morphology of the fabricated composites were characterized using X-ray diffraction, simultaneous thermal analysis, transmission electron microscopy, high-resolution transmission electron microscopy, and selected-area diffraction. A vibrating sample magnetometer was used to survey the samples' magnetic properties. The deposited carbon shell substantially affected the growth and magnetic properties of the CFNPs. Micro-Raman spectroscopy was used to study the carbon coating and revealed that the deposited carbon comprised graphite, multiwalled carbon nanotubes, and diamond-like carbon. With an increase in coating time, the intensity ratio between the amorphous and ordered peaks in the Raman spectra decreased, which indicated an increase in crystallite size.
基金financially supported by the Program B for Outstanding PhD Candidate of Nanjing University(No.201801B067)。
文摘Double-exchange(DE) interaction plays an important role in electrocatalytic oxygen evolution reaction(OER).However,precise achievement of DE interaction often requires foreign dopants or vacancy engineering,leading to destabilization of the catalysts and deterioration of performance.By contrast,the utilization of environmentally friendly,contactless,and continuously adjustable magnetic fields to study the OER process is profitable to avoid aforementioned interference factors and further elucidate the direct relationship_(0.5)between DE interaction and OER activity.Here,by using cobalt hydroxide carbonate(Co(OH)(CO_(3))·xH_(2)O,CoHC) nanostructures as a proof-of-concept study,external magnetic fields are carefully implemented to verify the role of DE interaction during water oxidation reaction.Detailed studies reveal that external magnetic fields effectively enhance the reaction rate of the catalyst,the overpotential decreases from 386 to 355 mV(100 mA·cm^(-2)),while Tafel slopes drastically decline from 93 to 67 mV·dec^(-1)(1.0 T).Moreover,magnetic field increment exhibits robust durability.Through in situ Raman and impedance measurements under external field,it can be found that magnetic field promotes the electron migration between Co^(2+) and Co^(3+) in the CoHC catalysts with the assistance of DE interactions,thus boosting the OER efficiency.
文摘Mesoporous carbon-supported cobalt (Co-MC) catalysts are widely applied as electrode materials for bat- teries. Conversely, the development of Co-MC as bifunctional catalysts for application in organic catalytic reactions and degradation of water contaminants is slower. Herein, the catalyst displayed high activity in the selective oxidation of toluene to benzaldehyde under mild conditions, attaining a high selectivity of 92.3%. Factors influencing the catalytic reaction performance were also investigated. Additionally, Co-MC displayed remarkable catalytic activity in degrading dyes relative to the pure metal counterpart. Moreover, the catalyst exhibited excellent reusability, as determined by the cyclic catalytic experiments. The paper demonstrates the potential of Co-MC as a bifunctional catalyst for both toluene selective oxidation and water contaminant degradation.
基金This work was supported by the National Natural Science Foundation of China(NSFC)(Nos.51772060,51372052,51672059,51621091,and 51902102)Natural Science Foundation of Hunan Province(No.2020JJ5042)Postdoctoral Science Foundation of China(No.2020M672478).
文摘CoCO_(3) with high theoretical capacity has been considered as a candidate anode for the next generation of lithium-ion batteries(LIBs).However,the electrochemical performance of CoCO_(3) itself,especially the cyclic stability at high current density,hinders its application.Herein,pure phase CoCO_(3) particles with different particle and pore sizes were prepared by adjusting the solvents(diethylene glycol,ethylene glycol,and deionized water).Among them,CoCO_(3) synthesized with diethylene glycol(DG-CC)as the solvent shows the best electrochemical performance owing to the smaller particle size and abundant mesoporous structure to maintain robust structural stability.A high specific capacity of 690.7 mAh/g after 1000 cycles was achieved,and an excellent capacity retention was presented.The capacity was contributed by diverse electrochemical reactions and the impedance of DG-CC under different cycles was further compared.Those results provide an important reference for the structural design and stable cycle performance of pure CoCO_(3).
基金the Fundamental Research Funds for the Central Universities (No.30920021120)Key Laboratory of Biomass Energy and Material,Jiangsu Province (No. JSBEM201912) for financial supporta project funded by the Priority Academic Program development of Jiangsu Higher Education Institution。
文摘An efficient sustainable and scalable strategy for the synthesis of porous cobalt/nitrogen co-doped carbons(Co@NCs) via pyrolysis of aniline-modified ZIFs,has been demonstrated.Aniline can coordinate and absorb on the surface of ZIF(ZIF-CoZn3-PhA),accelerate the precipitation of ZIFs,thus resulting in smaller ZIF particle size.Meanwhile,the aniline on the surface of ZIF-CoZn3-PhA promotes the formation of the protective carbon shell and smaller Co nanoparticles,and increases nitrogen content of the catalyst.Because of these prope rties of Co@NC-PhA-3,the oxidative esterification of 5-hydroxymethylfurfural can be carried out under ambient conditions.According to our experimental and computational results,a synergistic catalytic effect between CoNx sites and Co nanoparticles has been established,in which both Co nanoparticles and CoNx can activate O2 while Co nanoparticles bind and oxidize HMF.Moreover,the formation and release of active oxygen species in CoNx sites are reinfo rced by the electronic interaction between Co nanoparticles and CoNx.
基金This work was supported by the National Natural Science Foundation of China (Nos.91961103,21821004)the Beijing National Laboratory for Molecular Sciences,China(No.BNLMS-CXXM-202001).
文摘The catalytic hydrogenation of CO_(2) to multi-carbon compounds under mild conditions would not only provide value-added products, but also benefit for the reduction of CO_(2) emission if hydrogen derives from renewable energy sources. Herein, we report CoCO3 supported Ru and Pt nano-particles, which could catalyze hydrogenation of CO_(2)to produce higher hydrocarbons(C2-C26) and higher alcohols(C2OH-C6OH) at low temperatures of 80-130℃. The selectivity for C2+ compounds reached 81.1% at 80℃, which was the highest value reported so far. This work provides a promising catalyst for highly selective converting CO_(2)and H2 to C2+ compounds at low temperatures.