Fischer–Tropsch synthesis on impregnated cobalt-based catalysts:New insights into the effect of impregnation solutions and pH value

The Co-based catalysts were prepared with different cobalt acetate solutions. Effects of pH value were studied deeply on Fischer–Tropsch synthesis (FTS) through a semi-batch reactor. Among all impregnation solutions (water, butanol, amyl alcohol, acetic acid, nitric acid and ammonium nitrate), the catalyst prepared by NH4NO3solution showed the highest catalytic activity due to its small particle size and high reduction degree. However, the catalyst with the smallest particle size derived from water as impregnation solution exhibited low activity as well as high methane selectivity since it was difficult to be reduced and inactive in FTS. According to FT-IR spectra results, the low intensity of absorbed CO on the catalyst prepared from water solution resulted in low FTS activity. Whereas, the high activity of catalysts prepared from NH4NO3solution could be explained by the high intensity of absorbed CO on the catalysts. The cobalt species on the catalysts prepared under lower pH conditions exhibited smaller particle size distribution as well as lower CO conversion than those prepared at higher pH value. ? 2016 Science Press

Fischer-Tropsch Synthesis over Alumina- Supported Cobalt-Based Catalysts: Effect of Support Variables

Different kinds of aluminum precursors were obtained from precipitating ammonium bicarbonate, ammonium carbonate, and saturated ammonium bicarbonate, then, boehmite (AlO(OH)), ammonium alumina carbonate hydroxide (AACH) and their mixture were obtained, and then, different kinds of alumina were obtained after calcination. Three catalysts supported on the different alumina were obtained via impregnating cobalt and ruthenium by incipient wetness. The effects of different precipitants on composition of precursors were?studied by XRD, FTIR, and TGA. The property and structure of alumina were studied by XRD and BET. The supported catalysts were studied by characterizations of XRD and H2-TPR, and the catalytic performance for Fischer-Tropsch synthesis (FTS) were evaluated at a fix-bed reactor. The relations among the composition of precursors, the property of alumina and the catalytic performance of supported catalysts were researched thoroughly.

Nanosized cobalt-based catalyst prepared by supercritical phase condition for Fischer-Tropsch synthesis

A series of nanosized Co/Zn/Mn/K composite catalysts for Fischer-Tropsch synthesis （FTS） were prepared by supercritical fluid drying （SCFD） method and common drying （CD） method. The nanosized cobalt-based catalysts were characterized by XRD, TEM and BET techniques. Their catalytic performances were tested in a slurry-bed reactor under FTS reaction conditions. The drying and crystallization were carried out simultaneously during SCFD, therefore, the catalysts prepared by SCFD method have ideal structure and show the FTS performance superior to the others prepared by CD method. The FTS activity and selectivity were improved via adding Zn, Mn and K promoters, and less CH4 and CO2 as well as higher yield of C5＋ products were achieved. The optimal performance of a 92% CO conversion and a 65% C5＋ product yield was obtained over a catalyst with the component of Co/Zn/Mn/K = 100/50/10/7. Furthermore, the catalytic performance was studied under the conditions of liquid-phase and supercritical phase slurry-bed, and C5＋ product yield were 57.4% and 65.4%, respectively. In summary, better catalytic performance was obtained using the nanosized catalyst prepared by SCFD method under supercritical reaction conditions, resulting in higher conversion of CO, less CO2 byproduct, and higher yield of C5＋ products.

An Electrocatalytic Strategy for Dehydrogenative[4+2]Cycloaddition over a Cobalt-Based Catalyst

Exploring the anodic reaction to substitute conventional oxygen evolution reaction(OER)for the synthesis of complex pharmaceutical molecules is highly attractive.Here,we report an electrocatalytic strategy for dehydrogenative[4+2]cycloaddition of N,N-dialkylanilines with maleimides via dual functionalization of both C(sp3)-H and C(sp2)-H bonds,by using an electrochemically activated cobalt carbonate hydroxide hydrate supported on carbon cloth(CCHH-A/CC),affording various tetrahydroquinolines with high yields.This electrochemical transformation proceeds with high activity and stability,as well as good substrate compatibility.Mechanism study shows thatα-aminoalkyl radical exists in the electrooxidation reaction.This strategy shows significant potential for the synthesis of valuable chemicals by using an electrocatalytic strategy.

光学体表成像设备Catalyst的故障维修案例及日常保养方法

本文介绍了光学体表成像设备Catalyst HD的工作原理,以及处理常见的硬件和软件故障的方法,并提供了日常维护保养方法。其中,对于硬件故障,利用Catalyst HD系统的MutilZsn软件来判断Catalyst投影器和摄像头故障,对于软件故障方面,探讨了Catalyst HD系统在医用直线加速器上常见的Authorization Pending联锁问题的触发原因。本文为科室更好地开展光学体表引导放疗技术,高效地运用好设备提供参考意见。

Cobalt-based multicomponent nanoparticles supported on N-doped graphene as advanced cathodic catalyst for zinc-air batteries

To improve the efficiency of cathodic oxygen reduction reaction(ORR)in zinc-air batteries(ZABs),an adsorption-complexation-calcination method was proposed to generate cobalt-based multicomponent nanoparticles comprising Co,Co_(3)O_(4)and CoN,as well as numerous N heteroatoms,on graphene nanosheets(Co/Co_(3)O_(4)/CoN/NG).The Co/Co_(3)O_(4)/CoN nanoparticles with the size of less than 50 nm are homogeneously dispersed on N-doped graphene(NG)substrate,which greatly improve the catalytic behaviors for ORR.The results show that the half-wave potential is as high as 0.80 V vs.RHE and the limiting current density is 4.60 mA·cm^(−2),which are close to those of commercially available platinum/carbon(Pt/C)catalysts.Applying as cathodic catalyst for ZABs,the battery shows large specific capacity and open circuit voltage of 843.0 mAh∙g^(−1) and 1.41 V,respectively.The excellent performance is attributed to the efficient two-dimensional structure with high accessible surface area and the numerous multiple active sites provided by highly scattered Co/Co_(3)O_(4)/CoN particles and doped nitrogen on the carbon matrix.

Cobalt-Based Cocatalysts for Photocatalytic CO_(2)Reduction

Conversion of carbon dioxide(CO_(2))into valuable chemicals and renewable fuels via photocatalysis represents an eco-friendly route to achieve the goal of carbon neutralization.Although various types of semiconductor materials have been intensively explored,some severe issues,such as rapid charge recombination and sluggish redox reaction kinetics,remain.In this regard,cocatalyst modifi cation by trapping charges and boosting surface reactions is one of the most effi cient strategies to improve the effi ciency of semiconductor photocatalysts.This review focuses on recent advances in CO_(2)photoreduction over costeff ective and earth-abundant cobalt(Co)-based cocatalysts,which are competitive candidates of noble metals for practical applications.First,the functions of Co-based cocatalysts for promoting photocatalytic CO_(2)reduction are briefl y discussed.Then,diff erent kinds of Co-based cocatalysts,including cobalt oxides and hydroxides,cobalt nitrides and phosphides,cobalt sulfi des and selenides,Co single-atom,and Co-based metal–organic frameworks(MOFs),are summarized.The underlying mechanisms of these Co-based cocatalysts for facilitating CO_(2)adsorption–activation,boosting charge separation,and modulating intermediate formation are discussed in detail based on experimental characterizations and density functional theory calculations.In addition,the suppression of the competing hydrogen evolution reaction using Co-based cocatalysts to promote the product selectivity of CO_(2)reduction is highlighted in some selected examples.Finally,the challenges and future perspectives on constructing more effi cient Co-based cocatalysts for practical applications are proposed.

Catalytic effect in lithium metal batteries: From heterogeneous catalyst to homogenous catalyst

Lithium metal batteries are regarded as prominent contenders to address the pressing needs owing to the high theoretical capacity.Toward the broader implementation,the primary obstacle lies in the intricate multi-electron,multi-step redox reaction associated with sluggish conversion kinetics,subsequently giving rise to a cascade of parasitic issues.In order to smooth reaction kinetics,catalysts are widely introduced to accelerate reaction rate via modulating the energy barrier.Over past decades,a large amount of research has been devoted to the catalyst design and catalytic mechanism exploration,and thus the great progress in electrochemical performance has been realized.Therefore,it is necessary to make a comprehensive review toward key progress in catalyst design and future development pathway.In this review,the basic mechanism of lithium metal batteries is provided along with corresponding advantages and existing challenges detailly described.The main catalysts employed to accelerate cathode reaction with emphasis on their catalytic mechanism are summarized as well.Finally,the rational design and innovative direction toward efficient catalysts are suggested for future application in metal-sulfur/gas battery and beyond.This review is expected to drive and benefit future research on rational catalyst design with multi-parameter synergistic impacts on the activity and stability of next-generation metal battery,thus opening new avenue for sustainable solution to climate change,energy and environmental issues,and the potential industrial economy.

Fullerenes and derivatives as electrocatalysts: Promises and challenges

Carbon-based metal-free nanomaterials are promising alternatives to precious metals as electrocatalysts of key energy storage and conversion technologies.Of paramount significance are the establishment of design principles by understanding the catalytic mechanisms and identifying the active sites.Distinct from sp2-conjugated graphene and carbon nanotube,fullerene possesses unique characteristics that are growingly being discovered and exploited by the electrocatalysis community.For instance,the well-defined atomic and molecular structures,the good electron affinity to tune the electronic structures of other substances,the intermolecular self-assembly into superlattices,and the on-demand chemical modification have endowed fullerene with incomparable advantages as electrocatalysts that are otherwise not applicable to other carbon ma-terials.As increasing studies are being reported on this intriguing topic,it is necessary to provide a state-of-the-art overview of the recent progress.This review takes such an initiative by summarizing the promises and challenges in the electrocatalytic applications of fullerene and its derivatives.The content is structured according to the composition and structure of fullerene,including intact fullerene(e.g.,fullerene composite and superlattices)and fullerene derivatives(e.g.,doped,endohedral,and disintegrated fullerene).The synthesis,characterization,catalytic mechanisms,and deficiencies of these fullerene-based materials are explicitly elaborated.We conclude it by sharing our perspectives on the key aspects that future efforts shall consider.

Efficient and stable PtFe alloy catalyst for electrocatalytic methanol oxidation with high resistance to CO

Direct methanol fuel cells(DMFC) are widely considered to be an ideal green energy conversion device but their widespread applications are limited by the high price of the Pt-based catalysts and the instability in terms of surface CO toxicity in long-term operation.Herein,the PtFe alloy nanoparticles(NPs) with small particle size(~4.12 nm) supported on carbon black catalysts with different Pt/Fe atomic ratios(Pt_(1)Fe_(2)/C,Pt_(3)Fe_(4)/C,Pt_(1)Fe_(1)/C,and Pt_(2)Fe_(1)/C) are successfully prepared for enhanced anti-CO poisoning during methanol oxidation reaction(MOR).The optimal atomic ratio of Pt/Fe for the MOR is 1:2,and the mass activity of Pt_(1)Fe_(2)/C(5.40 A mg_(Pt)^(-1)) is 13.5 times higher than that of conventional commercial Pt/C(Pt/C-JM)(0.40 A mg_(Pt)^(-1)).The introduction of Fe into the Pt lattice forms the PtFe alloy phase,and the electron density of Pt is reduced after forming the PtFe alloy.In-situ Fourier transform infrared results indicate that the addition of oxyphilic metal Fe has reduced the adsorption of reactant molecules on Pt during the MOR.The doping of Fe atoms helps to desorb toxic intermediates and regenerate Pt active sites,promoting the cleavage of C-O bonds with good selectivity of CO_(2)(58.1%).Moreover,the Pt_(1)Fe_(2)/C catalyst exhibits higher CO tolerance,methanol electrooxidation activity,and long-term stability than other Pt_(x)Fe_(y)/C catalysts.

Catalyst光学体表监测在左侧乳腺癌ABC-DIBH放射治疗中的应用

目的 探讨在应用主动呼吸控制(Active Breathing Control,ABC)技术的左侧乳腺癌深吸气屏气(Deep Inspiration Breath Hold,DIBH)放疗中,使用光学体表追踪技术监测屏气的有效性和体位的重复性效果,以保证患者在放疗中吸气方式一致和体位不变,提高放射治疗的精确性。方法 选取应用ABC技术放疗的23例左侧乳腺癌患者为研究对象,以Catalyst进行治疗中DIBH体位监测,以分次内锥形束计算机断层扫描(Cone Beam Computed Tomography,CBCT)为参考标准,分别记录二者误差数据,应用Pearson法和Bland-Altman法分别评估两组误差的相关性和两种系统的一致性。将光学体表监测值与CBCT配准误差值之间的差值定义为Catalyst体表监测精度。结果 Catalyst监测在左右(x轴)方向、头脚(y轴)方向和前后(z轴)方向误差分别为(0.08±1.04)、(1.44±2.15)、(0.45±1.69)mm,CBCT配准误差分别为(0.15±1.15)、(1.51±2.28)、(0.44±1.81)mm。x轴方向和z轴方向相关系数r值分别为0.60、0.77,呈强相关;y轴方向r值为0.82,呈极强相关。二者95%CI值在x、y与z轴方向分别为[-2.01,1.86]、[-2.69,2.57]、[-2.32,2.34] mm,Catalyst监测精度在x、y、z轴方向分别为(-0.08±0.99)、(-0.06±1.34)、(0.01±1.19)mm。结论 Catalyst可有效监测使用ABC进行治疗左侧乳腺癌患者的屏气状态,能准确且实时监测患者位置,提高治疗精确度,具有临床应用价值。

Efficient Direct Decomposition of NO over La_(0.8)A_(0.2)NiO_(3)(A=K, Ba, Y) Catalysts under Microwave Irradiation

La_(0.8)A_(0.2)NiO_(3) (A=K,Ba,Y) catalysts supported on the microwave-absorbing ceramic heating carrier were prepared by the sol-gel method.The crystalline phase and the catalytic activity of the La_(0.8)A_(0.2)NiO_(3)catalysts were characterized by XRD and H_(2) temperature-programmed reduction (TPR).The effects of reaction temperature,oxygen concentration,and gas flow rate on the direct decomposition of nitric oxide over the synthesized catalysts were studied under microwave irradiation (2.45 GHz).The XRD results indicated that the La_(0.8)A_(0.2)NiO_(3) catalysts formed an ABO_(3) perovskite structure,and the H_(2)-TPR results revealed that the relative reducibility of the catalysts increased in the order of La_(0.8)K_(0.2)NiO_(3)>La_(0.8)Ba_(0.2)NiO_(3)>La_(0.8)Y_(0.2)Ni O_(3).Under microwave irradiation,the highest NO conversion amounted to 98.9%,which was obtained with the La_(0.8)K_(0.2)NiO_(3) catalyst at 400℃.The oxygen concentration did not inhibit the NO decomposition on the La_(0.8)A_(0.2)NiO_(3) catalysts,thus the N_(2) selectivity exceeded 99.8%under excess oxygen at 550℃.The NOconversion of the La_(0.8)A_(0.2)NiO_(3) catalysts decreased linearly with the increase in the gas flow rate.

An effective catalyst carrier SiO_(2):Enhancing catalytic and combustion properties of CuFe_(2)O_(4)on energetic components

To enhance the catalytic activity of copper ferrite(CuFe_(2)O_(4))nanoparticle and promote its application as combustion catalyst,a low-cost silicon dioxide(SiO_(2))carrier was employed to construct a novel CuFe_(2)O_(4)/SiO_(2)binary composites via solvothermal method.The phase structure,morphology and catalytic activity of CuFe_(2)O_(4)/SiO_(2)composites were studied firstly,and thermal decomposition,combustion and safety performance of ammonium perchlorate(AP)and 1,3,5-trinitroperhydro-1,3,5-triazine(RDX)with it affecting were then systematically analyzed.The results show that CuFe_(2)O_(4)/SiO_(2)composite can remarkably either advance the decomposition peak temperature of AP and RDX,or reduce the apparent activation energy at their main decomposition zone.Moreover,the flame propagation rate of RDX was promoted by about 2.73 times with SiO_(2)content of 3 wt%,and safety property of energetic component was also improved greatly,in which depressing the electrostatic discharge sensitivity of pure RDX by about 1.89 times.In addition,the effective range of SiO_(2)carrier content in the binary catalyst is found to be 3 to 5 wt%.Therefore,SiO_(2)opens a new insight on the design of combustion catalyst carrier and will promote the application of CuFe_(2)O_(4)catalyst in solid propellant.

100 W-class green hydrogen production from ammonia at a dual-layer electrode containing a Pt-Ir catalyst for an alkaline electrolytic process

Ammonia allows storage and transport of hydrogen over long distances and is an attractive potential hydrogen carrier.Electrochemical decomposition has recently been used for the conversion of ammonia to hydrogen and is regarded as a future technology for production of CO_(2)-free pure hydrogen.Herein,a heterostructural Pt-Ir dual-layer electrode is developed and shown to achieve successful long-term operation in an ammonia electrolyzer with an anion exchange membrane(AEM).This electrolyzer consisted of eight membra ne electrode assemblies(MEAs)with a total geometric area of 200 cm~2 on the anode side,which resulted in a hydrogen production rate of 25 L h~(-1).We observed the degradation in MEA performance attributed to changes in the anode catalyst layer during hydrogen production via ammonia electrolysis.Furthermore,we demonstrated the relationship between the ammonia oxidation reaction(AOR)and the oxygen evolution reaction(OER).

Enhanced stability of nitrogen-doped carbon-supported palladium catalyst for oxidative carbonylation of phenol

Enhancing the stability of supported noble metal catalysts emerges is a major challenge in both science and industry.Herein,a heterogeneous Pd catalyst(Pd/NCF)was prepared by supporting Pd ultrafine metal nanoparticles(NPs)on nitrogen-doped carbon;synthesized by using F127 as a stabilizer,as well as chitosan as a carbon and nitrogen source.The Pd/NCF catalyst was efficient and recyclable for oxidative carbonylation of phenol to diphenyl carbonate,exhibiting higher stability than Pd/NC prepared without F127 addition.The hydrogen bond between chitosan(CTS)and F127 was enhanced by F127,which anchored the N in the free amino group,increasing the N content of the carbon material and ensuring that the support could provide sufficient N sites for the deposition of Pd NPs.This process helped to improve metal dispersion.The increased metal-support interaction,which limits the leaching and coarsening of Pd NPs,improves the stability of the Pd/NCF catalyst.Furthermore,density functional theory calculations indicated that pyridine N stabilized the Pd^(2+)species,significantly inhibiting the loss of Pd^(2+)in Pd/NCF during the reaction process.This work provides a promising avenue towards enhancing the stability of nitrogen-doped carbon-supported metal catalysts.

Realizing methanol synthesis from CO and water via the synergistic effect of Cu^(0)/Cu^(+)over Cu/ZrO_(2) catalyst

The optimizing utilization of ca rbon resources has drawn wide attention all over the world,while exploiting the high-efficiency catalytic routes remains a challenge.Here,a direct methanol synthesis route is realized from pure CO and H_(2)O over 10%Cu/t-ZrO_(2) catalyst,where the time yield of methanol is144.43 mmol mol_(Cu)^(-1)h^(-1)and the methanol selectivity in hydrocarbons is 100%,The Cu species highly dispersed in the t-ZrO_(2) support lead parts of them in the cationic state.The Cu^(+)sites contribute to the dissociation of H_(2)O,providing the H*source for methanol synthesis,while the formed Cu^(0) sites promote the absorption and transfer of H*during the reaction.Moreover,the H_(2)O is even a better H resource than H_(2) due to its better dissociation effectivity in this catalytic system.The present work offers a new approach for methanol synthesis from CO and new insight into the process of supplying H donor.

Preparation of Modified UiO-66 Catalyst and Its Catalytic Performance for NH_(3)-SCR Denitration

Zirconium-based metal-organic framework UiO-66 was successfully prepared by solvothermal method,and UiO-66 was modified by adding regulators such as formic acid,acetic acid,and hydrochloric acid.The NH_(3)-SCR reactivity of the samples was evaluated by the denitration activity evaluation system,and the UiO-66 and the regulator-modified UiO-66 were characterized by XRD,SEM,BET,FTIR,TG,NH_(3)-TPD,etc.,the effects of regulator types on the structure and properties of UiO-66 were investigated.The experimental results show that,after adding the modifier,the morphology of UiO-66 changes from irregular quadrilateral with serious agglomeration to particles with regular crystal shape and good dispersibility,and the crystal morphology of the catalyst is improved.In addition,after adding the modifier,UiO-66 has a larger specific surface area and stronger surface acidity,which optimizes the catalytic performance of UiO-66.The catalytic performance test results of NH_(3)-SCR show that the low-temperature activity of UiO-66 is poor,and it only shows a certain catalytic activity at higher temperatures.The catalytic activity of UiO-66 was significantly improved after adding the regulator.Among them,the UiO-66-HCl modified with hydrochloric acid had the best catalytic activity,and the denitration rate reached 70%when the denitration temperature was 380℃.

Single-atom catalysts for the electrochemical reduction of carbon dioxide into hydrocarbons and oxygenates

The electrochemical reduction of carbon dioxide offers a sound and economically viable technology for the electrification and decarbonization of the chemical and fuel industries.In this technology,an electrocatalytic material and renewable energy-generated electricity drive the conversion of carbon dioxide into high-value chemicals and carbon-neutral fuels.Over the past few years,single-atom catalysts have been intensively studied as they could provide near-unity atom utilization and unique catalytic performance.Single-atom catalysts have become one of the state-of-the-art catalyst materials for the electrochemical reduction of carbon dioxide into carbon monoxide.However,it remains a challenge for single-atom catalysts to facilitate the efficient conversion of carbon dioxide into products beyond carbon monoxide.In this review,we summarize and present important findings and critical insights from studies on the electrochemical carbon dioxide reduction reaction into hydrocarbons and oxygenates using single-atom catalysts.It is hoped that this review gives a thorough recapitulation and analysis of the science behind the catalysis of carbon dioxide into more reduced products through singleatom catalysts so that it can be a guide for future research and development on catalysts with industry-ready performance for the electrochemical reduction of carbon dioxide into high-value chemicals and carbon-neutral fuels.

Boosting Fischer-Tropsch Synthesis via Tuning of N Dopants in TiO_(2)@CN-Supported Ru Catalysts

Nitrogen(N)-doped carbon materials as metal catalyst supports have attracted signifi cant attention,but the eff ect of N dopants on catalytic performance remains unclear,especially for complex reaction processes such as Fischer-Tropsch synthesis(FTS).Herein,we engineered ruthenium(Ru)FTS catalysts supported on N-doped carbon overlayers on TiO_(2)nanoparticles.By regulating the carbonization temperatures,we successfully controlled the types and contents of N dopants to identify their impacts on metal-support interactions(MSI).Our fi ndings revealed that N dopants establish a favorable surface environment for electron transfer from the support to the Ru species.Moreover,pyridinic N demonstrates the highest electron-donating ability,followed by pyrrolic N and graphitic N.In addition to realizing excellent catalytic stability,strengthening the interaction between Ru sites and N dopants increases the Ru^(0)/Ru^(δ+)ratios to enlarge the active site numbers and surface electron density of Ru species to enhance the strength of adsorbed CO.Consequently,it improves the catalyst’s overall performance,encompassing intrinsic and apparent activities,as well as its ability for carbon chain growth.Accordingly,the as-synthesized Ru/TiO_(2)@CN-700 catalyst with abundant pyridine N dopants exhibits a superhigh C_(5+)time yield of 219.4 mol CO/(mol Ru·h)and C_(5+)selectivity of 85.5%.

Elucidating the structure-activity relationship of Cu-Ag bimetallic catalysts for electrochemical CO_(2) reduction

Developing bimetallic catalysts is an effective strategy for enhancing the activity and selectivity of electrochemical CO_(2) reduction reactions,where understanding the structure-activity relationship is essential for catalyst design.Herein,we prepared two Cu-Ag bimetallic catalysts with Ag nanoparticles attached to the top or the bottom of Cu nanowires.When tested in a flow cell,the Cu-Ag catalyst with Ag nanoparticles on the bottom achieved a faradaic efficiency of 54%for ethylene production,much higher than the catalyst with Ag nanoparticles on the top.The catalysts were further studied in the H-cell and zero-gap MEA cell.It was found that placing the two metals in the intensified reaction zone is crucial to triggering the tandem reaction of bimetallic catalysts.Our work elucidates the structure-activity relationship of bimetallic catalysts for CO_(2) reduction and demonstrates the importance of considering both catalyst structures and cell characteristics to achieve high activity and selectivity.