According to the mass action law and the coexistence theory of slagstructure, the calculating models of mass action concentration for CaO-MgO-FeO-Fe_2O_3-SiO_2,CaO-MgO-MnO-FeO-Fe_2O_3-P_2O_5-SiO_2 and CaO-MgO-MnO-FeO-...According to the mass action law and the coexistence theory of slagstructure, the calculating models of mass action concentration for CaO-MgO-FeO-Fe_2O_3-SiO_2,CaO-MgO-MnO-FeO-Fe_2O_3-P_2O_5-SiO_2 and CaO-MgO-MnO-FeO-Fe_2O_3-Al_2O_3-P_2O_5-SiO_2 slag melts areformulated and sulphur distribution between the slag melts and liquid iron is treated. It is foundthat CaO, MnO and FeO promote desulphurization, while MgO is detrimental to desulphurization. Inaddition, the sulphur distribution coefficients between the slag melts and liquid iron andpresented.展开更多
According to the law of mass action and the coexistence theory of slag structure, the distribution of manganese between MnO FeO SiO 2 and MgO MnO FeO SiO 2 slag melts as well as liquid iron was analyzed. It is shown t...According to the law of mass action and the coexistence theory of slag structure, the distribution of manganese between MnO FeO SiO 2 and MgO MnO FeO SiO 2 slag melts as well as liquid iron was analyzed. It is shown that K ′ Mn and K MnO are only dependent on temperature and don’t change with basicities and compositions of slag melts. So the distribution of manganese between the above mentioned slag melts and molten iron obeys the law of mass action. But analysis of experimental results from other sources shows that K ′ Mn and K MnO really change with basicities of slag, which is probably arisen from not approaching equilibrium under low basicity slag melts.展开更多
文摘According to the mass action law and the coexistence theory of slagstructure, the calculating models of mass action concentration for CaO-MgO-FeO-Fe_2O_3-SiO_2,CaO-MgO-MnO-FeO-Fe_2O_3-P_2O_5-SiO_2 and CaO-MgO-MnO-FeO-Fe_2O_3-Al_2O_3-P_2O_5-SiO_2 slag melts areformulated and sulphur distribution between the slag melts and liquid iron is treated. It is foundthat CaO, MnO and FeO promote desulphurization, while MgO is detrimental to desulphurization. Inaddition, the sulphur distribution coefficients between the slag melts and liquid iron andpresented.
文摘According to the law of mass action and the coexistence theory of slag structure, the distribution of manganese between MnO FeO SiO 2 and MgO MnO FeO SiO 2 slag melts as well as liquid iron was analyzed. It is shown that K ′ Mn and K MnO are only dependent on temperature and don’t change with basicities and compositions of slag melts. So the distribution of manganese between the above mentioned slag melts and molten iron obeys the law of mass action. But analysis of experimental results from other sources shows that K ′ Mn and K MnO really change with basicities of slag, which is probably arisen from not approaching equilibrium under low basicity slag melts.