The effects of gas composition, temperature, ore to coke ratio and prereduction rate of ore on coke degradation were studied. The results showed that 1% increment in solution loss of coke reduces coke strength by 0.6%...The effects of gas composition, temperature, ore to coke ratio and prereduction rate of ore on coke degradation were studied. The results showed that 1% increment in solution loss of coke reduces coke strength by 0.6%, and the coke degradation is accelerated with the temperature. The higher the temperature, the more coke surface is involved in reactions, and the less negative effect on coke strength is. Hydrogen exerts stronger effect on coke degradation than CO at high temperature. The coke degradation is decreased with the reduction of ore to coke ratio and increase of ore prereduction rate.展开更多
The pore structure of coke under CO2 atmosphere was investigated by the carbon solution-loss reaction experiment.The results show that the pore size distribution of coke gradually changes from dispersion to relative c...The pore structure of coke under CO2 atmosphere was investigated by the carbon solution-loss reaction experiment.The results show that the pore size distribution of coke gradually changes from dispersion to relative concentration with the increase in carbon loss rate,but it tends to be dispersed again in the late stage of the reaction,and the pore volume and specific surface area also increase first and then decrease with the increase in carbon loss rate.Scanning electron microscopy results show that the evolution of coke pores is from the formation of micropores to the expansion of micropores,and finally the micropore and mesopores collapse to form a large number of string holes.The chemical bonds and functional groups of different reacted cokes were analyzed by Fourier-transform infrared spectroscopy.Furthermore,the microstructure of reacted cokes was analyzed by optical microscopy,and then the ordering of the affinity of different microstructures with CO2 was given.The volume hypothesis which was the theory about energy size of comminution was adopted to analyze the degradation behavior of reacted cokes.The breakage energy of reacted cokes was calculated by volume hypothesis,and the power consumption coefficient CK of different reacted cokes was determined by drum experiment,and then the degradation behavior of reacted cokes under different power consumptions was predicted.展开更多
文摘The effects of gas composition, temperature, ore to coke ratio and prereduction rate of ore on coke degradation were studied. The results showed that 1% increment in solution loss of coke reduces coke strength by 0.6%, and the coke degradation is accelerated with the temperature. The higher the temperature, the more coke surface is involved in reactions, and the less negative effect on coke strength is. Hydrogen exerts stronger effect on coke degradation than CO at high temperature. The coke degradation is decreased with the reduction of ore to coke ratio and increase of ore prereduction rate.
基金The authors would like to express their thanks for the support to this work by National Natural Science Foundation of China(51604208)Special Project of Shaanxi Provincial Department of Education(17JK0458)Natural Science Foundation of Shaanxi Province(2019JLM-34,2019JLP-15).
文摘The pore structure of coke under CO2 atmosphere was investigated by the carbon solution-loss reaction experiment.The results show that the pore size distribution of coke gradually changes from dispersion to relative concentration with the increase in carbon loss rate,but it tends to be dispersed again in the late stage of the reaction,and the pore volume and specific surface area also increase first and then decrease with the increase in carbon loss rate.Scanning electron microscopy results show that the evolution of coke pores is from the formation of micropores to the expansion of micropores,and finally the micropore and mesopores collapse to form a large number of string holes.The chemical bonds and functional groups of different reacted cokes were analyzed by Fourier-transform infrared spectroscopy.Furthermore,the microstructure of reacted cokes was analyzed by optical microscopy,and then the ordering of the affinity of different microstructures with CO2 was given.The volume hypothesis which was the theory about energy size of comminution was adopted to analyze the degradation behavior of reacted cokes.The breakage energy of reacted cokes was calculated by volume hypothesis,and the power consumption coefficient CK of different reacted cokes was determined by drum experiment,and then the degradation behavior of reacted cokes under different power consumptions was predicted.