Numerical Analysis of Cold-Formed Thin-Walled Steel Short Columns with Pitting Corrosion during Bridge Construction

Pitting corrosion is harmful during bridge construction,which will lead to uneven roughness of steel surfaces and reduce the thickness of steel.Hence,the effect of pitting corrosion on the mechanical properties of cold-formed thin-walled steel stub columns is studied,and the empirical formulas are established through regression fitting to predict the ultimate load of web and flange under pitting corrosion.In detail,the failure modes and load-displacement curves of specimens with different locations,area ratios,and depths are obtained through a large number of non-linear finite element analysis.As for the specimens with pitting corrosion on the web,all the specimens are subject to local buckling failure,and the failure mode will not change with pitting corrosion,but the failure location will change with pitting corrosion location;the size,location,and area ratio of pitting corrosion have little influence on the ultimate load of cold-formed thin-walled steel short columns,but the loss rate of pitting corrosion section area has a greater impact on the ultimate bearing capacity.As for the specimen with flange pitting corrosion,the location and area ratio of pitting corrosion have less influence on the ultimate load of cold-formed thin-walled steel short columns,and the section area loss rate has greater influence on the ultimate bearing capacity;the impact of web pitting corrosion on the ultimate load is greater than that of flange pitting corrosion under the same condition of pitting corrosion section area.The prediction formulas of limit load which are suitable for pitting corrosion of web and flange are established,which can provide a reference for performance evaluation of corroded cold-formed thin-walled steel.

Bond Performance of Adhesively Bonding Interface of Steel-Bamboo Composite Structure

The steel-bamboo composite structure is a newly developed structure,combining phyllostachys pubescens(also called Moso bamboo)plywood and cold-formed thin-walled steel with structural adhesive.The reliability of steelbamboo interface is the premise of composite effect.13 specimens were prepared to investigate the failure modes and mechanism of the steel-bamboo interface on the basis of push-out test,and the strain difference analysis method was proposed to study the distribution of shear stress.The results show that the main failure modes of steel-bamboo interface are adhesion failure and splitting of bamboo plywood.The shear stress is not evenly distributed along the longitudinal direction of the interface,showing a shape of“larger at two ends and smaller in the middle”.The lower end of the interface is the initial location of the interface failure and the shear stress concentration degree is positively correlated with the thickness of the externally bonded bamboo plate.The shear resistance of steel-bamboo interface can be enhanced by improving the adhesion between steel and structural adhesive and ameliorating the quality of bamboo products.