A lead-free base glaze suitable for pearlescent pigments was prepared by a low-temperature solid-phase reaction with alkali waste.Tests were performed to evaluate the effects of the sintering conditions and alkali was...A lead-free base glaze suitable for pearlescent pigments was prepared by a low-temperature solid-phase reaction with alkali waste.Tests were performed to evaluate the effects of the sintering conditions and alkali waste composition on the prepared base glaze and pearlescent glaze.The experimental results show that partially replacing SiO_(2) with B_(2)O_(3) effectively reduced the sintering temperature and time to form a glass network,but the network structure becomes disconnected as the B_(2)O_(3) content increases.An amorphous base glaze was obtained when soda ash was replaced with a small amount of alkali waste,but increasing the addition of NaCl further was adverse to base glaze formation by resulting in crystallization of the base glaze and a decrease in the bridging oxygen content.The pearlescent pigment was thermally stable in the glaze at 750℃,while higher temperatures caused the crystalline phase of NaAlSiO_(4) to appear and adhere to the surface of pigment granules,which degraded the pearlescent effect of the glaze.展开更多
A copper-red and silver-white metallic glaze of R_(2)O-RO-Al_(2)O_(3)-SiO_(2)-P_(2)O_(5)system was synthesized by adjusting the firing temperature and glaze components.The coloration mechanism of the metallic glaze wa...A copper-red and silver-white metallic glaze of R_(2)O-RO-Al_(2)O_(3)-SiO_(2)-P_(2)O_(5)system was synthesized by adjusting the firing temperature and glaze components.The coloration mechanism of the metallic glaze was revealed via investigation of the microstructure of the glaze.Our research reveals that the metallic glaze with different colors is mainly due to the amount of Fe_(2)O_(3).The metallic glaze shows a silver-white luster due to a structural color ofα-Fe_(2)O_(3)crystals with a good orientation when the sample contains 0.0939 mol of Fe_(2)O_(3),maintaining temperatures at 1150℃for 0.5 h.The metallic glaze is copper-red which is dominated by the coupling of chemical and structural color ofα-Fe_(2)O_(3)crystals when the sample contains 0.0783 mol of Fe_(2)O_(3).After testing the amount of SiO_(2),we find that 4.0499 mol is the optimal amount to form the ceramic network,and 0.27 mol AlPO_(4)is the best amount to promote phase separation.展开更多
A simple idea to obtain a desired color that hiding the black color, and the visibility of tubes and corrugations of the metal sheet （absorber） of the thermal solar collectors which is consider the main obstacle to ...A simple idea to obtain a desired color that hiding the black color, and the visibility of tubes and corrugations of the metal sheet （absorber） of the thermal solar collectors which is consider the main obstacle to facade integration buildings of solar thermal collectors will be presented in this study by designing a multilayer optical interference filter during RF magnetron sputtering process. This filter work as antireflection coating in the near IR region and also includes a high colored reflectance at a specific wavelength in the visible region, this is to gain an esthetic aspect for the thermal solar collector which can be used as building facades by employing appropriate dielectric materials with high refractive index （H） like SiO2 and low refractive index （L） such as MgF2 which they deposited on glass substrate for quarterwave thickness and for the optical model air//HL//glass.展开更多
This paper mainly discusses the Si/Al molar ratio, RO/R2O molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning...This paper mainly discusses the Si/Al molar ratio, RO/R2O molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning electron microscopy were used to analyze better experimental sample microstructure and color and so on. We explored the Longquan Celadon of pink coloration mechanism.展开更多
This paper mainly discusses the Si/A1 molar ratio, RO/R20 molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning...This paper mainly discusses the Si/A1 molar ratio, RO/R20 molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning electron microscopy were used to analyze better experimental sample microstructure and color and so on. We explored the Longquan Celadon of pink coloration mechanism.展开更多
The aim of this study was to compare the effects of different porcelain polishing techniques on the color change and surface roughness of feldspathic porcelains and lithium disilicate glass-ceramic system. 80 porcelai...The aim of this study was to compare the effects of different porcelain polishing techniques on the color change and surface roughness of feldspathic porcelains and lithium disilicate glass-ceramic system. 80 porcelain specimens were divided into two subgroups, each subgroup was divided into 4 groups of 10 specimens. Surfaces were polished with different ceramic polishers. VITA Easyshade spectrophotometer was used to measure color differences. Surface roughness was evaluated using a profilometer. The color change and surface roughness of porcelains were statistically analyzed by Two-way ANOVA followed by a Tukey HSD test (α = 05). There were relationships between the porcelain systems and polishing techniques (p 0.05). For △E values, there was relationship between the porcelain systems and polishing techniques (p 0.05). Chairside porcelain polishing systems were not able to provide a porcelain surface as smooth as the glazed surface for the IPS empress and Ceramco 3 porcelains.展开更多
As a kind of rare materials,nano-silver has broad application prospects in the fields of catalysis,medical treatment,new energy and so on.However,there are few reports on the systematic research of nano-silver in cera...As a kind of rare materials,nano-silver has broad application prospects in the fields of catalysis,medical treatment,new energy and so on.However,there are few reports on the systematic research of nano-silver in ceramic glazes.In this work,different color ceramic glazes were produced by tuning the nano-silver content and optimizing the firing process.The crystalline phase composition,micro-morphology and elemental distribution of fired glazes were analyzed and discussed in depth.The elemental composition and distribution of the samples were studied.The surface of the glazes with varying Ag contents fired under the reducing atmosphere exhibited blue-white.And the blue color is attributable to Rayleigh scattering that may arise because the phase-separation structures existed in glazes.Interestingly,the color of the ceramic glazes with varying Ag contents changed to golden-yellow when the ceramic glazes were fired under the air atmosphere.Golden-yellow color of the samples fired under the air atmosphere is mainly attributable to the silver nanoparticles,though Ag^(+) may be existed in the glazes.展开更多
基金by the National Natural Science Foundation of China(No.51402097)the College Students Innovation and Entrepreneurship Training Program of Hubei University of Technology(No.202010500045)。
文摘A lead-free base glaze suitable for pearlescent pigments was prepared by a low-temperature solid-phase reaction with alkali waste.Tests were performed to evaluate the effects of the sintering conditions and alkali waste composition on the prepared base glaze and pearlescent glaze.The experimental results show that partially replacing SiO_(2) with B_(2)O_(3) effectively reduced the sintering temperature and time to form a glass network,but the network structure becomes disconnected as the B_(2)O_(3) content increases.An amorphous base glaze was obtained when soda ash was replaced with a small amount of alkali waste,but increasing the addition of NaCl further was adverse to base glaze formation by resulting in crystallization of the base glaze and a decrease in the bridging oxygen content.The pearlescent pigment was thermally stable in the glaze at 750℃,while higher temperatures caused the crystalline phase of NaAlSiO_(4) to appear and adhere to the surface of pigment granules,which degraded the pearlescent effect of the glaze.
基金Funded by the National Natural Science Foundation of China(No.52202231)the College Students Innovation and Entrepreneurship Training Program of Hubei University of Technology(No.202310500039)。
文摘A copper-red and silver-white metallic glaze of R_(2)O-RO-Al_(2)O_(3)-SiO_(2)-P_(2)O_(5)system was synthesized by adjusting the firing temperature and glaze components.The coloration mechanism of the metallic glaze was revealed via investigation of the microstructure of the glaze.Our research reveals that the metallic glaze with different colors is mainly due to the amount of Fe_(2)O_(3).The metallic glaze shows a silver-white luster due to a structural color ofα-Fe_(2)O_(3)crystals with a good orientation when the sample contains 0.0939 mol of Fe_(2)O_(3),maintaining temperatures at 1150℃for 0.5 h.The metallic glaze is copper-red which is dominated by the coupling of chemical and structural color ofα-Fe_(2)O_(3)crystals when the sample contains 0.0783 mol of Fe_(2)O_(3).After testing the amount of SiO_(2),we find that 4.0499 mol is the optimal amount to form the ceramic network,and 0.27 mol AlPO_(4)is the best amount to promote phase separation.
文摘A simple idea to obtain a desired color that hiding the black color, and the visibility of tubes and corrugations of the metal sheet （absorber） of the thermal solar collectors which is consider the main obstacle to facade integration buildings of solar thermal collectors will be presented in this study by designing a multilayer optical interference filter during RF magnetron sputtering process. This filter work as antireflection coating in the near IR region and also includes a high colored reflectance at a specific wavelength in the visible region, this is to gain an esthetic aspect for the thermal solar collector which can be used as building facades by employing appropriate dielectric materials with high refractive index （H） like SiO2 and low refractive index （L） such as MgF2 which they deposited on glass substrate for quarterwave thickness and for the optical model air//HL//glass.
文摘This paper mainly discusses the Si/Al molar ratio, RO/R2O molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning electron microscopy were used to analyze better experimental sample microstructure and color and so on. We explored the Longquan Celadon of pink coloration mechanism.
文摘This paper mainly discusses the Si/A1 molar ratio, RO/R20 molar ratio, Fe content, glazing and firing system on the thickness of Longquan Celadon pink coloring effects, and using a colorimeter, field emission scanning electron microscopy were used to analyze better experimental sample microstructure and color and so on. We explored the Longquan Celadon of pink coloration mechanism.
基金This study was supported by the Mustafa Kemal Univer-sity Scientific Research Section
文摘The aim of this study was to compare the effects of different porcelain polishing techniques on the color change and surface roughness of feldspathic porcelains and lithium disilicate glass-ceramic system. 80 porcelain specimens were divided into two subgroups, each subgroup was divided into 4 groups of 10 specimens. Surfaces were polished with different ceramic polishers. VITA Easyshade spectrophotometer was used to measure color differences. Surface roughness was evaluated using a profilometer. The color change and surface roughness of porcelains were statistically analyzed by Two-way ANOVA followed by a Tukey HSD test (α = 05). There were relationships between the porcelain systems and polishing techniques (p 0.05). For △E values, there was relationship between the porcelain systems and polishing techniques (p 0.05). Chairside porcelain polishing systems were not able to provide a porcelain surface as smooth as the glazed surface for the IPS empress and Ceramco 3 porcelains.
基金financially supported by the National Natural Science Foundation of China(Grant No.52072327)Zhongyuan Thousand Talents(Zhongyuan Scholars)Program of Henan Province(No.202101510004)+2 种基金the Scientific and Technological Projects of Henan Province(No.202102210022)the Undergraduate Innovation and Entrepreneurship Project of Henan Province(No.202010480011)Henan Province Water Conservancy Technology Project(No.GG201922)。
文摘As a kind of rare materials,nano-silver has broad application prospects in the fields of catalysis,medical treatment,new energy and so on.However,there are few reports on the systematic research of nano-silver in ceramic glazes.In this work,different color ceramic glazes were produced by tuning the nano-silver content and optimizing the firing process.The crystalline phase composition,micro-morphology and elemental distribution of fired glazes were analyzed and discussed in depth.The elemental composition and distribution of the samples were studied.The surface of the glazes with varying Ag contents fired under the reducing atmosphere exhibited blue-white.And the blue color is attributable to Rayleigh scattering that may arise because the phase-separation structures existed in glazes.Interestingly,the color of the ceramic glazes with varying Ag contents changed to golden-yellow when the ceramic glazes were fired under the air atmosphere.Golden-yellow color of the samples fired under the air atmosphere is mainly attributable to the silver nanoparticles,though Ag^(+) may be existed in the glazes.