The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning ele...The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning electron microscope. The blocky compounds in these alloys were identified as rare earth compounds, (Cr, Ti)2 RE (Al, X)20 (X is magnesium, copper and zinc),body-centred cubic, with 184 atoms to the unit cell , lattice parameter 1.453￣1. 458 nm, Vickers hardness 4000￣5600 MPa and calculated density 3400 kg/m3. The results show that the amount of blocky compounds in the alloys decreases with decreasing of Ti and Cr content or with increasing of cooling rate during solidification.展开更多
The formation and the growth of Cu-Sn intermetallic compound (IMC) layer at the interface between Sn-3.0Ag-0.5Cu-xCe solder and Cu substrate during soldering and aging were studied. The results show that Cu6Sn5 IMC is...The formation and the growth of Cu-Sn intermetallic compound (IMC) layer at the interface between Sn-3.0Ag-0.5Cu-xCe solder and Cu substrate during soldering and aging were studied. The results show that Cu6Sn5 IMC is observed at the interface between solder and Cu substrate in all conditions. After aging for 120 h,the Cu3Sn IMC is then obtained. With increasing aging time,the scalloped Cu6Sn5 structure changes to a plate structure. The Cu3Sn film always forms with a relatively planar interface. By adding a small amount of the rare earth element Ce (only 0.1%,mass fraction) into the Sn-3.0Ag-0.5Cu solder alloy,the growth rate of the Cu-Sn IMC at the interface of solder alloy system is decreased. When the time exponent is approximately 0.5,the growth of the IMC layer is mainly controlled by a diffusion over the studied time range.展开更多
Perfluoroalkyl iodides reacted with conjugated dienes in aqueous acetonitrile solution in the presence of sodium dithionite at room temperature to give dimerization products, whereas, perfluo- roalkanesulfonyl bromide...Perfluoroalkyl iodides reacted with conjugated dienes in aqueous acetonitrile solution in the presence of sodium dithionite at room temperature to give dimerization products, whereas, perfluo- roalkanesulfonyl bromides reacted with conjugated dienes to form 1,4-adducts under actinic irradiation.展开更多
文摘The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning electron microscope. The blocky compounds in these alloys were identified as rare earth compounds, (Cr, Ti)2 RE (Al, X)20 (X is magnesium, copper and zinc),body-centred cubic, with 184 atoms to the unit cell , lattice parameter 1.453￣1. 458 nm, Vickers hardness 4000￣5600 MPa and calculated density 3400 kg/m3. The results show that the amount of blocky compounds in the alloys decreases with decreasing of Ti and Cr content or with increasing of cooling rate during solidification.
基金Project(06GK2002) supported by the Major Project of Hunan Provincial Science and Technology Development Strategy
文摘The formation and the growth of Cu-Sn intermetallic compound (IMC) layer at the interface between Sn-3.0Ag-0.5Cu-xCe solder and Cu substrate during soldering and aging were studied. The results show that Cu6Sn5 IMC is observed at the interface between solder and Cu substrate in all conditions. After aging for 120 h,the Cu3Sn IMC is then obtained. With increasing aging time,the scalloped Cu6Sn5 structure changes to a plate structure. The Cu3Sn film always forms with a relatively planar interface. By adding a small amount of the rare earth element Ce (only 0.1%,mass fraction) into the Sn-3.0Ag-0.5Cu solder alloy,the growth rate of the Cu-Sn IMC at the interface of solder alloy system is decreased. When the time exponent is approximately 0.5,the growth of the IMC layer is mainly controlled by a diffusion over the studied time range.
基金This research was supported by the National Natural Science Foundation of China as an item of major project.
文摘Perfluoroalkyl iodides reacted with conjugated dienes in aqueous acetonitrile solution in the presence of sodium dithionite at room temperature to give dimerization products, whereas, perfluo- roalkanesulfonyl bromides reacted with conjugated dienes to form 1,4-adducts under actinic irradiation.