以可膨胀石墨、膨胀石墨和高密度聚乙烯为原材料,在二甲苯溶剂中制备了聚乙烯/可膨胀石墨和聚乙烯/膨胀石墨复合材料。扫描电镜显示,聚乙烯已包覆在可膨胀石墨和膨胀石墨上,傅立叶红外光谱分析确认了包覆在可膨胀石墨和膨胀石墨上的高分子为聚乙烯分子。该法利用可膨胀石墨和膨胀石墨的导电性能改善不导电的聚乙烯,并且成功地制备出具有防静电性能的聚乙烯/石墨复合新材料。

石墨烯/氧化铝复合材料制备方法的对比研究

分别利用等离子电火花烧结（SPS）和管式炉气氛烧结技术,制备了石墨烯/氧化铝复合材料。分析对比了两种方法下制备的烧结体的微观组织和力学性能。研究显示：石墨烯均匀地分散在烧结体中,结合超声和球磨的分散工艺能较好实现石墨烯在陶瓷颗粒中的分散。管式炉烧结和SPS都可以实现石墨烯/氧化铝复合材料的致密化,烧结体的相对密度均可达97%以上。且通过管式炉烧结制备的样品与SPS制备的样品具有相近的力学性能,其中韧性可达4MPa·m^1/2左右,硬度可达17 GPa以上。SPS可在短时和较低温度下完成石墨烯与陶瓷粉体的烧结,其烧结过程对管式炉的烧结工艺具有重要的指导意义,而管式炉烧结则有望实现高性能石墨烯/陶瓷生物医用复合材料的批量生产。

基体合金种类对SiCw/Al复合材料拉伸性能的影响

对SiCw/LD2、SiCw/LC9复合材料进行了热挤压加工并沿其纵向进行了拉伸对比试验。结果表明:SiCw/LD2的抗拉强度为590MPa,而SiCw/LC9复合材料的抗拉强度高达750MPa。SEM分析发现,上述两种复合材料均为切应力作用下的韧窝形断口,但SiCw/LD2的断口有明显的晶须拔出。低于临界长径比的晶须被拔出是SiCw/LD2断裂的主要形式;高于临界长径比的晶须被拉断是SiCw/LC9断裂的主要形式;基体合金的不同导致了复合材料具有不同的晶须临界长径比,这也是SiCw/LC9复合材料较SiCw/LD2复合材料有更高抗拉强度的根本原因。

考虑桩土应力扩散的复合地基理论与应用

复合地基理论被广泛应用于处理软弱地基工程实践中,而加固桩体的有效桩长是复合地基理论中需要考虑的重要问题之一。文章从加固体的荷载传递规律和应力扩散理论角度出发,应用弹性半空间体内任意点附加应力Boussinesq解,求出有效桩长的计算公式,并结合工程实例介绍有效桩长在工程中的应用。

TiB_2和SiC_w对Al_2O_3陶瓷材料高温摩擦磨损特性的影响

研究了Ａｌ２Ｏ３、Ａｌ２Ｏ３／ＴｉＢ２和Ａｌ２Ｏ３／ＴｉＢ２／ＳｉＣｗ三种陶瓷材料在不同温度条件下的摩擦磨损特性．结果表明：三种陶瓷材料与硬质合金摩擦副的摩擦系数随温度的增加有不同的变化规律，摩擦表面的Ｘ射线衍射分析表明，摩擦系数的变化与陶瓷物膜的组成和结构有关，在高温下Ａｌ２Ｏ３／ＴｉＢ２陶瓷材料摩擦表面形成了具有优良的高温润滑性的ＴｉＯ２氧化膜，因而ＴｉＢ２的加入明显地改善了Ａｌ２Ｏ３陶瓷材料的摩擦磨损特性．Ａｌ２Ｏ３／ＴｉＢ２／ＳｉＣｗ陶瓷材料摩擦表明形成了含有ＴｉＯ２和Ａｌ２Ｏ３·２ＳｉＯ２的氧化膜，由于ＴｉＯ２和Ａｌ２Ｏ３·２ＳｉＯ２的热膨胀系数不匹配，而易使氧化膜产生开裂或剥落，因此ＳｉＣ晶须的加入对Ａｌ２Ｏ３／ＴｉＢ２陶瓷的高温摩擦磨损特性能有一定程度的不利影响．

管道纺纱装置结构的优化

本文对管道纺纱装置的结构进行了深入的研究,提出了在原管道纺纱装置的基础上,将吸风装置绕输纤管道的轴线旋转180°的新方案。以这个设计方案为基础,对其主要的结构参数和主要的工艺参数进行了优化,求得了最佳结构参数和最佳工艺参数。再根据最佳结构参数制造有关零件,装在管道纺纱单头试验机上,以求得的最佳工艺参数为工艺务件,实际纺制28tex 纯棉纱。这个新装置不仅能稳定地纺纱,而且其成纱的缕纱强力与优化计算的结果基本一致。

AgCu/QSn复合带的张力退火矫直

简要介绍了张力退火矫直的基本原理、设备及对AgCu/QSn复合带进行张力退火矫直的试验结果。退火试验温度为200,250,,300,350℃,分别加100,150,200,250MPa张力,氩气保护,退火时间分别为1,3min,结果表明,在200～350℃,加张力100～200MPa,退火1min的工艺条件能使复合带AgCu面硬度Hv>1100MPa,QSn面硬度Hv>2000MPa,抗拉强度σ_b>600MPa,延伸率δ>20%,平直度h<2mm。

Tribological Properties of Self-lubricating Laminated Ceramic Materials

In order to improve the tribological properties of ceramic composites, Al2O3/TiC-Al2O3/ TiC/CaF2 self-lubricating laminated ceramic composites were prepared by vacuum hot pressing sintering. Experiments were conducted to get mechanical properties and the friction and wear properties were also measured with friction and wear tester. The worn surfaces were observed by scanning electron microscope （SEM） and energy dispersion spectrum （EDS）. The wear resistance properties and the self-lubricating effect of ceramic composites were analyzed. Results show that the Al2O3/TiC-Al2O3/TiC/CaF2 self-lubricating laminated ceramic composites layers are well-defined with a higher bonding strength and the mechanical performances are uniform enough to overcome the anisotropy of weak laminated ceramic composites. In addition, the fracture toughness of Al2O3/TiC layers is also improved. Its friction coefficient and wear rates decrease with the increase of rotation speed and load. Al2O3/TiC-Al2O3/TiC/CaF2 self-lubricating laminated ceramic composites have good wear resistance because of the tribofilm formed by the CaF2 solid lubricants. The wear mechanisms of Al2O3/TiC/ CaF2 layers are abrasive wear and Al2O3/TiC layers are adhesive wear.

配筋钢纤维混凝土叠合梁受力性能试验研究

本文通过21根叠合梁的试验研究,探讨了配筋钢纤维混凝土叠合梁正截面受力性能,分析了钢纤维的掺入对叠合梁受拉钢筋“应力超前”效应减缓的程度,提出了配筋钢纤维混凝土叠合梁受拉钢筋应力限值的公式。

（Ni－W）－SiC复合镀层的研制

本文报道了制备（Ｎｉ－Ｗ）－ＳｉＣ复合镀层的电沉积工艺，获得了含碳化硅１．１％～８．３％、含钨４７．２％～５１．０％的（Ｎｉ－Ｗ）－ＳｉＣ复合镀层。讨论了微粒悬浮量、温度、ｐＨ值、阴极电流密度对镀层中碳化硅含量的影响。测试了复合镀层的硬度及耐磨性。结果表明，ＳｉＣ微粒的复合，明显增加了Ｎｉ－Ｗ合金镀层的硬度和耐磨性能。

低渗透油藏ASG复合泡沫体系注入参数优化

对ASG(碱、表面活性剂与氮气)复合泡沫体系与水交替注入提高采收率技术在高温高矿化度低渗透油藏的适用性进行研究。通过室内驱油实验的方法,开展ASG泡沫与水交替注入实验,并将之与水驱、氮气驱、表面活性剂驱进行对比。结果发现,ASG泡沫与水交替注入较水驱、氮气驱、表面活性剂驱分别采收率提高了16.61%、10.26%与9.21%。ASG泡沫与水交替注入的注入参数优化实验研究结果表明,在累积注入泡沫体积相同(1.2倍孔隙体积)的条件下,采用0.4倍孔隙体积泡沫段塞交替注入的效果最佳;泡沫注入速度的最优值为1.5mL/min,当注入速度过低时,产生泡沫较少,且容易发生气液分离,封堵效果不佳,当注入速度过高时,泡沫大小不一,容易发生气泡合并,引起气泡的破裂,同时容易造成泡沫的剪切消泡;分三次注入段塞气液质量比分别为3∶1、2∶1与1.5∶1时,较单一气液质量比泡沫采收率提高了2.04%。

轮履复合式机器人实验平台设计与研究

轮履复合机器人实验平台是在分析现有移动平台形式的基础上,针对工业现场和教学实践的双重需要,设计的一种可二次开发的通用机器人实验平台。该设计采用模糊逻辑控制器控制电机驱动单元实现机器人的自主移动,采用轮履复合式的机械结构极大地提高了机器人的灵活性和机动性,拓展了机器人的活动空间。软硬件均采用模块化设计,使机器人实验平台的通用性和开发便捷性进一步增强,可广泛应用于教学、救援、巡检、军事以及勘探等领域。

钢——砼组合梁的截面性能分析

本文用数值迭代法对钢——砼组合梁截面的弯矩—曲率关系和权限弯矩进行了计算分析。从理论上校核了用来确定组合梁极限抗弯强度的简化塑性理论。计算结果和分析表明,数值迭代法是计算组合梁截面曲率的有效方法。在已知滑移应变的情况下,数值迭代和数值积分计算可以较精确地估算不完全剪力连接钢—砼组合梁的挠度。