In order to investigate the size effect and other effects on the stress-strain relationship of confined concrete, 42 specimens with different sizes and section shapes were placed under axial compression loading. Effec...In order to investigate the size effect and other effects on the stress-strain relationship of confined concrete, 42 specimens with different sizes and section shapes were placed under axial compression loading. Effects of key parameters such as size of specimens, tie configuration, transverse reinforcement ratio, and concrete cover were studied. The results show that for specimens with the same configuration and the same volumetric ratio of the transverse reinforcement, along with the increasing specimen size, the peak stress, peak strain and deformation of the post-peak show a down trend, however, the volumetric ratio of the transverse reinforcement is lowered, the decreasing of the peak stress is accelerated, but the decreasing of the deformation is slow down. For specimens with the same volumetric ratio but different configurations of transverse reinforcement, though the transverse reinforcement configuration becomes more complicated, the peak stress of the large size specimen does not improve more than that of the small size. However, the deformation occurs before the stress declines to 85% of peak stress, and the improvement with the grid pattern tie configuration is much greater due to size effect.展开更多
The effects of cover thickness and W/C(water-to-cement) ratio on polarization properties of embedded steel bar were investigated with electrochemical methods.Corrosion potentials shift to the noble direction with incr...The effects of cover thickness and W/C(water-to-cement) ratio on polarization properties of embedded steel bar were investigated with electrochemical methods.Corrosion potentials shift to the noble direction with increasing the cover thickness.In addition,when the cover thickness increasingly becomes thinner and thinner,effect of the W/C ratio on variation of corrosion potential increases as well.Impedance value at 100 kHz indicating the resistance of cover thickness increases with the decrement of W/C ratio as well as the increment of cover thickness.However,in the case of W/C ratio at 0.6,impedance at 10 mHz shows the relatively larger value than that at W/C ratio of 0.4 or 0.5 in the range of cover thickness from 4 to 8 cm,which is probably expected that oxide film built up on the surface of steel bar due to strong alkali environment by hydration reaction with increasing W/C ratio is performed as the resistance polarization.It is also observed that liquid junction potential tends to increase with decreasing W/C ratio.展开更多
基金Project(50838001) supported by the National Natural Science Foundation of China
文摘In order to investigate the size effect and other effects on the stress-strain relationship of confined concrete, 42 specimens with different sizes and section shapes were placed under axial compression loading. Effects of key parameters such as size of specimens, tie configuration, transverse reinforcement ratio, and concrete cover were studied. The results show that for specimens with the same configuration and the same volumetric ratio of the transverse reinforcement, along with the increasing specimen size, the peak stress, peak strain and deformation of the post-peak show a down trend, however, the volumetric ratio of the transverse reinforcement is lowered, the decreasing of the peak stress is accelerated, but the decreasing of the deformation is slow down. For specimens with the same volumetric ratio but different configurations of transverse reinforcement, though the transverse reinforcement configuration becomes more complicated, the peak stress of the large size specimen does not improve more than that of the small size. However, the deformation occurs before the stress declines to 85% of peak stress, and the improvement with the grid pattern tie configuration is much greater due to size effect.
文摘The effects of cover thickness and W/C(water-to-cement) ratio on polarization properties of embedded steel bar were investigated with electrochemical methods.Corrosion potentials shift to the noble direction with increasing the cover thickness.In addition,when the cover thickness increasingly becomes thinner and thinner,effect of the W/C ratio on variation of corrosion potential increases as well.Impedance value at 100 kHz indicating the resistance of cover thickness increases with the decrement of W/C ratio as well as the increment of cover thickness.However,in the case of W/C ratio at 0.6,impedance at 10 mHz shows the relatively larger value than that at W/C ratio of 0.4 or 0.5 in the range of cover thickness from 4 to 8 cm,which is probably expected that oxide film built up on the surface of steel bar due to strong alkali environment by hydration reaction with increasing W/C ratio is performed as the resistance polarization.It is also observed that liquid junction potential tends to increase with decreasing W/C ratio.