Mechanical Behavior Based on Aggregates Microstructure of Ultra-high Performance Concrete

We developed ultra-high performance concrete(UHPC)incorporating mullite sand and brown corundum sand(BCS),and the quartz sand UHPC was utilized to prepare for comparison.The properties of compressive strength,elastic modulus,ultrasonic pulse velocity,flexural strength,and toughness were investigated.Scanning electron microscopy and nanoindentation were also conducted to reveal the underlying mechanisms affecting macroscopic performance.Due to the superior interface bonding properties between mullite sand and matrix,the compressive strength and flexural toughness of UHPC have been significantly improved.Mullite sand and BCS aggregates have higher stiffness than quartz sand,contributing to the excellent elastic modulus exhibited by UHPC.The stiffness and volume of aggregates have a more significant impact on the elastic modulus of UHPC than interface performance,and the latter contributes more to the strength of UHPC.This study will provide a reference for developing UHPC with superior elastic modulus for structural engineering.

Effect of Shrinkage Reducing Agent and Steel Fiber on the Fluidity and Cracking Performance of Ultra-High Performance Concrete

Due to the low water-cement ratio of ultra-high-performance concrete(UHPC),fluidity and shrinkage cracking are key aspects determining the performance and durability of this type of concrete.In this study,the effects of different types of cementitious materials,chemical shrinkage-reducing agents(SRA)and steel fiber(SF)were assessed.Compared with M2-UHPC and M3-UHPC,M1-UHPC was found to have better fluidity and shrinkage cracking performance.Moreover,different SRA incorporation methods,dosage and different SF types and aspect ratios were implemented.The incorporation of SRA and SF led to a decrease in the fluidity of UHPC.SRA internal content of 1%(NSRA-1%),SRA external content of 1%(WSRA-1%),STS-0.22 and STE-0.7 decreased the fluidity of UHPC by 3.3%,8.3%,9.2%and 25%,respectively.However,SRA and SF improved the UHPC shrinkage cracking performance.NSRA-1%and STE-0.7 reduced the shrinkage value of UHPC by 40%and 60%,respectively,and increased the crack resistance by 338%and 175%,respectively.In addition,the addition of SF was observed to make the microstructure of UHPC more compact,and the compressive strength and flexural strength of 28 d were increased by 26.9%and 19.9%,respectively.

Influence Mechanism of Curing Regimes on Interfacial Transition Zone of Lightweight Ultra-High Performance Concrete

This study aims to clarify the effects of curing regimes and lightweight aggregate(LWA)on the morphology, width and mechanical properties of the interfacial transition zone(ITZ) of ultra-high performance concrete(UHPC), and provide reference for the selection of lightweight ultra-high performance concrete(L-UHPC) curing regimes and the pre-wetting degree LWA. The results show that, under the three curing regimes(standard curing, steam curing and autoclaved curing), LWA is tightly bound to the matrix without obvious boundaries. ITZ width increases with the water absorption of LWA and decreases with increasing curing temperature. The ITZ microhardness is the highest when water absorption is 3%, and the microhardness value is more stable with the distance from LWA. Steam and autoclaved curing increase ITZ microhardness compared to standard curing. As LWA pre-wetting and curing temperatures increase, the degree of hydration at the ITZ increases, generating high-density CSH(HD CSH) and ultra-high-density CSH(UHD CSH), and reducing unhydrated particles in ITZ. ITZ micro-mechanical properties are optimized due to hydration products being denser.

集中配筋连接预制剪力墙抗震性能试验研究

针对现有预制混凝土剪力墙接缝施工容错率低、混凝土现场浇筑作业量大和钢筋锚固过长等不足,提出一种使用超高性能混凝土(UHPC)的集中配筋连接预制剪力墙。通过对比1片现浇剪力墙试件、3片不同接缝形式的集中配筋连接预制剪力墙试件的拟静力试验结果,揭示该类预制剪力墙的破坏规律和抗震性能、竖缝对墙体抗震性能的影响和连接钢筋的受力特点。采用ABAQUS软件对试件进行有限元模拟,分析轴压比和集中配筋率对试件抗震性能的影响。研究结果表明:预制试件与现浇试件具有相同的破坏规律,均为弯剪破坏;这2类试件的滞回曲线均较饱满,骨架曲线走势基本一致,耗能能力接近,且预制试件的最小承载力仅比现浇试件低5.6%,表明预制试件的抗震性能与现浇试件的抗震性能基本相同;竖缝对剪力墙承载力的影响较小,使剪力墙的延性和耗能能力有一定的削弱;不同竖缝形式预制墙的抗震性能相近但各有特点,竖缝形式预制墙采用UHPC出筋搭接具有更好的整体性,采用U形键槽的预制墙具有更大的刚度和更强的耗能能力;连接钢筋的应力分布具有典型受弯构件的特征;随着轴压比增加,模型的刚度和承载力不断增加,在轴压比从0.05增加到0.30时,最大的峰值荷载增幅发生在轴压比从0.05到0.10时,从承载力的提高、刚度、耗能和墙角抬高等方面考虑,试件的集中配筋率保持在90%~110%为宜。

STUDY ON OPTIMIZATION OF HIGH PERFORMANCE CONCRETE ADMIXTURES

Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polycarboxlic series high range water reduce agent and sodium sulfate hardening accelerating agent. Two kinds of curing condition, namely steam curing condition and standard curing condition, are adopted. The result shows that HPC, added with polycarboxlic series of high performance water reducer, has high workability and strength, while sodium sulfate accelerating agent causes poor workability and low strength. Thus for vapor-cured HPC and its formulations, naphthalene series high range water reducing agent with less sodium sulfate should be given pri- ority. Therefore, the differences of curing conditions should be considered when selecting HPC admixtures.

INFLUENCE OF AIRCRAFT DEICER ON FREEZE-THAW DURABILITY OF HIGH PERFORMANCE CONCRETE

The influence of glycol,the main composition of the most frequently used aircraft dicer,on the freeze-thaw durability of high performance concrete（HPC）is investigated.Freeze-thaw durability of HPC is tested by accelerated freeze-thaw test.Four kinds of the solution,i.e.,tap water,3.5% NaCl solution,glycol solutions,and a LBR-A type commercial aircraft deicer are employed.Results show that freeze-thaw durability of HPC exposed to glycol solutions is closely related to the solution concentrations.The failure of HPC exposed to 3.5% glycol solution is similar to that of those exposed to 3.5% NaCl solution,i.e.,serious surface scaling.While the damage of HPC exposed to 12.5%—25% glycol solutions is postponed.Compared with glycol solution,the commercial aircraft deicer has much more negative effects on HPC freeze-thaw durability compared with 3.5% NaCl solution.In the presence of commercial aircraft deicer for HPC subjected to freeze-thaw cycles,the deterioration is mainly due to scaling and spalling.

Analysis and Prediction Model Reinforced UHPC Shrinkage Property

This paper explores the shrinkage of reinforced UHPC under high-temperature steam curing and natural curing conditions.The results are compared with the existing shrinkage prediction models.The results show that the maximum shrinkage strain of reinforced UHPC after steam curing is 164μεand gradually becomes zero.As for natural curing,the maximum shrinkage strain is 173μεand the value stabilizes on the 10th day after pouring.This indicated that steam curing can significantly reduce shrinkage time.Compared with the plain UHPC tested in the previous literature,the structural reinforcement can significantly inhibit the UHPC shrinkage and greatly reduce the risk of cracking due to shrinkage.By comparing the results in this paper with the existing models for predicting the shrinkage strain development,it is found that the formula recommended in the French UHPC structural and technical specification is suitable for the shrinkage curve in the present paper.

Combined effect of steel fibres and steel rebars on impact resistance of high performance concrete

The impact properties of normal concrete (NC) and reinforced concrete (RC) specimens,steel fibre reinforced concrete (SFRC) specimens and RC+SFRC specimens with different steel fibre dosages were investigated with the drop-weight impact test recommended by ACI Committee 544.The results indicate that the number of blows to final failure is greatly increased by addition of steel fibres.Moreover,the combination of steel fibres and steel rebars demonstrates a significant positive composite effect on the impact resistance,which results in the improvement in impact toughness of concrete specimens.In the view of variation of impact test results,the two-parameter Weibull distribution was adopted to analyze the experimental data.It is proved that the probabilistic distributions of the blows to first crack and to final failure of six types of samples approximately follow two-parameter Weibull distribution.

Carbonation Resistance of Sulphoaluminate Cement-based High Performance Concrete

The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.

Pore Size Distribution of High Performance Metakaolin Concrete

The Compressive strength, porosity and pore size distribution of high performance metakaolin (MK) concrete were investigated. Concretes containing 0,5% , 10% and 20% metakaolin were prepared at a water / cementitious material ratio ( W/C) of 0. 30. In parallel, concrete mixtures with the replacement of cement by 20% fly ash or 5 and 10% silica fume were prepared for comparison. The specimens were cured in water at 27℃ for 3 to 90 days. The results show that at the early age of curing (3 days and 7 days), metakaolin replacements increase the compressive strength, but silica fume replacement slightly reduces the compressive strength. At the age of and after 28 days , the compressive strength of the concrete with metakaolin and silica fume replacement increases. A strong reduction in the total porosity and average pore diameter were observed in the concrete with MK 20% and 10% in the first 7 days.

High Performance Concrete and Its Typical Mixes

With the modern development of chemical and mineral admixtures, it is now possible to produce much higher performance concrete than before. Higher performance does not only mean higher strength, but also better durability, lower risk of thermal cracking and higher dimensional stability etc. The three most effective admixtures for producing high performance concrete are superplastieizer, pulverized fuel ash and condensed silica fume. This paper outlines the properties of these materials and presents some practical guidelines for their usage.

Design of Eco-friendly Ultra-high Performance Concrete with Supplementary Cementitious Materials and Coarse Aggregate

Aiming to investigate the mix design of eco-friendly UHPC with supplementary cementitious materials and coarser aggregates, we comprehensively studied the workability, microstructure, porosity, compressive strength, flexural strength, and Young’s modulus of UHPC. Relationship between compressive strength and Young’s modulus was obtained eventually. It is found that the compressive strength, flexural strength, and Young’s modulus of UHPC increase by 19.01%, 10.81%, and 5.99%, respectively, when 40 wt% cement is replaced with supplementary cementitious materials. The relationship between compressive strength and Young’s modulus of UHPC is an exponential form.

Effect of Pre-wetted Light-weight Aggregate on Internal RelativeHumidity and Autogenous Shrinkage of Concrete

This research indicates that the gradient of internal relative humidity （IRH） decreases rapidly within 7-day curing age in HPC. The amount of water imported by pre-wetted light-weight aggregate can regulate IRH of concrete. By importing a proper amount of water, the process of the decline of IRH can be delayed and the autogenous shrinkage can be reduced. The relationship among the amount of water imported by pre- wetted lightweight aggregate, IRH and AS was established. The result provides a new method of reducing early AS and enhancing early cracking resistance of HPC.

Characterization of Surface Hardness and Microstructure of High Performance Concrete

The relationship between compressive strength obtained by universal testing machine and rebound value obtained by the hammer of high performance concrete was systematically investigated at the macro level. And a model of high performance concrete strength curve was established from them. At the micro level, the microstructure, hydration products and pore structure of concrete surface were analyzed by scanning electron microscopy（SEM）, comprehensive thermal analysis（TG-DSC） and mercury intrusion porosimetry（MIP）, respectively. The effect of carbonation on surface strength was also investigated. The results showed that the concrete surface hardness layer grew rapidly at early stage and then stabilized at last with ongoing curing age; the rebound value and compressive strength of concrete with slag were higher than those of concrete with the same content of fly ash. In addition, the strength curve obtained by the least square method can satisfy the local standard requirements with an average relative error of 8.9% and a relative standard deviation of 11.3%. When the carbonation depth was 6 mm, the compressive strength calculated by national uniform strength curve was 25 PMa higher than that by high performance concrete.

Shrinkage Behavior of High Performance Concrete at Different Elevated Temperatures under Different Sealing Conditions

The shrinkage behavior of high performance cement concrete made from Portland cement, ultra fine granulated blast furnace slag and pulverized fly ash with addition of superplasticizer at different temperatures from ambient temperature to 120 ℃ under different seuliug conditions was investigated by means of length change measurement on cylindrical concrete specimens along with curing age. Results show that drying shrinkage deformations of titled concrete specimens increased rapidly as the curing temperature rose. The development of dryiing shrinkage deformatian can be efficiently controlled with the aid of aluminum tape sealing as compared with the unsealed specimens, especially when the curing temperature is below 60℃ , although it will increase dramatically when the curing temperature is elevated to above 90%＂ . Polymer coating on concrete specimens showed a similar effect on the control of drying shrinkage as the sealing operation with aluminum tape.

Preparation of Heavyweight Ultra-high Performance Concrete Using Barite Sand and Titanium-rich Heavy Slag Sand

The heavyweight ultra-high performance concrete(HUHPC)was prepared with barite sand partially replaced by titanium-rich heavy slag sand(THS)at replacement proportion of 0%,30%,50%,70%and 100%in this work.The results show that THS incorporation can effectively improve the mechanical properties and reduce the volume shrinkage of HUHPC.The HUHPC with 50%THS replacement reaches an apparent density of 2890 kg/m^(3)(for fresh HUHPC),28 d compressive strength of 129 MPa,28 d flexural strength of 23 MPa,28 d flexural toughness of 28.4,56 d volume shrinkage of 359×10^(-4) and,as expected,excellent durability.Microstructural investigation demonstrates that the internal curing of pre-wetted THS promotes the hydration of the surrounding cement paste thereby strengthening the interfacial transition zone,resulting in the“hard shell”formation around aggregate to“protect”the aggregate.Additionally,the“pin structure”significantly improves the cement paste-aggregate interfacial connection.The combination of“hard shell protection”and“pin structure”remarkably improve the mechanical properties of HUHPC produced with porous THS aggregate.

Dynamic Mechanical Behaviour of Ultra-high Performance Fiber Reinforced Concretes

Ultra-high performance fiber reinforced concretes （UHPFRC） were prepared by replacing 60% of cement with ultra-fine industrial waste powder. The dynamic mechanical behaviour of UHPFRC with different fiber volume fraction was researched on repeated compressive impact in four kinds of impact modes through split Hopkinson pressure bar （SHPB）. The experimental results show that the peak stress and elastic modulus decrease and the strain rate and peak strain increase gradually with the increasing of impact times. The initial material damage increases and the peak stress of the specimen decreases from the second impact with the increasing of the initial incident wave. Standard strength on repeated impact is defined to compare the ability of resistance against repeated impact among different materials. The rate of reduction of standard strength is decreased by fiber reinforcement under repeated impact. The material damage is reduced and the ability of repeated impact resistance of UHPFRC is improved with the increasing of fiber volume fraction.

Preparation and Application of C60 High Performance Concrete

C60 High Performance Concrete (HPC) was prepared by limiting cement content and adopting compositesuperplasticizer, low-alkalinity expansive agent and high-quality line mixture. The results showed that the performance of the prepared C60 HPC was excellent. By adopting some advanced construction techniques such as usingsecondary vibration and secondary face compaction, controlling temperature difference and paying special attentionto early curing in the construction process, the prepared C60 HPC had been successfully applied in the monolithicstructure of huge building.

Assessment on Chloride Contaminated Resistance of Concrete with Non-steady-state Migration Method

A preparation technology of chloride contaminated resistant concrete was presented. The newly developed non-steady-state migration test method was employed for the evaluation of chloride ions diffusion coefficient of the concrete. The experimental results show that this method has a good correlation with the traditional NT Build 443 method, and it provides an effective and quick approach to assess the resistant capacity of concrete against chloride ions.

The Corrosion Fatigue Properties of High Performance Concrete

With the loading test equipment of corrosion fatigue specially designed, the corrosion fatigue characteristics of high performance concrete (HPC) withstanding the interaction of third point fatigue loading and Na_2SO_4 solution were investigated and analyzed. The experimental results indicate that water-binder ratio evidently influences the corrosion fatigue characteristics of HPC, and a moderate quantitative fine mineral admixture enhances the corrosion fatigue resistance of HPC. The effect is more significant when fly ash and silica fume are added.