F mineral admixture (FMA) is made of the fin- ely divided powder of natural zeolite with a bit of other agent. When FMA is used to displace about 10% (by weight) of the ordinary portland cement (OPC) (strength grade 5...F mineral admixture (FMA) is made of the fin- ely divided powder of natural zeolite with a bit of other agent. When FMA is used to displace about 10% (by weight) of the ordinary portland cement (OPC) (strength grade 575#) in concrete and mixed with a suitable amount of super plasticizer (w/c =0.31-0.35), then a high-strength concrete with compressive strength about 80 MPa and slump about 180 MM can be obtained. The strength of this concrete is about 10-15% higher than that of the corresponding concrete mixing with pure OPC, and its bleeding decreases greatly. It makes no segre- gation and separation, and thus it satisfies the requirement of pumping concrete in construction.展开更多
The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing...The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.展开更多
This paper presents quantitatively the results of an experimental investigation on influence of mineral admixtures and superplasticizers on Vickers micro hardness(HV) of aggregate-paste interface in cement concrete. T...This paper presents quantitatively the results of an experimental investigation on influence of mineral admixtures and superplasticizers on Vickers micro hardness(HV) of aggregate-paste interface in cement concrete. The HV was measured by Vickers hardness testing equipment.The results indicate that addition of fly ash decreases HV of the concrete.Although it decreases with the increase of ground granulated blast furnace slag (GGBS) replacement,the HV is higher than that of concrete containing fly ash at all replacements.The flying ash and GGBS composition increases HV in later curing ages,but does not improve it in early curing ages.Aminosulfonic acid based superplasticizer and aliphatic hydroxy sulphonate condensate superplasticizer can enhance HV in early curing ages.The HV of concrete with polycarboxylic acid superplasticizer is higher in later curing ages.展开更多
This experimental study aims to examine the influence of many crucial parameters on the workability and compressive strength of Ready-Mix Concrete (RMC). The study utilized two distinct varieties of superplasticizers ...This experimental study aims to examine the influence of many crucial parameters on the workability and compressive strength of Ready-Mix Concrete (RMC). The study utilized two distinct varieties of superplasticizers obtained from the local market. The fine aggregates utilized in this study were sourced from Sylhet sand, whereas the coarse aggregates were comprised of boulder crushed stone chips. The experimental procedures adhered to the requirements outlined by ASTM. A comprehensive investigation was conducted on a range of concrete compositions that used diverse chemical admixtures. The slump test was performed at regular intervals of 15 minutes until the slump value reached or fell below 3 cm after the mixing of the concrete. In the scenario involving two-stage admixture dosage, the second stage of admixture was introduced once the slump reached or dropped below 3 cm, following which the casting process was initiated. The process of curing concrete specimens consists of two distinct stages: the main stage and the final stage. Cylindrical specimens, with a diameter of 4 inches and a height of 8 inches, were manufactured for the purpose of evaluating their compressive strength at both 7 and 28 days. During the experimental trials, the water-cement (w/c) ratio was kept consistent, while different dosages of admixture were applied. The findings of the study indicate that the utilization of a two-stage dose of admixture resulted in enhanced and extended workability, along with higher strength of the concrete in comparison to specimens that did not incorporate any admixture. This research study enhances the comprehension of optimizing qualities of ready-mix concrete (RMC) by varying the superplasticizer, providing useful insights for the building sector.展开更多
Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarbo...Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.展开更多
An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosa...An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosages in terms of Al2O3, these substances are ranged in the following order in respect of inhibiting effect: Al(OH)1.78(SO4)0.61 ≥ Al2(SO4)3 > Al(OH)3. It is found that the plasticizing agents of the main types used in cement compositions have no influence on the inhibiting effect of aluminum-bearing admixtures. To control the setting time of cement paste, iron(II) sulphate may be used for partial substitution of Al2SO4·18H2O, and this operation is not influence on the results of ASR expansion test.展开更多
文摘F mineral admixture (FMA) is made of the fin- ely divided powder of natural zeolite with a bit of other agent. When FMA is used to displace about 10% (by weight) of the ordinary portland cement (OPC) (strength grade 575#) in concrete and mixed with a suitable amount of super plasticizer (w/c =0.31-0.35), then a high-strength concrete with compressive strength about 80 MPa and slump about 180 MM can be obtained. The strength of this concrete is about 10-15% higher than that of the corresponding concrete mixing with pure OPC, and its bleeding decreases greatly. It makes no segre- gation and separation, and thus it satisfies the requirement of pumping concrete in construction.
基金Funded by the National Natural Science Foundation of China(No.50872043)
文摘The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete （HPC） were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite （AFt）, decomposes after carbonation.
基金the Special Foundation for Basic Scientific Research of Central Colleges of China (No:CHD2011ZD011)the Special Foundation of Basic Research for Chang'an University
文摘This paper presents quantitatively the results of an experimental investigation on influence of mineral admixtures and superplasticizers on Vickers micro hardness(HV) of aggregate-paste interface in cement concrete. The HV was measured by Vickers hardness testing equipment.The results indicate that addition of fly ash decreases HV of the concrete.Although it decreases with the increase of ground granulated blast furnace slag (GGBS) replacement,the HV is higher than that of concrete containing fly ash at all replacements.The flying ash and GGBS composition increases HV in later curing ages,but does not improve it in early curing ages.Aminosulfonic acid based superplasticizer and aliphatic hydroxy sulphonate condensate superplasticizer can enhance HV in early curing ages.The HV of concrete with polycarboxylic acid superplasticizer is higher in later curing ages.
文摘This experimental study aims to examine the influence of many crucial parameters on the workability and compressive strength of Ready-Mix Concrete (RMC). The study utilized two distinct varieties of superplasticizers obtained from the local market. The fine aggregates utilized in this study were sourced from Sylhet sand, whereas the coarse aggregates were comprised of boulder crushed stone chips. The experimental procedures adhered to the requirements outlined by ASTM. A comprehensive investigation was conducted on a range of concrete compositions that used diverse chemical admixtures. The slump test was performed at regular intervals of 15 minutes until the slump value reached or fell below 3 cm after the mixing of the concrete. In the scenario involving two-stage admixture dosage, the second stage of admixture was introduced once the slump reached or dropped below 3 cm, following which the casting process was initiated. The process of curing concrete specimens consists of two distinct stages: the main stage and the final stage. Cylindrical specimens, with a diameter of 4 inches and a height of 8 inches, were manufactured for the purpose of evaluating their compressive strength at both 7 and 28 days. During the experimental trials, the water-cement (w/c) ratio was kept consistent, while different dosages of admixture were applied. The findings of the study indicate that the utilization of a two-stage dose of admixture resulted in enhanced and extended workability, along with higher strength of the concrete in comparison to specimens that did not incorporate any admixture. This research study enhances the comprehension of optimizing qualities of ready-mix concrete (RMC) by varying the superplasticizer, providing useful insights for the building sector.
文摘Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.
文摘An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosages in terms of Al2O3, these substances are ranged in the following order in respect of inhibiting effect: Al(OH)1.78(SO4)0.61 ≥ Al2(SO4)3 > Al(OH)3. It is found that the plasticizing agents of the main types used in cement compositions have no influence on the inhibiting effect of aluminum-bearing admixtures. To control the setting time of cement paste, iron(II) sulphate may be used for partial substitution of Al2SO4·18H2O, and this operation is not influence on the results of ASR expansion test.