Based on the experimental results of the ratcheting for SS304 stainless steel, a new visco-plastic cyclic constitutive model was established to describe the uniaxial and multiaxial ratcheting of the material at room a...Based on the experimental results of the ratcheting for SS304 stainless steel, a new visco-plastic cyclic constitutive model was established to describe the uniaxial and multiaxial ratcheting of the material at room and elevated temperatures within the framework of unified visco-plasticity. In the model, the temperature dependence of the ratcheting was emphasized, and the dynamic strain aging occurred in the temperature range of 4 00-600℃ for the material was taken into account particularly. Finally, the prediction capability of the developed model was checked by comparing to the corresponding experimental results.展开更多
A series of monotonic uniaxial tensile tests, strain-controlled and stress-controlled cyclic tests of SA508-3 steel were conducted from 25 to 350℃. Results showed that the steel exhibited temperature-dependent cyclic...A series of monotonic uniaxial tensile tests, strain-controlled and stress-controlled cyclic tests of SA508-3 steel were conducted from 25 to 350℃. Results showed that the steel exhibited temperature-dependent cyclic softening characteristic and obvious ratcheting behavior, and dynamic strain aging was observed in the range of 250-350℃. Based on experimental observations, a temperature-dependent cyclic plastic constitutive model was proposed by introducing the nonlinear cyclic softening and kinematic hardening rules, and the dynamic strain aging was also considered into the constitutive model. Comparisons between experiments and simulations were carded out to validate the proposed model at elevated temperature.展开更多
基金supported by the Theoretical Research Fund of Sichuan Province(No.03JY029-062-2)the Scientific Research Foundation for the Returned Overseas Chinese Scholars(SRF-ROCS),State Education Ministry of China(No.2003-406-01).
文摘Based on the experimental results of the ratcheting for SS304 stainless steel, a new visco-plastic cyclic constitutive model was established to describe the uniaxial and multiaxial ratcheting of the material at room and elevated temperatures within the framework of unified visco-plasticity. In the model, the temperature dependence of the ratcheting was emphasized, and the dynamic strain aging occurred in the temperature range of 4 00-600℃ for the material was taken into account particularly. Finally, the prediction capability of the developed model was checked by comparing to the corresponding experimental results.
基金Financial supports by the National Natural Science Foundation of China (No. 11572265)the distinguished Young Scholars of Sichuan (No. 2017JQ0019)the Science and Technology on Reactor System Design Technology Laboratory of China are appreciated
文摘A series of monotonic uniaxial tensile tests, strain-controlled and stress-controlled cyclic tests of SA508-3 steel were conducted from 25 to 350℃. Results showed that the steel exhibited temperature-dependent cyclic softening characteristic and obvious ratcheting behavior, and dynamic strain aging was observed in the range of 250-350℃. Based on experimental observations, a temperature-dependent cyclic plastic constitutive model was proposed by introducing the nonlinear cyclic softening and kinematic hardening rules, and the dynamic strain aging was also considered into the constitutive model. Comparisons between experiments and simulations were carded out to validate the proposed model at elevated temperature.