Effects of Rare Earths and Al on Structure and Performance of High Chromium Cast Iron Containing Wolfram

Effects of RE and Al on the structure, impact toughness, hardness, and wear resistance of high chromium cast iron containing wolfram were investigated. The results show that without modification the volume fraction of austenite is high and the carbide appears to be thick lath and the grain size is relatively large; proper modification using RE combined with Al can reduce volume fraction of residual austenite in the as-cast structure obviously, refine grain size of primary austenite notably, and make the morphology of carbide changing from thick lath to thin lath, rosette, and feather-like modification can also increase hardness, wear resistance and impact toughness of cast iron.

Effect of CaO and CaCO3 on Reduction Rate of Iron Ore Pellets Containing Carbon

The effect of metallurgical fluxes CaO and CaCO3 on the reduction rate of iron ore pellets containing carbon in nitrogen atmosphere has been studied by a weight-loss thermal balance. The experimental results showed that adding CaO or CaCO3 can promote reduction reaction as the added CaO or CaCO3 probably decrease the apparent activation energy of iron ore concentrate-carbon-CaO or CaCO3 reaction, and the reduction rate constant changes with mass percent of CaO and CaCO3. The kinetic analysis also showed that the rate-controlling step of the reaction is inner gas diffusion.

Effect of RE Modification and Heat Treatment on Formation and Growth of Thermal Fatigue Crack in Wear Resistant Cast Iron Containing Low Alloy

The formation and growth of thermal fatigue crack and the function of RE and heat treatment in wear resistance of cast iron containing low alloy were investigated,and it was analyzed in view of the activation energy for the crack′s propagation. The results show that the thermal fatigue cracks are mainly generated at eutectic carbides,and the cracks are grown by themselves spreading and joining each other. RE can improve the eutectic carbide′s morphology,inhibit the generation and propagation of thermal fatigue cracks,therefore,promote the activation energy for the crack′s propagation,and especially,which is more noticeable in case of the RE modification in combination with heat treatment.

Influence of Rare Earth on Wear Resistance of Wear Resistant Cast Iron Containing Low Alloy

The Influence of RE on wear resistance of wear resistant cast iron containing low alloy was studied by means of slide wear and impact wear test. Moreover, its microstructure and characteristics of wearing surface was analyzed. The experimental results show that RE can improve the wear resistance of wear resistant cast iron containing low alloy, especially for impact wear resistance. The optimum wear resistance of wear resistant cast iron containing low alloy modified by RE of 0.046% can be obtained by normalization at 950 ℃ for 3 h. Moreover, the coordinated effect of rare earths and heat treatment was also revealed in this paper.

REDUCTION BEHAVIOR OF IRON ORE PELLETS CONTAININGCARBON UNDER NON-ISOTHERMAL CONDITION

The reduction behavior of iron ore pellets containing carbon under non-isothermal condition in the temperature range from 573 to 1373 K was investigated in a laboratory scale setup. The test results show that carbon content has no obvious effect on reduction degree of composite pellets (C/O mole ratio=1.0) by CO in the temperature range from 573 to 1373 K under linear temperature-rising program; reduction degree of iron ore pellets containing carbon is large in 90%CO-10%CO2 mixture than that of in 100%CO atmosphere or in 80%CO-20%CO2 mixture; the s type temperature-rising program has a better effect than that of linear one in increasing the reduction degree; and reduction degree of slower linear temperature-rising program is greater than that of faster one, but the final reduction degrees, i.e., those at the highest temperature are about the same for various CO partial pressures or temperature-rising programs. The kinetic analysis also shows that the reduction of iron ore-carbon composite pellets by CO or CO-CO2 mixture under non-isothermal condition should be controlled by surface reaction, and the apparent reduction activation energy changes with the reduction progress under various test conditions.

Comprehensive Utilization of Paigeite Ore Using Iron Nugget Making Process

The feasibility of paigeite ore treatment with iron nugget making process is proved. The isothermal reduc- tion experiments at laboratory scale were carried out, using carbon bearing pellets which were made of boron contai- ning iron concentrate and pulverized coal mainly, from 1 623 to 1 723 K with different heating time. The results indi- cated that iron nugget making process depends mainly on heating time and temperature. And the iron nugget and slag can separate in a clean manner at 1 673 K for 15 min. For the iron nugget, the C content is 3.57% （mass percent） and B is 0. 065~ （mass percent）. The B203 content of slag is 20.01~/00, and the boron was concentrated into one phase which is identified as suanite （Mg2BaOs） during the solidification. With an extraction ratio of 80~ under the atmospheric conditions, the activity of boron in slag is good. The boron-rich slag can be used to extract boric or boric acid and alleviate the shortage of boron resource. Through series of calculation and analysis related, it can be conclu- ded that the recovery ratio of Fe and boron are about 98% and 97% respectively. The results show that this method is feasible and effective on the utilization of paigeite ore.