Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed ...Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed through EBSD technique and X-ray diffraction method. The rule of texture density for the a,ε and γ fibers was analyzed. When the total reduction was increased from 82.9% to 97.1%, the gradient of microstrueture and texture for A steel surface layer and center layer was found, {001}〈110〉 texture had higher intensity, and {001}〈110〉texture was changed to { 110 } 〈 001 〉 and { 112 } 〈 111 〉. The texture distribution with different reduction schedules for B steel was basically similar, but the Goss texture orientation density and volume fraction for B steel were higher, the hot rolling reduction schedule of C1 was effective for the formation of Goss texture. The research work was useful theoretical basis and reference data to develop electrical steel by thin slab continuous casting and direct rolling technology.展开更多
The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling（TSCR） process in the laboratory.The texture evolution rule was investigated during hot rolling and cold rolling.The t...The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling（TSCR） process in the laboratory.The texture evolution rule was investigated during hot rolling and cold rolling.The texture distribution of cold rolled strips with four kinds of cold rolling reduction schedules was observed through X-ray diffraction method,and the orientation density variation of 1/16 layer,1/8 layer,1/4 layer,and 1/2 layer in thickness was analyzed.The cold rolled texture of steel A with four kinds of cold rolling reduction schedules was mainly composed of α and γ fibers.Cold rolling reduction ratio of 70% was more beneficial for obtaining more γ fibers.The γ fiber texture orientation density of {111}01-1 and {111}1-1-2 was the largest on the 1/8 layer and 1/4 layer and the least on the 1/16 layer and 1/2 layer for steel B.The texture orientation density of {001}-{223}11-0 in the α fibers for steel C was increased,but the texture orientation density of {332}-{110}11-0 was low.展开更多
基金Item Sponsored by National Natural Science Foundation of China(50534020)
文摘Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed through EBSD technique and X-ray diffraction method. The rule of texture density for the a,ε and γ fibers was analyzed. When the total reduction was increased from 82.9% to 97.1%, the gradient of microstrueture and texture for A steel surface layer and center layer was found, {001}〈110〉 texture had higher intensity, and {001}〈110〉texture was changed to { 110 } 〈 001 〉 and { 112 } 〈 111 〉. The texture distribution with different reduction schedules for B steel was basically similar, but the Goss texture orientation density and volume fraction for B steel were higher, the hot rolling reduction schedule of C1 was effective for the formation of Goss texture. The research work was useful theoretical basis and reference data to develop electrical steel by thin slab continuous casting and direct rolling technology.
基金Item Sponsored by National Natural Science Foundation of China(50534020)
文摘The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling（TSCR） process in the laboratory.The texture evolution rule was investigated during hot rolling and cold rolling.The texture distribution of cold rolled strips with four kinds of cold rolling reduction schedules was observed through X-ray diffraction method,and the orientation density variation of 1/16 layer,1/8 layer,1/4 layer,and 1/2 layer in thickness was analyzed.The cold rolled texture of steel A with four kinds of cold rolling reduction schedules was mainly composed of α and γ fibers.Cold rolling reduction ratio of 70% was more beneficial for obtaining more γ fibers.The γ fiber texture orientation density of {111}01-1 and {111}1-1-2 was the largest on the 1/8 layer and 1/4 layer and the least on the 1/16 layer and 1/2 layer for steel B.The texture orientation density of {001}-{223}11-0 in the α fibers for steel C was increased,but the texture orientation density of {332}-{110}11-0 was low.