Chloromethylated poly(phthalazinone ether sulfone ketone) (CMPPESK) was prepared from poly(phthalazinone ether sulfone ketone) (PPESK) using chloromethyl octyl ethers (CMOE) with lower toxicity as chlorometh...Chloromethylated poly(phthalazinone ether sulfone ketone) (CMPPESK) was prepared from poly(phthalazinone ether sulfone ketone) (PPESK) using chloromethyl octyl ethers (CMOE) with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc) and chloroform. Quaternized poly(phthalazinone ether sulfone ketone) (QAPPESK) was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid (98%) and swollen in N,N-dimethylformamide (DMF). The vanadium redox flow battery (V-RFB) using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.展开更多
A novel series of poly(aryl ether sulfone ketone)s (PPESKs) containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were...A novel series of poly(aryl ether sulfone ketone)s (PPESKs) containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures (Tg) and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction (WAXD).展开更多
1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and ...1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.展开更多
Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (C...Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (CMPPESK),was prepared by using chioromethylether as chloromethylation agent.Then,poly(ethylene glycol) methyl ether methacrylate(PEGMA) was used as monomer to synthesize PPESK-g-P(PEGMA) by ATRP method under the catalysis of a cuprous chloride/2,2'-bipyridyl system.PPESK/PPESK-g-P(PEGMA) blend m...展开更多
基金partly financed by the Major State Basic Research Development Program of China(No.2003 CB615700)the National Natural Science Foundation of China(No.20604005).
文摘Chloromethylated poly(phthalazinone ether sulfone ketone) (CMPPESK) was prepared from poly(phthalazinone ether sulfone ketone) (PPESK) using chloromethyl octyl ethers (CMOE) with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone (NMP), N,N-dimethylacetamide (DMAc) and chloroform. Quaternized poly(phthalazinone ether sulfone ketone) (QAPPESK) was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid (98%) and swollen in N,N-dimethylformamide (DMF). The vanadium redox flow battery (V-RFB) using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.
文摘A novel series of poly(aryl ether sulfone ketone)s (PPESKs) containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures (Tg) and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction (WAXD).
基金the National Natural Science Foundation of China for financial support.
文摘1, 2-Diliydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in concentrated Sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one, and 4,4'-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and H-1-NMR.
基金supported by the"973"program of China(No.2009CB623402)Engineering Research Center of Ministry of Education of China(No.JD09011)
文摘Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (CMPPESK),was prepared by using chioromethylether as chloromethylation agent.Then,poly(ethylene glycol) methyl ether methacrylate(PEGMA) was used as monomer to synthesize PPESK-g-P(PEGMA) by ATRP method under the catalysis of a cuprous chloride/2,2'-bipyridyl system.PPESK/PPESK-g-P(PEGMA) blend m...