POLYCAPROLACTONE-POLY (ETHYLENE GLYCOL) BLOCK COPOLYMER Ⅲ DRUG RELEASE BEHAVIOR

The drug release behavior of degradable polymer--polycaprolactone-poly (ethyleneglycol)block copolymer(PCE) in vitro was investigated by using 5-Fluoro-uracil (5-Fu) asa model drug under a condition of pH 7. 4 at 37C. It is found that the release rate of 5-Fufrom PCE increased with increasing polyether content of the copolymer. The results showthat the increasing polyether content of the copolymer caused increasing hydrophilicity anddecreasing crystallinity of the PCE copolymer. Thus, the drug release behavior and thedegradable property of the PCE can be controlled by adjusting the composition of thecopolymer.

刚性聚芳醚腈合成与性能研究

用２，６二氟苯甲腈和间苯二酚为原料，在碱性条件下，于非质子极性溶剂中，通过溶液高温缩聚法制备聚芳醚腈［Ｐｏｌｙ（ｃｙａｎｏａｒｙｌｅｔｈｅｒ）ＰＣＥ］．并用ＩＲ、ＤＳＣ、ＴＧ、ＷＡＸＤ等手段对其结构及热性能、结晶行为进行了研究．结果表明，ＰＣＥ高聚物不仅具备较好的耐高温和耐热老化性能，而且具有较好的结晶性能．同时，用对比的方法，对ＰＣＥ的晶体结构进行了初步的探讨．

间苯二酚-2,6-二氟苯甲腈 - 酚酞三元共聚合成及表征

由亲核缩聚反应合成了间苯二酚Ｒｓ２，６二氟苯甲腈（ＤＦＢＮ）酚酞ＰＰｈ三元共聚物，并用ＩＲ、ＤＳＣ、ＴＧ和ＷＡＸＤ对其结构和性能进行了表征．结果表明：随ＰＰｈ／ＲＳ组成增加可得结晶或无定形聚芳醚腈，聚合物的玻璃化转变温度在１４８℃～２６０℃之间，但熔融温度逐渐下降，三元共聚物较酚酞聚芳醚均聚物有更好的耐溶剂性．

PLLA-r-PCL无规共聚物的结构调控及热学性能、力学性能和气体阻隔性能

文中制备出不同组分比的PLLA-r-PCL无规共聚物薄膜,研究了其热学性能、力学性能和气体阻隔性能,探讨气体阻隔性能与共聚物结构之间的关系。通过红外光谱仪和差示扫描量热仪测试了材料的结晶性能。研究表明,随着PCL组分的增加,材料的结晶度呈降低趋势,薄膜材料几乎完全处于无定形态。采用拉力试验机对薄膜的力学性能进行测定,相较于纯PLLA,PLLA-r-PCL30的断裂伸长率达到了611%,为PLLA的70倍。同时,采用压差法透气仪对薄膜的透气性能进行了全面的分析,相较于纯PLLA,在40℃时,PLLA-r-PCL30的CO2和O2透过系数分别提高了801%和523%;在5℃时,PLLA-r-PCL30的CO2/O2的透过比(α(CO2/O2))达到7.0,提高了115%;此外,20℃时PLLA-r-PCL30的H2O蒸汽透过率提高了354%。