Columnar-grained QSn6. 5-0. 1 alloy slabs with a width of 70 mm and thickness of 10 mm were fabricated by heating-cooling combined mold（ HCCM） horizontal continuous casting. The effects of process parameters on soli...Columnar-grained QSn6. 5-0. 1 alloy slabs with a width of 70 mm and thickness of 10 mm were fabricated by heating-cooling combined mold（ HCCM） horizontal continuous casting. The effects of process parameters on solidification microstructure,surface quality,composition segregation and mechanical properties were studied. The results showed that the slabs with good surface quality,excellent mechanical properties and no obvious segregation could be prepared at the melt casting temperature of 1 250 ℃,the heating-mold temperature of 1 150- 1 200℃,the cooling water flow rate of 600 L / h and the casting speed of 20- 80 mm / min. The slabs had the yield strength of 124- 155 MPa,the elongation rate of 46. 6%- 56. 3% and the surface roughness of 0. 22- 0. 55μm,which enabled them to be directly processed without subsequent milling surface. The ratio of Sn content in the surface to that in the core was 0. 83- 1. 10,with an average value close to 1. 0,and not obviously influenced by process parameters. When the casting speed increased from 20 to 80 mm / min,the grain size changed little if the other process parameters were the same. When the heating-mold temperature increased from 1 150 to 1 200℃,the grain size was obviously refined and became more uniform if the casting speed was the same. Within the range of the casting speed at which the columnar grain structure could be obtained,the columnar grain size was mainly influenced by the heating-mold temperature.展开更多
The calculation of elastic constants of Ag/Pd superlattice thin films by molecular dynamics simulations with many-body potentials is presented. It reveals that the elastic constants C11 and C55 increase with decreasin...The calculation of elastic constants of Ag/Pd superlattice thin films by molecular dynamics simulations with many-body potentials is presented. It reveals that the elastic constants C11 and C55 increase with decreasing modulation wavelength A of the films, which is consistent with experiments. However, the change of C11 and C55 with A is found to be around the values determined by a rule of mixture using bulk elastic constants of metals. No supermodulus effect is observed and it is due to cancellation between enhanced and reduced contributions to elastic constants from Ag and Pd layers subjected to compressive and tensile strains, respectively.展开更多
基金financial support from the National Key Technology Support Program of China(No.2011BAE23B03 )the National Natural Science Foundation of China(51504023)the China Scholarship Council Project(No.201506465055)
文摘Columnar-grained QSn6. 5-0. 1 alloy slabs with a width of 70 mm and thickness of 10 mm were fabricated by heating-cooling combined mold（ HCCM） horizontal continuous casting. The effects of process parameters on solidification microstructure,surface quality,composition segregation and mechanical properties were studied. The results showed that the slabs with good surface quality,excellent mechanical properties and no obvious segregation could be prepared at the melt casting temperature of 1 250 ℃,the heating-mold temperature of 1 150- 1 200℃,the cooling water flow rate of 600 L / h and the casting speed of 20- 80 mm / min. The slabs had the yield strength of 124- 155 MPa,the elongation rate of 46. 6%- 56. 3% and the surface roughness of 0. 22- 0. 55μm,which enabled them to be directly processed without subsequent milling surface. The ratio of Sn content in the surface to that in the core was 0. 83- 1. 10,with an average value close to 1. 0,and not obviously influenced by process parameters. When the casting speed increased from 20 to 80 mm / min,the grain size changed little if the other process parameters were the same. When the heating-mold temperature increased from 1 150 to 1 200℃,the grain size was obviously refined and became more uniform if the casting speed was the same. Within the range of the casting speed at which the columnar grain structure could be obtained,the columnar grain size was mainly influenced by the heating-mold temperature.
基金Supported by the National Natural Science Foundation of China under Grant Nos 50471010 and 50531040.
文摘The calculation of elastic constants of Ag/Pd superlattice thin films by molecular dynamics simulations with many-body potentials is presented. It reveals that the elastic constants C11 and C55 increase with decreasing modulation wavelength A of the films, which is consistent with experiments. However, the change of C11 and C55 with A is found to be around the values determined by a rule of mixture using bulk elastic constants of metals. No supermodulus effect is observed and it is due to cancellation between enhanced and reduced contributions to elastic constants from Ag and Pd layers subjected to compressive and tensile strains, respectively.