Copper electrolyte was purified by copper arsenite that was prepared with As2O3.And electrolysis experiments of purified electrolyte were carried out at 235 and 305 A/m2,respectively.The results show that the yield of...Copper electrolyte was purified by copper arsenite that was prepared with As2O3.And electrolysis experiments of purified electrolyte were carried out at 235 and 305 A/m2,respectively.The results show that the yield of copper arsenite is up to 98.64% when the molar ratio of Cu to As is 1.5 in the preparation of copper arsenite.The removal rates of Sb and Bi reach 74.11% and 65.60% respectively after copper arsenite is added in electrolyte.The concentrations of As,Sb and Bi in electrolyte nearly remain constant during electrolysis of 13 d.The appearances of cathode copper obtained at 235 and 305 A/m2 are slippery and even,and the qualification rate is 100% according to the Chinese standard of high-pure cathode copper(GB/T467-97).展开更多
The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu ...The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu to As was 2：1 and pH value of the neutralized wastewater was adjusted to 8.0 by sodium hydroxide. The arsenious acid solution and red residue were produced after copper arsenite mixed with water according to the ratio of liquid to solid of 4：1 and copper arsenite was reduced by SO2 at 60℃ for 1 h. The white powder was gained after the arsenious acid solution was evaporated and cooled. Copper sulfate solution was obtained after the red residue was leached by H2SO4 solution under the action of air. The results show that red residue is Cu3（SO3）2·2H2O and the white powder is As2O3. The leaching rate of Cu reaches 99.00% when the leaching time is 1.5 h, molar ratio of H2SO4 to Cu is 1.70, H2SO4 concentration is 24% and the leaching temperature is 80 ℃. The direct recovery rate of copper sulfate is 79.11% and the content of CuSOa·5H2O is up to 98.33% in the product after evaporating and cooling the copper sulfate solution.展开更多
基金Project(200501045) supported by Innovation Fund of Hubei Daye Nonferrous Metal Limited Company of China
文摘Copper electrolyte was purified by copper arsenite that was prepared with As2O3.And electrolysis experiments of purified electrolyte were carried out at 235 and 305 A/m2,respectively.The results show that the yield of copper arsenite is up to 98.64% when the molar ratio of Cu to As is 1.5 in the preparation of copper arsenite.The removal rates of Sb and Bi reach 74.11% and 65.60% respectively after copper arsenite is added in electrolyte.The concentrations of As,Sb and Bi in electrolyte nearly remain constant during electrolysis of 13 d.The appearances of cathode copper obtained at 235 and 305 A/m2 are slippery and even,and the qualification rate is 100% according to the Chinese standard of high-pure cathode copper(GB/T467-97).
文摘The solid sodium hydroxide neutralized acidic As-containing wastewater till pH value was 6. Green copper arsenite was prepared after copper sulfate was added into the neutralized wastewater when the molar ratio of Cu to As was 2：1 and pH value of the neutralized wastewater was adjusted to 8.0 by sodium hydroxide. The arsenious acid solution and red residue were produced after copper arsenite mixed with water according to the ratio of liquid to solid of 4：1 and copper arsenite was reduced by SO2 at 60℃ for 1 h. The white powder was gained after the arsenious acid solution was evaporated and cooled. Copper sulfate solution was obtained after the red residue was leached by H2SO4 solution under the action of air. The results show that red residue is Cu3（SO3）2·2H2O and the white powder is As2O3. The leaching rate of Cu reaches 99.00% when the leaching time is 1.5 h, molar ratio of H2SO4 to Cu is 1.70, H2SO4 concentration is 24% and the leaching temperature is 80 ℃. The direct recovery rate of copper sulfate is 79.11% and the content of CuSOa·5H2O is up to 98.33% in the product after evaporating and cooling the copper sulfate solution.