A sulphuric acid bake–leach method for the treatment of mixed copper-cobalt oxide minerals was investigated as an alternative to the reductive leaching method. Sulphuric acid bake-leach process of the mixed copper-co...A sulphuric acid bake–leach method for the treatment of mixed copper-cobalt oxide minerals was investigated as an alternative to the reductive leaching method. Sulphuric acid bake-leach process of the mixed copper-cobalt oxide ore was carried out by mixing the sample with sulphuric acid followed by baking of the mixture in a muffle furnace. Baking tests were conducted at different conditions such as temperature, time, and varying amounts of acid. The reacted samples were then subjected to water leaching at room temperature to determine the leachability of copper and cobalt from the baked material. The dissolutions of copper and cobalt were dependent on acid concentration with cobalt showing more sensitivity to the amount of acid. Both copper and cobalt were extracted from the baked material within short leaching times and without the addition of reducing agents. The outcome of this work has shown that the sulphuric acid bake-leach process is a possible alternative to the reductive leaching method for copper-cobalt oxide ores.展开更多
Electrochemical conversion of nitrate(NO_(3)~-) to ammonia(NH_(3)) can target two birds with one stone well, in NO_(3)^(-)-containing sewage remediation and sustainable NH_(3) production. However, single metalbased ca...Electrochemical conversion of nitrate(NO_(3)~-) to ammonia(NH_(3)) can target two birds with one stone well, in NO_(3)^(-)-containing sewage remediation and sustainable NH_(3) production. However, single metalbased catalysts are difficult to drive high-efficient NO_(3)~- removal due to the multi-electron transfer steps.Herein, we present a tandem catalyst with simple structure, Cu-Co binary metal oxides(Cu-Co-O), by engineering intermediate phases as catalytic active species for NO_(3)~- conversion. Electrochemical evaluation,X-ray photoelectron spectroscopy, and in situ Raman spectra together suggest that the newly-generated Cu-based phases was prone to NO_(3)~- to NO_(2)~- conversion, then NO_(2)~- was reduced to NH_(3) on Co-based species. At an applied potential of -1.1 V vs. saturated calomel electrode, the Cu-Co-O catalyst achieved NO_(3)~- -N removal of 90% and NH_(3) faradaic efficiency of 81% for 120 min in 100 m L of 50 mg/L NO_(3)~- -N,consuming only 0.69 k Wh/mol in a two-electrode system. This study provides a facile and efficient engineering strategy for developing high-performance catalysts for electrocatalytic nitrate conversion.展开更多
Cobalt has excellent electrochemical,magnetic,and heat properties.As a strategic resource,it has been applied in many hightech products.However,the recent rapid growth of the battery industry has substantially deplete...Cobalt has excellent electrochemical,magnetic,and heat properties.As a strategic resource,it has been applied in many hightech products.However,the recent rapid growth of the battery industry has substantially depleted cobalt resources,leading to a crisis of cobalt resource supply.The paper examines cobalt ore reserves and distribution,and the recent development and consumption of cobalt resources are summarized as well.In addition,the principles,advantages and disadvantages,and research status of various methods are discussed comprehensively.It can be concluded that the use of diverse sources(Cu-Co ores,Ni-Co ores,zinc plant residues,and waste cobalt products)for cobalt production should be enhanced to meet developmental requirements.Furthermore,in recovery technology,the pyro-hydrometallurgical process employs pyrometallurgy as the pretreatment to modify the phase structure of cobalt minerals,enhancing its recovery in the hydrometallurgical stage and facilitating high-purity cobalt production.Consequently,it represents a promising technology for future cobalt recovery.Lastly,based on the above conclusions,the prospects for cobalt are assessed regarding cobalt ore processing and sustainable cobalt recycling,for which further study should be conducted.展开更多
文摘A sulphuric acid bake–leach method for the treatment of mixed copper-cobalt oxide minerals was investigated as an alternative to the reductive leaching method. Sulphuric acid bake-leach process of the mixed copper-cobalt oxide ore was carried out by mixing the sample with sulphuric acid followed by baking of the mixture in a muffle furnace. Baking tests were conducted at different conditions such as temperature, time, and varying amounts of acid. The reacted samples were then subjected to water leaching at room temperature to determine the leachability of copper and cobalt from the baked material. The dissolutions of copper and cobalt were dependent on acid concentration with cobalt showing more sensitivity to the amount of acid. Both copper and cobalt were extracted from the baked material within short leaching times and without the addition of reducing agents. The outcome of this work has shown that the sulphuric acid bake-leach process is a possible alternative to the reductive leaching method for copper-cobalt oxide ores.
基金supported by National Natural Science Foundation of China (Nos.52131003 and 42007180)Special Research Assistant Program of Chinese Academy of Science, Natural Science Foundation of Chongqing (No.cstc2020jcyj-msxm X0775)+1 种基金Scientific Research Instrument Development Project of Chinese Academy of Sciences (No.YJKYYQ20200044)Outstanding Scientist of Chongqing Talent Program (No.CQYC20210101288)。
文摘Electrochemical conversion of nitrate(NO_(3)~-) to ammonia(NH_(3)) can target two birds with one stone well, in NO_(3)^(-)-containing sewage remediation and sustainable NH_(3) production. However, single metalbased catalysts are difficult to drive high-efficient NO_(3)~- removal due to the multi-electron transfer steps.Herein, we present a tandem catalyst with simple structure, Cu-Co binary metal oxides(Cu-Co-O), by engineering intermediate phases as catalytic active species for NO_(3)~- conversion. Electrochemical evaluation,X-ray photoelectron spectroscopy, and in situ Raman spectra together suggest that the newly-generated Cu-based phases was prone to NO_(3)~- to NO_(2)~- conversion, then NO_(2)~- was reduced to NH_(3) on Co-based species. At an applied potential of -1.1 V vs. saturated calomel electrode, the Cu-Co-O catalyst achieved NO_(3)~- -N removal of 90% and NH_(3) faradaic efficiency of 81% for 120 min in 100 m L of 50 mg/L NO_(3)~- -N,consuming only 0.69 k Wh/mol in a two-electrode system. This study provides a facile and efficient engineering strategy for developing high-performance catalysts for electrocatalytic nitrate conversion.
基金the financial support of Guangxi Science and Technology Major Project(Guike AA22068078)the Natural Science Foundation of Henan Province(No.222300420548)+2 种基金Henan Province Science and Technology Research and Development plan joint Fund(No.232301420043)the Key Project of the National Key Research and Development Program of China(No.2021YFC2902604)Modern Analysis and Computing Centre in Zhengzhou University。
文摘Cobalt has excellent electrochemical,magnetic,and heat properties.As a strategic resource,it has been applied in many hightech products.However,the recent rapid growth of the battery industry has substantially depleted cobalt resources,leading to a crisis of cobalt resource supply.The paper examines cobalt ore reserves and distribution,and the recent development and consumption of cobalt resources are summarized as well.In addition,the principles,advantages and disadvantages,and research status of various methods are discussed comprehensively.It can be concluded that the use of diverse sources(Cu-Co ores,Ni-Co ores,zinc plant residues,and waste cobalt products)for cobalt production should be enhanced to meet developmental requirements.Furthermore,in recovery technology,the pyro-hydrometallurgical process employs pyrometallurgy as the pretreatment to modify the phase structure of cobalt minerals,enhancing its recovery in the hydrometallurgical stage and facilitating high-purity cobalt production.Consequently,it represents a promising technology for future cobalt recovery.Lastly,based on the above conclusions,the prospects for cobalt are assessed regarding cobalt ore processing and sustainable cobalt recycling,for which further study should be conducted.