Copper-cobalt Bimetallic Oxides-doped Alumina Hollow Spheres: a Highly Efficient Catalyst for Epoxidation of Styrene

Copper-cobalt bimetallic oxides-doped alumina hollow spheres(CuCo/AHS)were labricatcd through the sacrificial carbonaceous template strategy.The dependence of the physicochemical properties and morphologies of CuCo/AHS on the composition of copper and cobalt in CuxCoy/AHS(x/y=9/1,7/3,5/5,and 3/7)was characterized bv means of X-ray powder diffraction,nitrogen physisorption,atomic adsorption spectroscopy,scanning electron microscopy,transmission electron microscopy and X-ray photoelectron spectroscopy.Among these catalysts, Cu7-Co3/AHS catalyst exhibited perfect hollow sphere structure,thin wall,and big pore size.The calcined catalysts were examined for the epoxidation of styrene with tert-butyl hydroperoxide as oxidant.Compared with the monometallic counterparts(Cu/AHS and Co/AHS)and other CuxCoy/AHS catalysts,Cu7Co3/AHS catalyst showed higher performance,yielding a styrene conversion of 64.6% with 93.0% selectivity toward styrene oxide.In addition,the strong interaction of Cu^2+or Co^2+ with AHS ensured good stability after four consecutive reactions.

Synergistic catalysis of the N-hydroxyphthalimide on flower-like bimetallic metal-organic frameworks for boosting oxidative desulfurization

Synergic catalytic effect between active sites and supports greatly determines the catalytic activity for the aerobic oxidative desulfurization of fuel oils.In this work,Ni-doped Co-based bimetallic metal-organic framework(CoNi-MOF)is fabricated to disperse N-hydroxyphthalimide(NHPI),in which the whole catalyst provides plentiful synergic catalytic effect to improve the performance of oxidative desulfurization(ODS).As a bimetallic MOF,the second metal Ni doping results in the flower-like morphology and the modification of electronic properties,which ensure the exposure of NHPI and strengthen the synergistic effect of the overall catalyst.Compared with the monometallic Co-MOF and naked NHPI,the NHPI@CoNi-MOF triggers the efficient activation of molecular oxygen and improves the ODS performance without an initiator.The sulfur removal of dibenzothiophene-based model oil reaches 96.4%over the NHPI@CoNi-MOF catalyst in 8 h of reaction.Furthermore,the catalytic product of this aerobic ODS reaction is sulfone,which is adsorbed on the catalyst surface due to the difference in polarity.This work provides new insight and strategy for the design of a strong synergic catalytic effect between NHPI and bimetallic supports toward high-activity aerobic ODS materials.

Graphene-loaded nickel−vanadium bimetal oxides as hydrogen pumps to boost solid-state hydrogen storage kinetic performance of magnesium hydride

To modify the thermodynamics and kinetic performance of magnesium hydride(MgH_(2))for solid-state hydrogen storage,Ni_(3)V_(2)O_(8)-rGO(rGO represents reduced graphene oxide)and Ni_(3)V_(2)O_(8)nanocomposites were prepared by hydrothermal and subsequent heat treatment.The beginning hydrogen desorption temperature of 7 wt.%Ni_(3)V_(2)O_(8)-rGO modified MgH_(2)was reduced to 208℃,while the additive-free MgH_(2)and 7 wt.%Ni_(3)V_(2)O_(8)doped MgH_(2)appeared to discharge hydrogen at 340 and 226℃,respectively.A charging capacity of about 4.7 wt.%H_(2)for MgH_(2)+7 wt.%Ni_(3)V_(2)O_(8)-rGO was achieved at 125℃ in 10 min,while the dehydrogenated MgH_(2)took 60 min to absorb only 4.6 wt.%H_(2)at 215℃.The microstructure analysis confirmed that the in-situ generated Mg_(2)Ni/Mg_(2)N_(i)H_(4) and metallic V contributed significantly to the enhanced performance of MgH_(2).In addition,the presence of rGO in the MgH_(2)+7 wt.%Ni_(3)V_(2)O_(8)-rGO composite reduced particle aggregation tendency of Mg/MgH_(2),leading to improving the cyclic stability of MgH_(2)during 20 cycles.

Bimetallic Cr-In/H-SSZ-13 for selective catalytic reduction of nitric oxide by methane

Bimetallic Cr-In/H-SSZ-13 zeolites were prepared by wet impregnation and investigated for selective catalytic reduction of nitric oxide by methane(CH4-SCR).Reduction-oxidation treatments led to close contact and interaction between Cr and In species in these zeolites,as revealed by transmission electron microscopy and X-ray photoelectron spectroscopy.Compared to monometallic Cr/H-SSZ-13 and In/H-SSZ-13,the bimetallic catalyst system exhibited dramatically enhanced CH4-SCR performance,i.e.,NO conversion greater than 90%and N2 selectivity greater than 99%at 550°C in the presence of 6%H2O under a high gas hourly space velocity of 75 000/h.The bimetallic Cr-In/H-SSZ-13 showed very good stability in CH4-SCR with no significant activity loss for over 160 h.Catalytic data revealed that CH4 and NO were activated on the In and Cr sites of Cr-In/H-SSZ-13,respectively,both in the presence of O2 during CH4-SCR.

Metal–Oleate Complex?Derived Bimetallic Oxides Nanoparticles Encapsulated in 3D Graphene Networks as Anodes for Efficient Lithium Storage with Pseudocapacitance

In this manuscript, we have demonstrated the delicate design and synthesis of bimetallic oxides nanoparticles derived from metal–oleate complex embedded in 3D graphene networks(MnO/CoMn_2O_4  GN), as an anode material for lithium ion batteries. The novel synthesis of the MnO/CoMn_2O_4  GN consists of thermal decomposition of metal–oleate complex containing cobalt and manganese metals and oleate ligand, forming bimetallic oxides nanoparticles, followed by a selfassembly route with reduced graphene oxides. The MnO/CoMn_2O_4  GN composite, with a unique architecture of bimetallic oxides nanoparticles encapsulated in 3D graphene networks, rationally integrates several benefits including shortening the di usion path of Li^+ ions, improving electrical conductivity and mitigating volume variation during cycling. Studies show that the electrochemical reaction processes of MnO/Co Mn_2O_4  GN electrodes are dominated by the pseudocapacitive behavior, leading to fast Li^+ charge/discharge reactions. As a result, the MnO/CoMn_2O_4  GN manifests high initial specific capacity, stable cycling performance, and excellent rate capability.

Phase separation-hydrogen etching-derived Cu-decorated Cu-Mn bimetallic oxides with oxygen vacancies boosting superior sodium-ion storage kinetics

Understanding the crystal phase evolution of bimetallic oxide anodes is the main concern to profoundly reveal the conversion reaction kinetics and sodium-ion storage mechanisms.Herein,an integrated selfsupporting anode of the Cu-decorated Cu-Mn bimetallic oxides with oxygen vacancies(Ov-BMO-Cu)are in-situ generated by phase separation and hydrogen etching using nanoporous Cu-Mn alloy as selfsacrificial templates.On this basis,we have elucidated the relationship between the phase evolution,oxygen vacancies and sodium-ion storage mechanisms,further demonstrating the evolution of oxygen vacancies and the inhibition effect of manganese oxides as an“anchor”on grain aggregation of copper oxides.The kinetic analyses confirm that the expanded lattice space and increased oxygen vacancies of cycled Ov-BMO-Cu synergistically guarantee effective sodium-ion diffusion and storage mechanisms.Therefore,the Ov-BMO-Cu electrode exhibits higher reversible capacities of 4.04 mA h cm^(-2)at 0.2 mA cm^(-2)after 100 cycles and 2.20 m A h cm^(-2)at 1.0 mA cm^(-2)after 500 cycles.Besides,the presodiated Ov-BMO-Cu anode delivers a considerable reversible capacity of 0.79 m A h cm^(-2)at 1.0 mA cm^(-2)after 60 cycles in full cells with Na_(3)V_(2)(PO_(4))_(3)cathode,confirming its outstanding practicality.Thus,this work is expected to provide enlightenment for designing high-capacity bimetallic oxide anodes.

Selective suppression of toluene formation in solvent-free benzyl alcohol oxidation using supported Pd-Ni bimetallic nanoparticles

The solvent‐free oxidation of benzyl alcohol was studied using supported Pd‐Ni bimetallic nanoparticles.Compared with monometallic Pd,the addition of Ni to Pd was found to be effective in suppressing the nondesired product toluene,thereby enhancing the selectivity towards benzaldehyde.This result was attributed to a dual effect of Ni addition:the weakening of dissociative adsorption of benzyl alcohol and the promotion of oxygen species involved in the oxidation pathway.

Advancements in transition bimetal catalysts for electrochemical 5-hydroxymethylfurfural(HMF) oxidation

The electrochemical oxidation of 5-hydroxymethylfurfural(HMF) represents a significant avenue for sustainable chemical synthesis, owing to its potential to generate high-value derivatives from biomass feedstocks. Transition metal catalysts offer a cost-effective alternative to precious metals for catalyzing HMF oxidation, with transition bimetallic catalysts emerging as particularly promising candidates. In this review, we delve into the intricate reaction pathways and electrochemical mechanisms underlying HMF oxidation, emphasizing the pivotal role of transition bimetallic catalysts in enhancing catalytic efficiency. Subsequently, various types of transition bimetallic catalysts are explored, detailing their synthesis methods and structural modulation strategies. By elucidating the mechanisms behind catalyst modification and performance enhancement, this review sets the stage for upcoming advancements in the field, ultimately advancing the electrochemical HMF conversion and facilitating the transition towards sustainable chemical production.

Base-free aerobic oxidation of glycerol on TiO_2-supported bimetallic Au–Pt catalysts

The aerobic oxidation of glycerol provides an economically viable route to glyceraldehyde, dihydroxyacetone and glyceric acid with versatile applications, for which monometallic Pt, Au and Pd and bimetallic Au-Pt, Au- Pd and Pt-Pd catalysts on TiO2 were examined under base-free conditions. Pt exhibited a superior activity relative to Pd, and Au-Pd and Pt-Pd while Au was essentially inactive. The presence of Au on the Au-Pt/TiO2 catalysts led to their higher activities （normalized per Pt atom） in a wide range of Au/Pt atomic ratios （i.e. 1/3-7/1 ）, and the one with the Au/Pt ratio of 3/1 exhibited the highest activity. Such promoting effect is ascribed to the increased electron density on Pt via the electron transfer from Au to Pt, as characterized by the temperature-programmed desorption of CO and infra-red spectroscopy for CO adsorption. Meanwhile, the presence of Au on Au-Pt/TiO2, most like due to the observed electron transfer, changed the product selectivity, and facilitated the oxidation of the secondary hydroxyl groups in glycerol, leading to the favorable formation of dihydroxyacetone over glyceraldehyde and glyceric acid that were derived from the oxidation of the primary hydroxyl groups. The synergetic effect between Au and Pt demonstrates the feasibility in the efficient oxidation of glycerol to the targeted products, for example, by rational tuning of the electronic properties of metal catalysts.

Improvement of ionic conductivity of solid polymer electrolyte based on Cu-Al bimetallic metal-organic framework fabricated through molecular grafting

A composite solid electrolyte comprising a Cu-Al bimetallic metal-organic framework(CAB),lithium salt(LiTFSI)and polyethylene oxide(PEO)was fabricated through molecular grafting to enhance the ionic conductivity of the PEO-based electrolytes.Experimental and molecular dynamics simulation results indicated that the electrolyte with 10 wt.%CAB(PL-CAB-10%)exhibits high ionic conductivity(8.42×10~(-4)S/cm at 60℃),high Li+transference number(0.46),wide electrochemical window(4.91 V),good thermal stability,and outstanding mechanical properties.Furthermore,PL-CAB-10%exhibits excellent cycle stability in both Li-Li symmetric battery and Li/PL-CAB-10%/LiFePO4 asymmetric battery setups.These enhanced performances are primarily attributable to the introduction of the versatile CAB.The abundant metal sites in CAB can react with TFSI~-and PEO through Lewis acid-base interactions,promoting LiTFSI dissociation and improving ionic conductivity.Additionally,regular pores in CAB provide uniformly distributed sites for cation plating during cycling.

Bimetallic CoNi single atoms supported on three-dimensionally ordered mesoporous chromia:highly active catalysts for n-hexane combustion

Developing the alternative supported noble metal catalysts with low cost,high catalytic efficiency,and good resistance toward carbon dioxide and water vapor is critically demanded for the oxidative removal of volatile organic compounds(VOCs).In this work,we prepared the mesoporous chromia-supported bimetallic Co and Ni single-atom(Co_(1)Ni_(1)/meso-Cr_(2)O_(3))and bimetallic Co and Ni nanoparticle(Co_(NP)Ni_(NP)/mesoCr_(2)O_(3))catalysts adopting the one-pot polyvinyl pyrrolidone(PVP)-and polyvinyl alcohol(PVA)-protecting approaches,respectively.The results indicate that the Co_(1)Ni_(1)/meso-Cr_(2)O_(3)catalyst exhibited the best catalytic activity for n-hexane(C_(6)H_(14))combustion(T_(50%)and T_(90%)were 239 and 263℃ at a space velocity of 40,000 mL g^(-1)h^(-1);apparent activation energy and specific reaction rate at 260℃ were 54.7 kJ mol^(-1)and 4.3×10^(-7)mol g^(-1)_(cat)s^(-1),respectively),which was associated with its higher(Cr^(5+)+Cr^(6+))amount,large n-hexane adsorption capacity,and good lattice oxygen mobility that could enhance the deep oxidation of n-hexane,in which Ni_(1) was beneficial for the enhancements in surface lattice oxygen mobility and low-temperature reducibility,while Co_(1) preferred to generate higher contents of the high-valence states of chromium and surface oxygen species as well as adsorption and activation of n-hexane.n-Hexane combustion takes place via the Mars van Krevelen(MvK)mechanism,and its reaction pathways are as follows:n-hexane→olefins or 3-hexyl hydroperoxide→3-hexanone,2-hexanone or 2,5-dimethyltetrahydrofuran→2-methyloxirane or 2-ethyl-oxetane→acrylic acid→CO_x→CO_(2)and H_(2)O.

Pt–Pd bimetallic nanoparticles anchored on uniform mesoporous MnO_(2) sphere as an advanced nanocatalyst for highly efficient toluene oxidation

Improving catalytic performance is a yet still challenge in thermal catalytic oxidation.Herein,uniform mesoporous MnO_(2) nanospheresupported bimetallic Pt–Pd nanoparticles were successfully fabricated via a SiO_(2) template strategy for the total catalytic degradation of volatile organic compounds at low temperature.The introduction of mesopores into the MnO_(2) support induces a large specific surface area and pore size,thus providing numerous accessible active sites and enhanced diffusion properties.Moreover,the addition of a secondary noble metal can adjust the O_(ads)/O_(latt) molar ratios,resulting in high catalytic activity.Among them,the catalyst having a Pt/Pd molar ratio of 7:3 exhibits optimized catalytic activity at a weight hourly space velocity of 36,000 mL g^(-1) h^(-1),reaching 100%toluene oxidation at 175℃ with a lower activation energy(57.0 kJ mol^(-1))than the corresponding monometallic Pt or non-Pt-based catalysts(93.8 kJ mol^(-1) and 214.2 kJ mol^(-1)).Our findings demonstrate that the uniform mesoporous MnO_(2) nanosphere-supported bimetallic Pt–Pd nanoparticles catalyst is an effective candidate for application in elimination of toluene.

Bimetallic Pt–Ru covalently bonded on carbon nanotubes for efficient methanol oxidation

Platinum-based nanocomposites have been considered as one of the most promising catalysts for methanol oxidation reactions(MORs), which yet still suffer from low electrochemical activity and electron-transfer properties. Apart from van-der-Waals heterostructures,herein, we report a novel nanocomposite with the structure of Pt–Ru bimetallic nanoparticles covalently-bonded onto multi-walled carbon nanotubes (MWCNTs)(Pt–Ru@MWCNT), which have been successfully fabricated via a facile and green synthesis method. It is demonstrated that the Pt–Ru@MWCNT nanocomposite possesses much enhanced electrocatalytic activity with the electrochemical active surface area(ECSA) of 110.4 m^(2)·g^(-1)for Pt towards MOR, which is 2.67 and 4.0 times higher than those of 20wt%commercial Pt@C and Pt-based nanocomposite prepared by other method, due to the improved electron-transfer properties originated from M–O–C covalent bonds. This work provides us a new strategy for the structural design of highly-efficient electrocatalysts in boosting MOR performance.

Bimetallic water oxidation: One-site catalysis with two-sites oxidation

Water oxidation is the key half reaction to achieve full splitting of water to hydrogen and oxygen.Herein,a binuclear complex,[(L^(4-))Co_(2)~Ⅲ(OH)]ClO_(4),was reported as a stable and efficient homogenous catalyst for electrocatalytic water oxidation in 0.1 M phosphate buffer(pH 7.0).Cyclic voltammetry experiments indicated that the catalytic process proceed via "one-site catalysis with two-sites oxidation" mechanism in which both two metal sites store the required oxidation equivalents for water oxidation and O-O bond formation occurs by single-site water nucleophilic attack(WNA).

An examination of active sites on Au-Ag bimetallic catalysts based on CO oxidation over Au/Ag_2O and a comparison to Ag-contaminated Au powder

There are two theories regarding the origin of the remarkable synergistic effect observed in Au‐Ag bimetallic catalysts when applied to various oxidative reactions. One is based on the importance of the contact interfaces between AgOx regions and the surface of the bulk Au as active working sites, while the other holds that charge transfer from Ag to Au in a surface Au‐Ag alloy causes the catalytic activity. One key point in examining these theories and determining the origin of the synergy in‐volves determining whether or not Ag exists as an oxide or as a metallic alloy on the Au surface. To confirm that enhanced activity results from contact between Ag2O and Au nanoparticles （NPs）, a comparative study of catalytic CO oxidation over Au/Ag2O and Ag2O was performed in the present work, using a closed recirculation reaction system. A reaction mixture consisting of a stoichiometric composition of CO and O2 （CO/O2=2/1） was supplied to both catalysts and the resulting pressure decrease rates were tracked, from which the amounts of gas consumed as well as the quantity of CO2 produced were determined. The steady state reactions of both Au/Ag2O and Ag2O did not lead to any meaningful difference in the rate of pressure decrease during the oxidation. The pressure decrease over both catalysts was attributed to the reduction of surface lattice O on Ag2O by CO. The results obtained for Au/Ag2O are in good agreement with previous data resulting from the use of Ag‐contaminated Au powder （Ag/Au‐b） having an oxidized surfaces. This finding suggests that the perimeters between AgOx zones and the bulk Au surface may not function as active sites during CO oxidation. A review of previous results obtained with Ag/Au‐b specimens having so‐called steady state surfaces indicates that AgOx species in such materials are reduced to the 0 state to form a Ag‐Au alloy that provides the active sites.

Sulphuric Acid Bake-Leach Process for the Treatment of Mixed Copper-Cobalt Oxide Ores

A sulphuric acid bake–leach method for the treatment of mixed copper-cobalt oxide minerals was investigated as an alternative to the reductive leaching method. Sulphuric acid bake-leach process of the mixed copper-cobalt oxide ore was carried out by mixing the sample with sulphuric acid followed by baking of the mixture in a muffle furnace. Baking tests were conducted at different conditions such as temperature, time, and varying amounts of acid. The reacted samples were then subjected to water leaching at room temperature to determine the leachability of copper and cobalt from the baked material. The dissolutions of copper and cobalt were dependent on acid concentration with cobalt showing more sensitivity to the amount of acid. Both copper and cobalt were extracted from the baked material within short leaching times and without the addition of reducing agents. The outcome of this work has shown that the sulphuric acid bake-leach process is a possible alternative to the reductive leaching method for copper-cobalt oxide ores.

NO Adsorption on Ag/Pt（110）-（1×2） Bimetallic Surfaces： Unexpected Formation of Nitrite/nitrate Surface Species

NO adsorption on Ag/Pt（110）-（1×2） bimetallic surfaces at room temperature was investigated by means of Auger electron spectroscopy, X-ray photoelectron spectroscopy and thermal desorption spectroscopy. An unexpected formation of nitrite/nitrate surface species on Ag/Pt（110）-（1 ×2） bimetallic surfaces is observed, then decompose at elevated temperatures to form N2. However, such nitrite/nitrate surface species do not form on clean Pt（110） and Ag-Pt alloy surfaces upon NO exposure at room temperature. The formation of nitrite/nitrate surface species on Ag/Pt（110）-（1×2） bimetallic surfaces is attributed to high reactivity of highly coordination-unsaturated Ag clusters and the synergetic effect between Ag clusters and Pt substrate.

Pt-Re/rGO bimetallic catalyst for highly selective hydrogenation of cinnamaldehyde to cinnamylalcohol

In the present work, a series of Pt-based catalysts, alloyed with a second metal, i.e., Re, Sn, Er, La, and Y, and supported on activated carbon, ordered mesoporous carbon, N-doped mesoporous carbon or reduced graphene oxide(rGO), have been developed for selective hydrogenation of cinnamaldehyde to cinnamylalcohol. Re and rGO were proved to be the most favorable metal dopant and catalyst support, respectively. Pt_(50) Re_(50)/rGO showed the highest cinnamylalcohol selectivity of 89% with 94% conversion of cinnamaldehyde at the reaction conditions of 120 °C, 2.0 MPaH_2 and 4 h.

Advances in Noble Metal-Decorated Metal Oxide Nanomaterials for Chemiresistive Gas Sensors:Overview

Highly sensitive gas sensors with remarkably low detection limits are attractive for diverse practical application fields including real-time environmental monitoring,exhaled breath diagnosis,and food freshness analysis.Among various chemiresistive sensing materials,noble metal-decorated semiconducting metal oxides(SMOs)have currently aroused extensive attention by virtue of the unique electronic and catalytic properties of noble metals.This review highlights the research progress on the designs and applications of different noble metal-decorated SMOs with diverse nanostructures(e.g.,nanoparticles,nanowires,nanorods,nanosheets,nanoflowers,and microspheres)for high-performance gas sensors with higher response,faster response/recovery speed,lower operating temperature,and ultra-low detection limits.The key topics include Pt,Pd,Au,other noble metals(e.g.,Ag,Ru,and Rh.),and bimetals-decorated SMOs containing ZnO,SnO_(2),WO_(3),other SMOs(e.g.,In_(2)O_(3),Fe_(2)O_(3),and CuO),and heterostructured SMOs.In addition to conventional devices,the innovative applications like photo-assisted room temperature gas sensors and mechanically flexible smart wearable devices are also discussed.Moreover,the relevant mechanisms for the sensing performance improvement caused by noble metal decoration,including the electronic sensitization effect and the chemical sensitization effect,have also been summarized in detail.Finally,major challenges and future perspectives towards noble metal-decorated SMOs-based chemiresistive gas sensors are proposed.

Synthesis and catalytic property of Cu-Mn-Ce/γ-Al_2O_3 complex oxide

A new type of catalytic material for purification of automobile exhaust, Cu Mn Ce O/ γ Al 2O 3, has been studied. The factors affecting its catalytic activity, such as calcination temperature and the period of calcinations and so on have been investigated. Its catalytic activity after SO 2 poisoning was determined in a fixed bed reactor by exposing the sample to the atmosphere of 160?mL/min SO 2/air. The study reveals that the catalyst has shown high catalytic activities for the conversion of NH 3 oxidation by NO after sulfate. The conversion of NO reduction over the sulfated catalyst is somewhat higher than that over the fresh catalyst except that the optimum temperature has increased about 100?℃. Also at the optimum process for the experiment, the selective catalytic oxidation of CO by NO is over 76% and the conversion of NO reduction is over 80% by NH 3.