To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstr...To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically studied by heating microscope, X-ray diffraction, scanning electronic microscope and thermal analysis. Properties（physical properties, electrical properties and coefficient of thermal expansion（CTE）） were tested for comprehensive performance evaluation. The results showed that the utilization of poor quality kaolin broadened the firing range of cordierite ceramic which was from 1 200 to 1 380 ℃. Microstructure becomes loose with increasing of the pore size, which had significant influence on bending strength and electrical properties. High content of K2 O in poor quality kaolin was the reason for liquid phase generation in sintering process, which further leads to microstructural changes. The cordierite ceramic sintered at 1 320 ℃ had the properties as follows： CTE of 1.98×10^（-6） ℃^（-1）（500 ℃）, bending strength of 90 MPa, apparent porosity of 15.1%, dielectric constant of 7.5（100 Hz）, and volume resistivity of 1.05×109 Ω·cm（100 Hz）. The comprehensive properties are very suitable for use as electric heater supports.展开更多
Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the s...Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the surface acid-base properties of catalysts by introduction of alkali metal （Na, K） oxides inhibits the carbonization and as a result, improves the operational stability of these catalysts. An effect of promotion of nickel-alumina based composite doped by lanthanum oxide is found. This effect, caused by an additional route for the CO2 activation on Ni-La2O3/Al2O3/cordierite catalyst, is displayed in increase of methane conversion under conditions of an oxidant excess.展开更多
基金Funded by the Major State Basic Research Development Program of China(973 Program)(No.2010CB227105)
文摘To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically studied by heating microscope, X-ray diffraction, scanning electronic microscope and thermal analysis. Properties（physical properties, electrical properties and coefficient of thermal expansion（CTE）） were tested for comprehensive performance evaluation. The results showed that the utilization of poor quality kaolin broadened the firing range of cordierite ceramic which was from 1 200 to 1 380 ℃. Microstructure becomes loose with increasing of the pore size, which had significant influence on bending strength and electrical properties. High content of K2 O in poor quality kaolin was the reason for liquid phase generation in sintering process, which further leads to microstructural changes. The cordierite ceramic sintered at 1 320 ℃ had the properties as follows： CTE of 1.98×10^（-6） ℃^（-1）（500 ℃）, bending strength of 90 MPa, apparent porosity of 15.1%, dielectric constant of 7.5（100 Hz）, and volume resistivity of 1.05×109 Ω·cm（100 Hz）. The comprehensive properties are very suitable for use as electric heater supports.
文摘Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the surface acid-base properties of catalysts by introduction of alkali metal （Na, K） oxides inhibits the carbonization and as a result, improves the operational stability of these catalysts. An effect of promotion of nickel-alumina based composite doped by lanthanum oxide is found. This effect, caused by an additional route for the CO2 activation on Ni-La2O3/Al2O3/cordierite catalyst, is displayed in increase of methane conversion under conditions of an oxidant excess.