This study explores the fabrication of Fe-based amorphous/crystalline coating by air plasma spraying and its dependency on the coating parameters(plasma power,primary gas flow rate,powder feed rate,and stand-off dista...This study explores the fabrication of Fe-based amorphous/crystalline coating by air plasma spraying and its dependency on the coating parameters(plasma power,primary gas flow rate,powder feed rate,and stand-off distance).X-ray diffraction of the coatings deposited at optimized spray parameters showed the presence of amorphous/crystalline phase.Coatings deposited at a lower plasma power and highest gas flow rate exhibited better density,hardness,and wear resistance.All coatings demonstrated equally good resistance against the corrosive environment(3.5wt%NaCl solution).Mechanical,wear,and tribological studies indicated that a single process parameter optimization cannot provide good coating performance;instead,all process parameters have a unique role in defining better properties for the coating by con-trolling the in-flight particle temperature and velocity profile,followed by the cooling pattern of molten droplet before impingement on the substrate.展开更多
文摘This study explores the fabrication of Fe-based amorphous/crystalline coating by air plasma spraying and its dependency on the coating parameters(plasma power,primary gas flow rate,powder feed rate,and stand-off distance).X-ray diffraction of the coatings deposited at optimized spray parameters showed the presence of amorphous/crystalline phase.Coatings deposited at a lower plasma power and highest gas flow rate exhibited better density,hardness,and wear resistance.All coatings demonstrated equally good resistance against the corrosive environment(3.5wt%NaCl solution).Mechanical,wear,and tribological studies indicated that a single process parameter optimization cannot provide good coating performance;instead,all process parameters have a unique role in defining better properties for the coating by con-trolling the in-flight particle temperature and velocity profile,followed by the cooling pattern of molten droplet before impingement on the substrate.