Corrosion of Mg–Y alloy was studied using electrochemical evaluations, immersion tests and SEM observations. Corrosion mechanisms of Mg-（0.25 and 2.5） Y alloy and Mg-（5, 8, and 15） Y alloy were uniform corrosion ...Corrosion of Mg–Y alloy was studied using electrochemical evaluations, immersion tests and SEM observations. Corrosion mechanisms of Mg-（0.25 and 2.5） Y alloy and Mg-（5, 8, and 15） Y alloy were uniform corrosion and pitting corrosion respectively, and the content of Mg_（24）Y_5 phases determined its effect acting as cathode to accelerate the corrosion or corrosion barrier to inhibit the corrosion. Corrosion resistance of Mg-（0.25, 2.5, 5, 8, and 15） Y alloys was as follows： Rt（Mg-0.25Y） 〈 Rt（Mg-8Y） 〈 Rt（Mg-15Y） 〈 Rt（Mg-5Y） 〈 Rt（Mg-2.5Y）. Y could significantly improve the corrosion resistance of the Mg-Y alloy, but the excess of Y deteriorated the corrosion resistance of the Mg-Y alloy. The optimum content of Y in the studied alloys was 2.5%.展开更多
A series of austenitic cast iron samples with different compositions were cast and a part of nickel in the samples was replaced by manganese for economic reason. Erosion–corrosion tests were conducted under 2wt% sulf...A series of austenitic cast iron samples with different compositions were cast and a part of nickel in the samples was replaced by manganese for economic reason. Erosion–corrosion tests were conducted under 2wt% sulfuric acid and 15wt% quartz sand. The results show that the matrix of cast irons remains austenite after a portion of nickel is replaced with manganese.（Fe,Cr）3C is a common phase in the cast irons, and nickel is the main alloying element in high-nickel cast iron; whereas,（Fe,Mn）3C is observed with the increased manganese content in low-nickel cast iron. Under erosion–corrosion tests, the weight-loss rates of the cast irons increase with increasing time. Wear plays a more important role than corrosion in determining the weight loss. It is indicated that the processes of weight loss for the cast irons with high and low nickel contents are different. The erosion resistance of the cast iron containing 7.29wt% nickel and 6.94wt% manganese is equivalent to that of the cast iron containing 13.29wt% nickel.展开更多
基金Funded by the National Key Technology R&D Program of China(Nos.2011BAE22B01 and 2011BAE22B06)
文摘Corrosion of Mg–Y alloy was studied using electrochemical evaluations, immersion tests and SEM observations. Corrosion mechanisms of Mg-（0.25 and 2.5） Y alloy and Mg-（5, 8, and 15） Y alloy were uniform corrosion and pitting corrosion respectively, and the content of Mg_（24）Y_5 phases determined its effect acting as cathode to accelerate the corrosion or corrosion barrier to inhibit the corrosion. Corrosion resistance of Mg-（0.25, 2.5, 5, 8, and 15） Y alloys was as follows： Rt（Mg-0.25Y） 〈 Rt（Mg-8Y） 〈 Rt（Mg-15Y） 〈 Rt（Mg-5Y） 〈 Rt（Mg-2.5Y）. Y could significantly improve the corrosion resistance of the Mg-Y alloy, but the excess of Y deteriorated the corrosion resistance of the Mg-Y alloy. The optimum content of Y in the studied alloys was 2.5%.
基金financially supported by the National Nature Science Foundation of China (No. 51101109)
文摘A series of austenitic cast iron samples with different compositions were cast and a part of nickel in the samples was replaced by manganese for economic reason. Erosion–corrosion tests were conducted under 2wt% sulfuric acid and 15wt% quartz sand. The results show that the matrix of cast irons remains austenite after a portion of nickel is replaced with manganese.（Fe,Cr）3C is a common phase in the cast irons, and nickel is the main alloying element in high-nickel cast iron; whereas,（Fe,Mn）3C is observed with the increased manganese content in low-nickel cast iron. Under erosion–corrosion tests, the weight-loss rates of the cast irons increase with increasing time. Wear plays a more important role than corrosion in determining the weight loss. It is indicated that the processes of weight loss for the cast irons with high and low nickel contents are different. The erosion resistance of the cast iron containing 7.29wt% nickel and 6.94wt% manganese is equivalent to that of the cast iron containing 13.29wt% nickel.