Inhibition of aluminium corrosion in NaOH solution by anionic surfactant as sodium (lauryl)sulphate, cationic surfactant as cetyl trimethyl ammonium bromide and non ionic surfactant asTriton-X 100 has been studied usi...Inhibition of aluminium corrosion in NaOH solution by anionic surfactant as sodium (lauryl)sulphate, cationic surfactant as cetyl trimethyl ammonium bromide and non ionic surfactant asTriton-X 100 has been studied using weight-loss and hydrogen evolution methods. It is foundthat the inhibition efficiency depends on the type of SAS as well as its concentration. The orderof increasing inhibition is as followsSLS < Triton - X 100 < CTABThermodynamic parameters are calculated.展开更多
This study emphasizes on the evaluation and comparison of the anticorrosive properties of sol-gel coatings with and without inhibitor loaded nanocontainers.In this case,naturally available clay nanotubes(halloysite)we...This study emphasizes on the evaluation and comparison of the anticorrosive properties of sol-gel coatings with and without inhibitor loaded nanocontainers.In this case,naturally available clay nanotubes(halloysite)were loaded with cationic corrosion inhibitors Ce 3+/Zr 4+.These nanocontainers were dispersed in hybrid organic-inorganic sol-gel matrix sol.Coating was applied on magnesium alloy AZ91D using the sols containing modified and unmodified nanocontainers employing the dip coating method and cured at 130℃for 1 h in air.Corrosion resistance of coated/uncoated substrates were analyzed using electrochemical impedance spectroscopy,potentiodynamic polarization and weight loss measurements after exposure to 3.5 wt%NaCl solution for varying time durations between 24 h to 120 h.Self-healing ability of coatings was evaluated by micro-Raman spectroscopy after 120 h exposure to 3.5 wt%NaCl solution.Coatings generated after dispersion of corrosion inhibitor loaded clay in hybrid sol-gel matrix have shown more promising corrosion resistance when compared to just the sol-gel matrix coatings,after prolonged exposure to corrosive environment.展开更多
在甲醇钠催化下,丁二酸二甲酯与N,N-二甲基乙醇胺进行酯交换反应合成二(二甲基胺基乙基)丁二酸酯,产率91.2%(以丁二酸二甲酯计);再与正溴代十二烷或正溴代十六烷反应合成了两种新型含丁二酸酯基的Gem in i阳离子表面活性剂n-CnH2n+1(CH3...在甲醇钠催化下,丁二酸二甲酯与N,N-二甲基乙醇胺进行酯交换反应合成二(二甲基胺基乙基)丁二酸酯,产率91.2%(以丁二酸二甲酯计);再与正溴代十二烷或正溴代十六烷反应合成了两种新型含丁二酸酯基的Gem in i阳离子表面活性剂n-CnH2n+1(CH3)2N+CH2CH2OCOCH2CH2COOCH2-CH2N+(CH3)2CnH2n+1-n.2B r(n=12或16)[以二(二甲基胺基乙基)丁二酸酯计,产率85%].研究了其在1 M HC l介质中对碳钢的缓蚀效果,结果表明,在1×10-3mol.L-1时,对碳钢的缓蚀效率分别为97.27%和98.10%.展开更多
文摘Inhibition of aluminium corrosion in NaOH solution by anionic surfactant as sodium (lauryl)sulphate, cationic surfactant as cetyl trimethyl ammonium bromide and non ionic surfactant asTriton-X 100 has been studied using weight-loss and hydrogen evolution methods. It is foundthat the inhibition efficiency depends on the type of SAS as well as its concentration. The orderof increasing inhibition is as followsSLS < Triton - X 100 < CTABThermodynamic parameters are calculated.
基金financial sup-port from SERB,DST for the funding provided through grant number SB/S3/ME/007/2014.
文摘This study emphasizes on the evaluation and comparison of the anticorrosive properties of sol-gel coatings with and without inhibitor loaded nanocontainers.In this case,naturally available clay nanotubes(halloysite)were loaded with cationic corrosion inhibitors Ce 3+/Zr 4+.These nanocontainers were dispersed in hybrid organic-inorganic sol-gel matrix sol.Coating was applied on magnesium alloy AZ91D using the sols containing modified and unmodified nanocontainers employing the dip coating method and cured at 130℃for 1 h in air.Corrosion resistance of coated/uncoated substrates were analyzed using electrochemical impedance spectroscopy,potentiodynamic polarization and weight loss measurements after exposure to 3.5 wt%NaCl solution for varying time durations between 24 h to 120 h.Self-healing ability of coatings was evaluated by micro-Raman spectroscopy after 120 h exposure to 3.5 wt%NaCl solution.Coatings generated after dispersion of corrosion inhibitor loaded clay in hybrid sol-gel matrix have shown more promising corrosion resistance when compared to just the sol-gel matrix coatings,after prolonged exposure to corrosive environment.
文摘在甲醇钠催化下,丁二酸二甲酯与N,N-二甲基乙醇胺进行酯交换反应合成二(二甲基胺基乙基)丁二酸酯,产率91.2%(以丁二酸二甲酯计);再与正溴代十二烷或正溴代十六烷反应合成了两种新型含丁二酸酯基的Gem in i阳离子表面活性剂n-CnH2n+1(CH3)2N+CH2CH2OCOCH2CH2COOCH2-CH2N+(CH3)2CnH2n+1-n.2B r(n=12或16)[以二(二甲基胺基乙基)丁二酸酯计,产率85%].研究了其在1 M HC l介质中对碳钢的缓蚀效果,结果表明,在1×10-3mol.L-1时,对碳钢的缓蚀效率分别为97.27%和98.10%.