The paper aims at investigating whether corundum bricks can be used for the bottom, of the direct reduction furnace of high phosphorus oolitic hematite. The reducing materials including high phosphorus oolitic hemati...The paper aims at investigating whether corundum bricks can be used for the bottom, of the direct reduction furnace of high phosphorus oolitic hematite. The reducing materials including high phosphorus oolitic hematite, bitumite, Ca（OH） 2 and Na2CO3 at a mass ratio of 1：0. 15：0. 15：0. 03 were mixed and pressed into carbon containing cylindrical specimens with the size of Ф15 mm × 20 mm. The specimens were placed on the corundum bricks and reduced in a high temperature tube furnace at 1 200 ℃ for 40, 60, 80, 140 and 220 min, respective- ly. The corrosion and penetration resistance of corundum. bricks to high phosphorus oolitic hematite reducing materials were analyzed with XRD, SEM and EDS. It shows that the reducing slag formed in the reduction process corrodes the surface of corundum bricks to form a product layer of anorthite and hercynite, retarding the further corrosion of the reducing slag; the reducing slag which has penetrated into the interior of the brick goes through the gaps between the particles and generates anorthite and hercynite, filling the gaps and hindering the reducing slag penetration.展开更多
The paper presents a new method to synthesize β-Sialon bonded corundum brick (β-SBCB) from Al-Si alloy directly and easily under 1430℃ , the volume expansion of reaction between Al powder and Nitrogen can help to e...The paper presents a new method to synthesize β-Sialon bonded corundum brick (β-SBCB) from Al-Si alloy directly and easily under 1430℃ , the volume expansion of reaction between Al powder and Nitrogen can help to establish the fast diffusion channel in Al-Si alloy; the suitable crystal seed of Si3N4 is helpful to the fast synthesis of β-Sialon.展开更多
为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和...为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和α-氧化铝微粉加入量分别为3%和8%时,试验砖的性能最佳。该砖在太钢90 t LF钢包熔池及包底部位使用,其寿命达到105炉。展开更多
文摘The paper aims at investigating whether corundum bricks can be used for the bottom, of the direct reduction furnace of high phosphorus oolitic hematite. The reducing materials including high phosphorus oolitic hematite, bitumite, Ca（OH） 2 and Na2CO3 at a mass ratio of 1：0. 15：0. 15：0. 03 were mixed and pressed into carbon containing cylindrical specimens with the size of Ф15 mm × 20 mm. The specimens were placed on the corundum bricks and reduced in a high temperature tube furnace at 1 200 ℃ for 40, 60, 80, 140 and 220 min, respective- ly. The corrosion and penetration resistance of corundum. bricks to high phosphorus oolitic hematite reducing materials were analyzed with XRD, SEM and EDS. It shows that the reducing slag formed in the reduction process corrodes the surface of corundum bricks to form a product layer of anorthite and hercynite, retarding the further corrosion of the reducing slag; the reducing slag which has penetrated into the interior of the brick goes through the gaps between the particles and generates anorthite and hercynite, filling the gaps and hindering the reducing slag penetration.
文摘The paper presents a new method to synthesize β-Sialon bonded corundum brick (β-SBCB) from Al-Si alloy directly and easily under 1430℃ , the volume expansion of reaction between Al powder and Nitrogen can help to establish the fast diffusion channel in Al-Si alloy; the suitable crystal seed of Si3N4 is helpful to the fast synthesis of β-Sialon.
文摘为了满足生产低碳钢和超低碳钢的技术要求,以棕刚玉、板状刚玉、电熔镁铝尖晶石粉为原料,电熔镁砂粉和α-氧化铝微粉为添加剂,络合镁铝溶胶为结合剂,研制出了机压成型免烧刚玉-尖晶石无碳砖,并进行了实验。试验结果表明:当电熔镁砂粉和α-氧化铝微粉加入量分别为3%和8%时,试验砖的性能最佳。该砖在太钢90 t LF钢包熔池及包底部位使用,其寿命达到105炉。