The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht cr...The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht crushing strength, hot modulus of rupture and thermal shock resistance were compared and studied. The results show that： 1） the six tabular corundum materials have similar main chemical composition but their physical properties vary for the different technical procedures which result in different properties of castables ; 2 ） the optimal properties of corundum - spinel castables corre- spotut to different tabular corundum types, so the corundum type shall be selected according to the application of the castables.展开更多
Corundum -spinel castables containing lightweight aggregates have drawn many attentions due to their po- tential for energy-saving, especially when applied in the high-temperature region, such as the work lining of re...Corundum -spinel castables containing lightweight aggregates have drawn many attentions due to their po- tential for energy-saving, especially when applied in the high-temperature region, such as the work lining of refi- ning ladle. One main aspect that restricts their applica- tion is the slag corrosion performance. In this study, one dense tabular corundum and three kinds of lightweight corundum were chosen as aggregates to prepare four dif- ferent corundum - spinel castables. The slag resistance was compared through the induction furnace corrosion test. SEM - EDS, XRD, and thermodynamic and kinet- ics analysis were adopted for the discussion of the corro- sion mechanism. Results show that the crystal grain size and shape of aggregates are important for the slag corro- sion resistance of lightweight corundum -spinel castables under dynamic condition （enforced convection） , yet the effects of pore characteristics are not dominated. Aggre- gates with large flake-like crystal grains show a thicker dissolution diffusion boundary layer and a lower dissolution rate, resulting in a favorable corrosion resist- ance of the castable. The poor microstructure of the ag- gregates, namely, larger pores and small and spherical grains, would cause deterioration of castables＇ slag resistance.展开更多
Corundum spinel castable was prepared using tabular corundum as aggregates,white fused corundum powder,spinel powder and alumina powder as the matrix,pure calcium aluminate cement as a binder,and extra adding calcium ...Corundum spinel castable was prepared using tabular corundum as aggregates,white fused corundum powder,spinel powder and alumina powder as the matrix,pure calcium aluminate cement as a binder,and extra adding calcium chloride(0,1%,2%,and 3%,by mass).The effects of the CaCl2 addition on the cold physical properties,the hot strength,the thermal shock resistance and the microstructure of the castable were studied.The results show that,for the corundum spinel castable fired at 1550℃,with the increase of the CaCl2 addition from 0 to 3%,the cold strengthes first increase,then decrease,the apparent porosity increases,the volume density decreases,and the linear change rate first decreases and then increases,while the overall change is not significant;however,the hot modulus of rupture and the thermal shock resistance are obviously improved.This is mainly due to that,CaCl2 is evenly distributed in the castable in the form of solution,and reacts with Al2O3 to form small flake CA6 crystals,which evenly distributed in the sample matrix strengthening and toughening the material.展开更多
文摘The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht crushing strength, hot modulus of rupture and thermal shock resistance were compared and studied. The results show that： 1） the six tabular corundum materials have similar main chemical composition but their physical properties vary for the different technical procedures which result in different properties of castables ; 2 ） the optimal properties of corundum - spinel castables corre- spotut to different tabular corundum types, so the corundum type shall be selected according to the application of the castables.
基金The National Natural Science Foundation of China(Grant No.51204126 and No.51474165)
文摘Corundum -spinel castables containing lightweight aggregates have drawn many attentions due to their po- tential for energy-saving, especially when applied in the high-temperature region, such as the work lining of refi- ning ladle. One main aspect that restricts their applica- tion is the slag corrosion performance. In this study, one dense tabular corundum and three kinds of lightweight corundum were chosen as aggregates to prepare four dif- ferent corundum - spinel castables. The slag resistance was compared through the induction furnace corrosion test. SEM - EDS, XRD, and thermodynamic and kinet- ics analysis were adopted for the discussion of the corro- sion mechanism. Results show that the crystal grain size and shape of aggregates are important for the slag corro- sion resistance of lightweight corundum -spinel castables under dynamic condition （enforced convection） , yet the effects of pore characteristics are not dominated. Aggre- gates with large flake-like crystal grains show a thicker dissolution diffusion boundary layer and a lower dissolution rate, resulting in a favorable corrosion resist- ance of the castable. The poor microstructure of the ag- gregates, namely, larger pores and small and spherical grains, would cause deterioration of castables＇ slag resistance.
文摘Corundum spinel castable was prepared using tabular corundum as aggregates,white fused corundum powder,spinel powder and alumina powder as the matrix,pure calcium aluminate cement as a binder,and extra adding calcium chloride(0,1%,2%,and 3%,by mass).The effects of the CaCl2 addition on the cold physical properties,the hot strength,the thermal shock resistance and the microstructure of the castable were studied.The results show that,for the corundum spinel castable fired at 1550℃,with the increase of the CaCl2 addition from 0 to 3%,the cold strengthes first increase,then decrease,the apparent porosity increases,the volume density decreases,and the linear change rate first decreases and then increases,while the overall change is not significant;however,the hot modulus of rupture and the thermal shock resistance are obviously improved.This is mainly due to that,CaCl2 is evenly distributed in the castable in the form of solution,and reacts with Al2O3 to form small flake CA6 crystals,which evenly distributed in the sample matrix strengthening and toughening the material.