The hot cracking tendency of 7075 semi-solid alloy under different conditions was studied by critical diameter method.The experiment and simulation results show that the dendrite arms of the rod grow from the edge to ...The hot cracking tendency of 7075 semi-solid alloy under different conditions was studied by critical diameter method.The experiment and simulation results show that the dendrite arms of the rod grow from the edge to the center.The smaller the diameter of the rod is,the more obvious the directional growth of dendrite is,and the greater the tendency of hot cracking is.Compared with ordinary melt,for semi-solid slurry,increasing mould temperature or decreasing pouring temperature can significantly decrease hot cracking tendency of 7075 alloy,decreasing hot cracking grade from 256 to 100 mm^2.Furthermore,based on the RDG criterion,the effects of solidification conditions on the hot cracking tendency were discussed combined with simulation.At the same time,the application and development of RDG criterion were also researched.展开更多
A modified testing system characterized by full automation, steady operation and high accuracy of strain and stress measurements was developed to determine the cracking tendency of high strength concrete （HSC） in re...A modified testing system characterized by full automation, steady operation and high accuracy of strain and stress measurements was developed to determine the cracking tendency of high strength concrete （HSC） in restrained condition at early ages. The shrinkage stress and the tensile creep behavior of HSC at early ages were investigated. The influence of W/C ratio and curing conditions on the early-age shrinkage stress and tensile creep was evaluated. It was found that the lower W/C ratio and drying curing condition resulted in higher shrinkage stress, stress induced tensile creep and greater cracking tendency.展开更多
Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagati...Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagation were predicted by the relationship between temperature,shrinkage force and solidification time during the casting solidification process.The reliability and practicability of the multichannel"cross"hot tearing device were verified by casting experiments and numerical simulations.The theoretical calculation based on Clyne-Davies model and numerical simulation results show that the hot tearing tendency decreases in the order:2024 Al alloy>Al-Cu alloy>Al-Si alloy at a pouring temperature of 670°C and a mold temperature of 25°C.Feeding of liquid films at the end of solidification plays an important role in the propagation process of hot tearing.The decrease of hot tearing tendency is attributed to the feeding of liquid film and intergranular bridging.展开更多
Poor casting properties restrict the application of high strength casting Al-5.0%Cu alloy. The addition of element can improve the casting properties of this alloy. Effect of Si on the casting properties of Al-5.0%Cu ...Poor casting properties restrict the application of high strength casting Al-5.0%Cu alloy. The addition of element can improve the casting properties of this alloy. Effect of Si on the casting properties of Al-5.0%Cu alloy was studied. It has been found that the addition of Si can improve the casting properties of Al-5.0%Cu alloy obviously. With the increase of Si content, the hot cracking tendency of the alloy decreases significantly, and the fluidity of the alloy increases firstly and then decreases slowly. When the content of Si element is higher than 2wt.%, the fluidity of the alloy increases greatly with the increasing of Si content.展开更多
基金Project(17YF1407100)supported by the Shanghai Sailing Program of ChinaProject(17PJ1408600)supported by Shanghai Pujiang Program of China
文摘The hot cracking tendency of 7075 semi-solid alloy under different conditions was studied by critical diameter method.The experiment and simulation results show that the dendrite arms of the rod grow from the edge to the center.The smaller the diameter of the rod is,the more obvious the directional growth of dendrite is,and the greater the tendency of hot cracking is.Compared with ordinary melt,for semi-solid slurry,increasing mould temperature or decreasing pouring temperature can significantly decrease hot cracking tendency of 7075 alloy,decreasing hot cracking grade from 256 to 100 mm^2.Furthermore,based on the RDG criterion,the effects of solidification conditions on the hot cracking tendency were discussed combined with simulation.At the same time,the application and development of RDG criterion were also researched.
基金the National Natural Science Foundation of China(No.50408016)
文摘A modified testing system characterized by full automation, steady operation and high accuracy of strain and stress measurements was developed to determine the cracking tendency of high strength concrete （HSC） in restrained condition at early ages. The shrinkage stress and the tensile creep behavior of HSC at early ages were investigated. The influence of W/C ratio and curing conditions on the early-age shrinkage stress and tensile creep was evaluated. It was found that the lower W/C ratio and drying curing condition resulted in higher shrinkage stress, stress induced tensile creep and greater cracking tendency.
基金This work was financially supported by the National Natural Science Foundation of China(Grant No.51875365).
文摘Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagation were predicted by the relationship between temperature,shrinkage force and solidification time during the casting solidification process.The reliability and practicability of the multichannel"cross"hot tearing device were verified by casting experiments and numerical simulations.The theoretical calculation based on Clyne-Davies model and numerical simulation results show that the hot tearing tendency decreases in the order:2024 Al alloy>Al-Cu alloy>Al-Si alloy at a pouring temperature of 670°C and a mold temperature of 25°C.Feeding of liquid films at the end of solidification plays an important role in the propagation process of hot tearing.The decrease of hot tearing tendency is attributed to the feeding of liquid film and intergranular bridging.
基金This work was financiallysupported by the Fund of BeijingJiaotong University(No.2004SZ006).
文摘Poor casting properties restrict the application of high strength casting Al-5.0%Cu alloy. The addition of element can improve the casting properties of this alloy. Effect of Si on the casting properties of Al-5.0%Cu alloy was studied. It has been found that the addition of Si can improve the casting properties of Al-5.0%Cu alloy obviously. With the increase of Si content, the hot cracking tendency of the alloy decreases significantly, and the fluidity of the alloy increases firstly and then decreases slowly. When the content of Si element is higher than 2wt.%, the fluidity of the alloy increases greatly with the increasing of Si content.