Non-stoichiometric Nd_((1+x))(Mg_(1/2)Sn_(1/2))O_(3)(-0.04=x≤0.04,NMS)ceramics were fabricated via a conventional solid-state reaction method.Crystal structures and morphologies were investigated by Xray diffraction(...Non-stoichiometric Nd_((1+x))(Mg_(1/2)Sn_(1/2))O_(3)(-0.04=x≤0.04,NMS)ceramics were fabricated via a conventional solid-state reaction method.Crystal structures and morphologies were investigated by Xray diffraction(XRD)and scanning electron microscopy(SEM),respectively.The main crystalline phase is monoclinic Nd(Mg_(1/2)Sn_(1/2))O_(3) with a double perovskite structure(P21/n space group)for the NMS system proved by XRD.The sample at x=0.01 has the best crystallinity and evenly distributed crystal grains observed by SEM.The optimum performances(ε_(r)=19.87,Q×f=41840 GHz,f=12.05 GHz)are obtained at x=0.01.Lattice vibrational modes of the Raman spectra were assigned and illustrated,in detail.The dielectric properties obtained by fitting infrared reflectance spectra with the help of four-parameter semi-quantum model are consistent with the calculated values by microscopic polarization and damping coefficients.The reverse translational vibration of the NdeMgO_(6),the F_(5u)^((5)) mode,provides the greatest contribution to the dielectric response.The relationships between crystal structures and dielectric properties were mainly established using lattice vibrational modes as a media.展开更多
Sr_(2)MgWO_(6)(SMW)is a typical perovskite oxide compound,but there has been little research on the effects of processing on its dielectric properties.In this work,SMW ceramics were prepared by solid-state synthesis w...Sr_(2)MgWO_(6)(SMW)is a typical perovskite oxide compound,but there has been little research on the effects of processing on its dielectric properties.In this work,SMW ceramics were prepared by solid-state synthesis with sintering at 1450℃,1475℃,1500℃and 1525℃,respectively.XRD results confirmed that the samples possessed double perovskite structure(Fm-3m).The Raman and FTIR spectra were used to study the lattice vibrational modes.The FPSQ model was used to obtain the fitting curves of the FTIR spectra and derive the intrinsic properties of the material that were found to be in agreement with the measured data.The structure-property relationships were successfully established based on the Raman mode results.The optimal sintering temperature of SMW ceramics was identified as 1475℃due to the excellent performances characteristics(ε_(r)=16.97,Q×f=23,872 GHz,τ_(f)=-35.38 ppm/℃)obtained at this temperature.This study explored the relationships among the crystal structures,lattice vibrational characteristics and dielectric properties of SMW ceramics,so as to further understand their dielectric response mechanism and lay a solid theoretical foundation for the development of microwave ceramics.展开更多
基金supported by National Natural Science Foundation of China(Grant 11874240)Guangxi Information Materials Key Laboratory Open Research Fund(171007-K)+3 种基金State Key Laboratory of New Ceramic and Fine Processing Tsinghua University(No.KF201811)the Opening Project of Key Laboratory of Inorganic Functional Materials and Devices,Chinese Academy of Sciences(Grant No.KLIFMD201803)the Natural Science Foundation of Shandong Province,China(No.ZR2016EMM21)Scientific Research Foundation of Shandong University of Science and Technology for Recruited Talents(No.2016RCJJ002).
文摘Non-stoichiometric Nd_((1+x))(Mg_(1/2)Sn_(1/2))O_(3)(-0.04=x≤0.04,NMS)ceramics were fabricated via a conventional solid-state reaction method.Crystal structures and morphologies were investigated by Xray diffraction(XRD)and scanning electron microscopy(SEM),respectively.The main crystalline phase is monoclinic Nd(Mg_(1/2)Sn_(1/2))O_(3) with a double perovskite structure(P21/n space group)for the NMS system proved by XRD.The sample at x=0.01 has the best crystallinity and evenly distributed crystal grains observed by SEM.The optimum performances(ε_(r)=19.87,Q×f=41840 GHz,f=12.05 GHz)are obtained at x=0.01.Lattice vibrational modes of the Raman spectra were assigned and illustrated,in detail.The dielectric properties obtained by fitting infrared reflectance spectra with the help of four-parameter semi-quantum model are consistent with the calculated values by microscopic polarization and damping coefficients.The reverse translational vibration of the NdeMgO_(6),the F_(5u)^((5)) mode,provides the greatest contribution to the dielectric response.The relationships between crystal structures and dielectric properties were mainly established using lattice vibrational modes as a media.
基金supported by National Natural Science Foundation of China(Grant 11874240)Shandong Provincial Key Research and Development Program,China(No.2019GGX101060).
文摘Sr_(2)MgWO_(6)(SMW)is a typical perovskite oxide compound,but there has been little research on the effects of processing on its dielectric properties.In this work,SMW ceramics were prepared by solid-state synthesis with sintering at 1450℃,1475℃,1500℃and 1525℃,respectively.XRD results confirmed that the samples possessed double perovskite structure(Fm-3m).The Raman and FTIR spectra were used to study the lattice vibrational modes.The FPSQ model was used to obtain the fitting curves of the FTIR spectra and derive the intrinsic properties of the material that were found to be in agreement with the measured data.The structure-property relationships were successfully established based on the Raman mode results.The optimal sintering temperature of SMW ceramics was identified as 1475℃due to the excellent performances characteristics(ε_(r)=16.97,Q×f=23,872 GHz,τ_(f)=-35.38 ppm/℃)obtained at this temperature.This study explored the relationships among the crystal structures,lattice vibrational characteristics and dielectric properties of SMW ceramics,so as to further understand their dielectric response mechanism and lay a solid theoretical foundation for the development of microwave ceramics.