Cubic boron nitride thin films were deposited on silicon substrates by low-pressure inductively coupled plasmaenhanced chemical vapour deposition. It was found that the introduction of 02 into the deposition system su...Cubic boron nitride thin films were deposited on silicon substrates by low-pressure inductively coupled plasmaenhanced chemical vapour deposition. It was found that the introduction of 02 into the deposition system suppresses both nucleation and growth of cubic boron nitride. At a B2H6 concentration of 2.5% during film deposition, the critical O2 concentration allowed for the nucleation of cubic boron nitride was found to be less than 1.4%, while that for the growth of cubic boron nitride was higher than 2.1%. Moreover, the infrared absorption peak observed at around 1230- 1280 cm^-1, frequently detected for cubic boron nitride films prepared using non-ultrahigh vacuum systems, appears to be due to the absorption of boron oxide, a contaminant formed as a result of the oxygen impurity. Therefore, the existence of trace oxygen contamination in boron nitride films can be evaluated qualitatively by this infrared absorption peak.展开更多
This paper investigates the procedure of cubic boron nitride （cBN） thin film delamination by Fourier-transform infrared （IR） spectroscopy. It finds that the apparent IR absorption peak area near 1380cm^-1 and 1073...This paper investigates the procedure of cubic boron nitride （cBN） thin film delamination by Fourier-transform infrared （IR） spectroscopy. It finds that the apparent IR absorption peak area near 1380cm^-1 and 1073 cm^-1 attributed to the B-N stretching vibration of sp2-bonded BN and the transverse optical phonon of cBN, respectively, increased up to 195% and 175% of the original peak area after film delamination induced compressive stress relaxation. The increase of IR absorption of sp2-bonded BN is found to be non-linear and hysteretic to film delamination, which suggests that the relaxation of the turbostratic BN （tBN） layer from the compressed condition is also hysteretic to film delamination. Moreover, cross-sectional transmission electron microscopic observations revealed that cBN film delamination is possible from near the aBN（amorphous BN）/tBN interface at least for films prepared by plasma-enhanced chemical vapour deposition.展开更多
基金Project supported by the National Natural Science Foundation of China (Grant No. 50772096)the Educational Department of Zhejiang Province, China (Grant No. 20061365)
文摘Cubic boron nitride thin films were deposited on silicon substrates by low-pressure inductively coupled plasmaenhanced chemical vapour deposition. It was found that the introduction of 02 into the deposition system suppresses both nucleation and growth of cubic boron nitride. At a B2H6 concentration of 2.5% during film deposition, the critical O2 concentration allowed for the nucleation of cubic boron nitride was found to be less than 1.4%, while that for the growth of cubic boron nitride was higher than 2.1%. Moreover, the infrared absorption peak observed at around 1230- 1280 cm^-1, frequently detected for cubic boron nitride films prepared using non-ultrahigh vacuum systems, appears to be due to the absorption of boron oxide, a contaminant formed as a result of the oxygen impurity. Therefore, the existence of trace oxygen contamination in boron nitride films can be evaluated qualitatively by this infrared absorption peak.
基金supported by the National Science Foundation of Zhejiang Province,China (Grant No Y405051)the Zhejiang Provincial Education Department,China (Grant No 20061365)the Education Ministry Scientific Research Startup Foundation for Returnee,China (Grant No 2007-24)
文摘This paper investigates the procedure of cubic boron nitride （cBN） thin film delamination by Fourier-transform infrared （IR） spectroscopy. It finds that the apparent IR absorption peak area near 1380cm^-1 and 1073 cm^-1 attributed to the B-N stretching vibration of sp2-bonded BN and the transverse optical phonon of cBN, respectively, increased up to 195% and 175% of the original peak area after film delamination induced compressive stress relaxation. The increase of IR absorption of sp2-bonded BN is found to be non-linear and hysteretic to film delamination, which suggests that the relaxation of the turbostratic BN （tBN） layer from the compressed condition is also hysteretic to film delamination. Moreover, cross-sectional transmission electron microscopic observations revealed that cBN film delamination is possible from near the aBN（amorphous BN）/tBN interface at least for films prepared by plasma-enhanced chemical vapour deposition.