Spent catalyst used for denitration by selective catalytic reduction(spent SCR denitration catalysts) is one of the important urban mines due to the high content of TiO_(2)(~85 wt%) and the massive accumulation amount...Spent catalyst used for denitration by selective catalytic reduction(spent SCR denitration catalysts) is one of the important urban mines due to the high content of TiO_(2)(~85 wt%) and the massive accumulation amount(over 100,000 tons),therefore,value-added reutilization of titanium in spent SCR catalysts is considerably meaningful.In this paper,a novel method is proposed for converting the titanium oxide in spent SCR denitration catalysts to metallic titanium.Specifically,titanium dioxide(TiO_(2)) was firstly obtained from spent SCR denitration catalysts after removing the impurities by hydrometallurgy process.Then,TiO_(2) is converted to Ti_(2)CO by carbothermic reduction method,and Ti_(2)CO was further purified by oleic acid capture.Finally,by utilizing the as-prepared Ti_(2)CO as the consumable anode in the NaCl-KCl molten salt,high-purity metallic titanium was deposited at cathode,all confirming the feasibility for the conversion of low-grade TiO_(2) in the spent catalysts,from 60 wt% to high-purity metallic Ti(99.5 wt%), furthermore,the energy consumption of this process is 3950 kWh tonne-1 Ti,which is lower than that of most traditional titanium metallurgy methods.The method herein can provide new insights for the value-added recycling of titanium resources in urban mines.展开更多
Selective catalytic reduction technology using NH3 as a reducing agent(NH3-SCR) is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb mo...Selective catalytic reduction technology using NH3 as a reducing agent(NH3-SCR) is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer(XRD), Brunauer-Emmett-Teller(BET), Transmission electron microscopy(TEM), Fourier transform infrared spectroscopy(FT-IR), UV-Vis diffuse reflectance spectroscopy(UV-Vis DRS), Raman and Hydrogen temperature-programmed reduction(H2-TPR). The catalytic activities of V5 CexS by/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5 CexS by/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400℃, the V5 CexS by/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210℃, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased.展开更多
The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reducti...The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reduction of NOx by NH3.Four different methods,namely pre-impregnation,post-impregnation,coimpregnation,and co-precipitation,were used to synthesize a series of V2 O5-WO3-TiO2-CeO2-ZrO2 catalysts.The catalysts were characterized by XRD,BET,NH3-TPD,XPS,and H2-TPR techniques.Moreover,the activity and anti-K poisoning performance were tested by an NH3-SCR model reaction.The results show that the introduction of Ce^4+and Zr^4+can improve the catalytic performance of V2O5-WO3/TiO2 catalyst,but the impregnation method cannot enhance the anti-K poisoning performance.Ce^4+and Zr^4+introduced by co-precipitation method can effectively improve the tolerance of K,which is mainly due to the incorporation of Ce^4+and Zr^4+into TiO2 lattice to form a uniform TiO2-CeO2-ZrO2 solid solution,resulting in the optimal surface acidity and redox performance,and reducing the decreases caused by Kpoisoning.Furthermore,based on the best introduction method,we further optimized the molar ratio of Ce^4+/Zr^4+,It is found that the catalyst exhibits the best anti-K poisoning performance when the molar ratio of Ce^4+/Zr^4+is 2:1.展开更多
基金the National Natural Science Foundation of China(Grant No.51804277)supported by the State Key Laboratory of Special Rare Metal Materials(No.SKL2020K004)+1 种基金Northwest Rare Metal Materials Research Institutesupported by the State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization(No.CNMRCUKF2008)。
文摘Spent catalyst used for denitration by selective catalytic reduction(spent SCR denitration catalysts) is one of the important urban mines due to the high content of TiO_(2)(~85 wt%) and the massive accumulation amount(over 100,000 tons),therefore,value-added reutilization of titanium in spent SCR catalysts is considerably meaningful.In this paper,a novel method is proposed for converting the titanium oxide in spent SCR denitration catalysts to metallic titanium.Specifically,titanium dioxide(TiO_(2)) was firstly obtained from spent SCR denitration catalysts after removing the impurities by hydrometallurgy process.Then,TiO_(2) is converted to Ti_(2)CO by carbothermic reduction method,and Ti_(2)CO was further purified by oleic acid capture.Finally,by utilizing the as-prepared Ti_(2)CO as the consumable anode in the NaCl-KCl molten salt,high-purity metallic titanium was deposited at cathode,all confirming the feasibility for the conversion of low-grade TiO_(2) in the spent catalysts,from 60 wt% to high-purity metallic Ti(99.5 wt%), furthermore,the energy consumption of this process is 3950 kWh tonne-1 Ti,which is lower than that of most traditional titanium metallurgy methods.The method herein can provide new insights for the value-added recycling of titanium resources in urban mines.
基金supported by the Natural Science Foundation of China (Nos. 21376261, 21173270)the Beijing Natural Science Foundation (2142027)+1 种基金Doctor select Foundation (No. 20130007110007)the National Hi-Tech Research and Development Program (863) of China (No. 2013AA065302)
文摘Selective catalytic reduction technology using NH3 as a reducing agent(NH3-SCR) is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer(XRD), Brunauer-Emmett-Teller(BET), Transmission electron microscopy(TEM), Fourier transform infrared spectroscopy(FT-IR), UV-Vis diffuse reflectance spectroscopy(UV-Vis DRS), Raman and Hydrogen temperature-programmed reduction(H2-TPR). The catalytic activities of V5 CexS by/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5 CexS by/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400℃, the V5 CexS by/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210℃, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased.
基金Project supported by the National Natural Science Foundation of China(21876168)the Key Projects for Common Key Technology Innovation in Key Industries in Chongqing(cstc2016zdcy-ztzx0020-01)+1 种基金Youth Innovation Promotion Association CAS(2019376)the Graduate Innovation Project of Chongqing Technology and Business University(yjscxx201803-028-22)。
文摘The purpose of this work is to explore the effects of the introduction methods of Ce^4+and Zr^4+on the physicochemical properties,activity,and K tolerance of V2 O5-WO3/TiO2 catalyst for the selective catalytic reduction of NOx by NH3.Four different methods,namely pre-impregnation,post-impregnation,coimpregnation,and co-precipitation,were used to synthesize a series of V2 O5-WO3-TiO2-CeO2-ZrO2 catalysts.The catalysts were characterized by XRD,BET,NH3-TPD,XPS,and H2-TPR techniques.Moreover,the activity and anti-K poisoning performance were tested by an NH3-SCR model reaction.The results show that the introduction of Ce^4+and Zr^4+can improve the catalytic performance of V2O5-WO3/TiO2 catalyst,but the impregnation method cannot enhance the anti-K poisoning performance.Ce^4+and Zr^4+introduced by co-precipitation method can effectively improve the tolerance of K,which is mainly due to the incorporation of Ce^4+and Zr^4+into TiO2 lattice to form a uniform TiO2-CeO2-ZrO2 solid solution,resulting in the optimal surface acidity and redox performance,and reducing the decreases caused by Kpoisoning.Furthermore,based on the best introduction method,we further optimized the molar ratio of Ce^4+/Zr^4+,It is found that the catalyst exhibits the best anti-K poisoning performance when the molar ratio of Ce^4+/Zr^4+is 2:1.