Leaching behavior and microstructure of phosphorus in converter slag

Converter slag is a by-product of the steelmaking process and contains a large amount of Ca,Fe,P and other elements.If the phosphorus in the converter slag can be effectively extracted,the resulting phosphorus can be used as a phosphate fertilizer.Phosphorus in converter slag is mainly enriched in 2CaO·SiO_(2)-3CaO·P_(2)O_(5)(C_(2)S-C_(3)P)solid solution and is easily dissolved in water.Therefore,acid leaching method was used to dissolve the solid solution to extract phosphorus in converter slag,so as to realize the recycling of phosphorus resources in converter slag.The leaching behavior of three actual converter slags from different steel mills in acid leaching solutions composed of citric acid,sodium hydroxide,hydrochloric acid and deionized water was studied by X-ray diffraction,scanning electron microscopy combined with energy dispersive spectrometry,Fourier transform infrared spectroscopy and Raman spectroscopy to reveal the change in object image structure as well as SiO_(4) and PO_(4) tetrahedron before and after acid leaching.The results show that only a small amount of phosphorus in converter slag with too low basicity is enriched in C_(2)S-C_(3)P solid solution,resulting in poor leaching effect.When the converter slag has a high basicity,the removal effect of phosphorus is 70.64%-81.88%.In addition,when the basicity of converter slag is roughly the same,the dephosphorization effect of slag with high FeO content is relatively poor.And acid leaching will cause depolymerization behavior of SiO_(4) and PO_(4) tetrahedron,so that the mole fraction of Q0(Si)(asymmetric stretching vibration of Si-O bond in SiO_(4) tetrahedron with bridge oxygen number of 0)and NBO/Si(non-bridging oxygen in silicate tetrahedra)will increase.Phosphate-containing solids can be obtained from the solution after acid leaching through static precipitation,and the solids have the potential to make phosphate fertilizers.

Melting Characteristics of Recycling Slag in Decarburization Converter and Its Application Effects

The steel slag in the decarburization converter is treated by the little water-spreading （ LWS ） and the heat-stewed （ HS ） methods , which is used as the furnace burden of the dephosphorization converter.The slag characteristics by the LWS and the HS methods and its application effects as the furnace burden are researched.The results show the moisture content in the HS slag is higher than that of the LWS slag.There is higher total iron content in the HS and the LWS slags and almost same melting point.The dicalcium silicate content in the LWS slag is higher than that in the HS slag.The tricalcium silicate in the LWS slag is lower than that in the HS slag.There are a lot of calcium ferrite in the LWS and the HS slags , which is beneficial to dephosphorization and slag melting.The LWS and the HS slags are added to dephosphorization converter each charge by 3or 6t.The results show that the saving lime is 0.7-1.0tfor each charge.The petrographic constitute of final slag for the dephosphorization converter by adding the LWS and the HS slags is dicalcium silicate , RO phase and glass phase.There are a little calcium ferrite phase in the LWS slag , which is helpful to dephosphorization.So there are better dephosphorization effects for the LWS and HS slags.