The growth of coarse grains of diamond was observed with graphite as carbon source and Fe80Ni20 alloy powder as catalyst at HPHT in a China-type SPD 6×1670T cubic high-pressure apparatus with highly exact control...The growth of coarse grains of diamond was observed with graphite as carbon source and Fe80Ni20 alloy powder as catalyst at HPHT in a China-type SPD 6×1670T cubic high-pressure apparatus with highly exact control system. To synthesize coarse grains of diamond crystal with high quality,ad-vanced indirect heat assembly,powder catalyst technology and catalyst with optimal granularity were used. Especially the nucleation of diamond and the growth rate were strictly controlled by the opti-mized synthesis craft. At last,diamond crystals (about 0.85 mm) in the perfect hex-octahedron shape were successfully synthesized at ～5.4 GPa and ～1360℃ in 60 min. The characteristic of crystal growth with powder catalyst technology under HPHT was discussed. The results and techniques might be useful for production of coarse grains of diamond.展开更多
基金Supported by the National Natural Science Foundation of China (Grant No.50572032)
文摘The growth of coarse grains of diamond was observed with graphite as carbon source and Fe80Ni20 alloy powder as catalyst at HPHT in a China-type SPD 6×1670T cubic high-pressure apparatus with highly exact control system. To synthesize coarse grains of diamond crystal with high quality,ad-vanced indirect heat assembly,powder catalyst technology and catalyst with optimal granularity were used. Especially the nucleation of diamond and the growth rate were strictly controlled by the opti-mized synthesis craft. At last,diamond crystals (about 0.85 mm) in the perfect hex-octahedron shape were successfully synthesized at ～5.4 GPa and ～1360℃ in 60 min. The characteristic of crystal growth with powder catalyst technology under HPHT was discussed. The results and techniques might be useful for production of coarse grains of diamond.