The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrheniu...The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrhenius behavior and modifying the baseline of DSC curves, has been proposed. The results show that JMAK exponent and recrystallization activation energy of the drawn copper wires with a strain of 2.77 are about 2.39 and 125 k J/mol, respectively. The line linking the tangency points of DSC curve hypotenuse can be used as the baseline when calculating recrystallization fraction. The JMAK exponent obtained by the DSC method is in a good agreement with that obtained by microhardness measurements. Compared to traditional methods to measure the exponent, the proposed method is faster and less labor intensive.展开更多
In order to test the thermal decomposition of 1,3,5-trinitro-1,3,5-triazinane(RDX),the linear temperature rise experiment of RDX was carried out by differential scanning calorimeter under different heating rate condit...In order to test the thermal decomposition of 1,3,5-trinitro-1,3,5-triazinane(RDX),the linear temperature rise experiment of RDX was carried out by differential scanning calorimeter under different heating rate conditions.The kinetic calculation of RDX thermal decomposition curve was carried out by Kissinger and Ozawa methods,respectively,and the thermal analysis software was used to calculate the parameters such as self-accelerating decomposition temperature.The results show that the initial decomposition temperature range,decomposition peak temperature range,and decomposition completion temperature range of RDX are 208.4-214.2,225.7-239.3 and 234.0-252.4℃,respectively,and the average decomposition enthalpy is 362.9 J·g^-1.Kissinger method was used to calculate the DSC experimental data of RDX,the apparent activation energy obtained is 190.8 kJ·mol^-1,which is coincident with the results calculated by Ozawa method at the end of the reaction,indicating that the apparent activation energy calculated by the two methods is relatively accurate.When the packaging mass values are 1.0,2.0 and 5.0 kg,respectively,the self-accelerating decomposition temperatures are 97.0,93.0 and 87.0℃,respectively,indicating that with the increase of packaging mass,the self-accelerating decomposition temperature gradually decreases,and the risk increases accordingly.展开更多
The differential scanning calorimetric (DSC)curves of the mitochondria isolated from two varieties of sporophyte cytoplasmic male sterile and their fertile lines of Yie Bai and Ma Xie type rice have been determined. T...The differential scanning calorimetric (DSC)curves of the mitochondria isolated from two varieties of sporophyte cytoplasmic male sterile and their fertile lines of Yie Bai and Ma Xie type rice have been determined. The curves show that the energy is released continuously as temperature rise to 70℃. Some thermodynamic and kinetic parameters of the energy release of the mitochondria have been obtained. The presented results showed that the mitochondria from cytoplasmic male sterile rice released more heat and they had higher energy barrier, less rate, and more complicated mechanism than that of their fertile lines in the energy release process.展开更多
Differential scanning calorimeter combined with flux(dehydrated B2O3) processing was used to realize and precisely measure the undercooling of germanium melts.The highest undercooling obtained in this way was 190 K.Re...Differential scanning calorimeter combined with flux(dehydrated B2O3) processing was used to realize and precisely measure the undercooling of germanium melts.The highest undercooling obtained in this way was 190 K.Relations between the undercooling and cooling rate or overheating tem-perature are analyzed respectively.The undercooling obtained is found to be increased with increasing of the cooling rate in the range from 5 to 40 K/min.At a given cooling rate,the undercooling reached is increased with the increasing of the overheating temperature of the melt,but tends to be constant at last.Crystallization of the undercooled germanium melt is investigated at the same time.It is clearly shown that,the higher the cooling rate,the shorter time is needed for crystallization.展开更多
A new differential equation was derived from the modified first-order kinetic model to describe the polymer crystallization processes. The crystallization experiments were carried out by means of DSC. Poly (ethylene t...A new differential equation was derived from the modified first-order kinetic model to describe the polymer crystallization processes. The crystallization experiments were carried out by means of DSC. Poly (ethylene terephthalate) resins were selected as the samples containing different catalysts. The relationships between the parameters obtained from the known Avrami equation and from one in the present paper were discussed. A method for applying the equation to determine the kinetic parameters from a constant heating and a constant cooling curve was proposed.展开更多
HOT-DIPPING Zn+5% Al + (0.01%-0.2%) RE alloy on steel surface by the gas reductionmethod is a new technology. Owing to its good anti-corrosive and forming properties as wellas good technical periormances, the coating ...HOT-DIPPING Zn+5% Al + (0.01%-0.2%) RE alloy on steel surface by the gas reductionmethod is a new technology. Owing to its good anti-corrosive and forming properties as wellas good technical periormances, the coating attracts wide interest and has been put into indus-trial production rapidly. The authors successfully produced the coating by the electrolytic ac-tivity aid agent method and put it into industrial production. The products have been used inthe electric power and railway engineerings. Results show that the anti-corrosive展开更多
The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calcul...The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.展开更多
基金Projects(51171135,51371132,51471123) supported by the National Natural Science Foundation of ChinaProjects(2012K07-08,2013KJXX-61) supported by Key Science and Technology Program of Shaanxi Province,ChinaProject(2013JC14) supported by the Education Department Foundation of Shaanxi Province,China
文摘The drawn copper wires have been analyzed by differential scanning calorimeter(DSC) and a new method, which uses DSC measurements to determine the Johnson-Mehl-Avrami-Kolmogorov(JMAK) exponent via introducing Arrhenius behavior and modifying the baseline of DSC curves, has been proposed. The results show that JMAK exponent and recrystallization activation energy of the drawn copper wires with a strain of 2.77 are about 2.39 and 125 k J/mol, respectively. The line linking the tangency points of DSC curve hypotenuse can be used as the baseline when calculating recrystallization fraction. The JMAK exponent obtained by the DSC method is in a good agreement with that obtained by microhardness measurements. Compared to traditional methods to measure the exponent, the proposed method is faster and less labor intensive.
文摘In order to test the thermal decomposition of 1,3,5-trinitro-1,3,5-triazinane(RDX),the linear temperature rise experiment of RDX was carried out by differential scanning calorimeter under different heating rate conditions.The kinetic calculation of RDX thermal decomposition curve was carried out by Kissinger and Ozawa methods,respectively,and the thermal analysis software was used to calculate the parameters such as self-accelerating decomposition temperature.The results show that the initial decomposition temperature range,decomposition peak temperature range,and decomposition completion temperature range of RDX are 208.4-214.2,225.7-239.3 and 234.0-252.4℃,respectively,and the average decomposition enthalpy is 362.9 J·g^-1.Kissinger method was used to calculate the DSC experimental data of RDX,the apparent activation energy obtained is 190.8 kJ·mol^-1,which is coincident with the results calculated by Ozawa method at the end of the reaction,indicating that the apparent activation energy calculated by the two methods is relatively accurate.When the packaging mass values are 1.0,2.0 and 5.0 kg,respectively,the self-accelerating decomposition temperatures are 97.0,93.0 and 87.0℃,respectively,indicating that with the increase of packaging mass,the self-accelerating decomposition temperature gradually decreases,and the risk increases accordingly.
文摘The differential scanning calorimetric (DSC)curves of the mitochondria isolated from two varieties of sporophyte cytoplasmic male sterile and their fertile lines of Yie Bai and Ma Xie type rice have been determined. The curves show that the energy is released continuously as temperature rise to 70℃. Some thermodynamic and kinetic parameters of the energy release of the mitochondria have been obtained. The presented results showed that the mitochondria from cytoplasmic male sterile rice released more heat and they had higher energy barrier, less rate, and more complicated mechanism than that of their fertile lines in the energy release process.
基金This work was supported by the National Natural Science Foundation of China(Grant No.50171059)by the Nature Science Foundation of Hebei Province,China(Grant No.503278).
文摘Differential scanning calorimeter combined with flux(dehydrated B2O3) processing was used to realize and precisely measure the undercooling of germanium melts.The highest undercooling obtained in this way was 190 K.Relations between the undercooling and cooling rate or overheating tem-perature are analyzed respectively.The undercooling obtained is found to be increased with increasing of the cooling rate in the range from 5 to 40 K/min.At a given cooling rate,the undercooling reached is increased with the increasing of the overheating temperature of the melt,but tends to be constant at last.Crystallization of the undercooled germanium melt is investigated at the same time.It is clearly shown that,the higher the cooling rate,the shorter time is needed for crystallization.
文摘A new differential equation was derived from the modified first-order kinetic model to describe the polymer crystallization processes. The crystallization experiments were carried out by means of DSC. Poly (ethylene terephthalate) resins were selected as the samples containing different catalysts. The relationships between the parameters obtained from the known Avrami equation and from one in the present paper were discussed. A method for applying the equation to determine the kinetic parameters from a constant heating and a constant cooling curve was proposed.
文摘HOT-DIPPING Zn+5% Al + (0.01%-0.2%) RE alloy on steel surface by the gas reductionmethod is a new technology. Owing to its good anti-corrosive and forming properties as wellas good technical periormances, the coating attracts wide interest and has been put into indus-trial production rapidly. The authors successfully produced the coating by the electrolytic ac-tivity aid agent method and put it into industrial production. The products have been used inthe electric power and railway engineerings. Results show that the anti-corrosive
基金Project(2012CB619500)supported by the National Basic Research Program of China
文摘The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.