Acoustic emission （ AE ） features during the fracture process of notched wrought aluminum alloy 7N01 and weld were investigated under the three-point bending load. Wavelet transform is used to investigate the time-f...Acoustic emission （ AE ） features during the fracture process of notched wrought aluminum alloy 7N01 and weld were investigated under the three-point bending load. Wavelet transform is used to investigate the time-frequency features of AE signals during the test. The experimental results showed that AE energy was effective indicators to detect the crack initiation for 7N01 aluminum. The digital images from monitoring the notch tip region of 7 NO1 aluminum sample verify the prediction of AE signals. The weld emits low energy, weak signal strength, and low peak amplitude, while stronger AE energy, amplitude, and more AE event counts for the base metal. In short, the AE technique was more sensitive to the changes in the fracture mode and could be used to monitor the damage development in welded structures.展开更多
文摘Acoustic emission （ AE ） features during the fracture process of notched wrought aluminum alloy 7N01 and weld were investigated under the three-point bending load. Wavelet transform is used to investigate the time-frequency features of AE signals during the test. The experimental results showed that AE energy was effective indicators to detect the crack initiation for 7N01 aluminum. The digital images from monitoring the notch tip region of 7 NO1 aluminum sample verify the prediction of AE signals. The weld emits low energy, weak signal strength, and low peak amplitude, while stronger AE energy, amplitude, and more AE event counts for the base metal. In short, the AE technique was more sensitive to the changes in the fracture mode and could be used to monitor the damage development in welded structures.