Direct-chill semi-continuous casting process of three-layer composite ingot of 4045/3004/4045 aluminum alloys

Three-layer composite ingot of 4045/3004/4045 aluminum alloys was prepared by direct-chill semi-continuous casting process,the temperature field distribution near the composite interface,macro-morphology,microstructure and composition distribution of the composite interface were investigated.The results show that semi-solid layer with a certain thickness forms near the interface due to the effect of cooling plate,which ensures successful implementation of casting the composite ingot.Two different aluminum alloys are well bonded metallurgically.The mechanical properties of composite interface were measured,the tensile and shearing strengths of composite interface are 105 and 88 MPa,respectively,which proves that the composite interface is a kind of metallurgical bonding.

Research progress on semi-continuous casting of magnesium alloys under external field

High-performance magnesium alloys are moving towards a trend of being produced on a large scale and in an integrated manner.The foundational key to their successful production is the high-quality cast ingots.Magnesium alloys produced through the conventional semi-continuous casting process inevitably contain casting defects,which makes it challenging to manufacture high-quality ingots.The integration of external field assisted controlled solidification technology,which combines physical fields such as electromagnetic and ultrasonic fields with traditional semi-continuous casting processes,enables the production of high-quality magnesium alloy ingots characterized by a homogeneous microstructure and absence of cracks.This article mainly summarizes the technical principles of those external field assisted casting process.The focus is on elaborating the refinement mechanism of different types of electromagnetic fields,ultrasonic fields,and combined physical fields during the solidification of magnesium alloys.Finally,the development prospects of producing highquality magnesium alloy ingots through semi-continuous casting under the external field were discussed.

Characteristics evolution of 6009/7050 bimetal slab prepared by direct-chill casting process

6009/7050 alloy bimetal slab was prepared by a direct-chill (DC) casting process. Homogenizing annealing, hot rolling and T6 treatment were successively performed and their effects on microstructure and properties of the slab were studied. The results reveal that the average diffusion layer thickness of as-cast slab, determined by interdiffusion of elements Zn, Cu, Mg and Si, was about 400 μm. Excellent metallurgical bonding was achieved because all tensile samples fractured on the softer 6009 alloy side after homogenizing annealing. After homogenizing annealing plus rolling, the average diffusion layer thickness decreased to 100 μm, while the network structure of 7050 alloy side transformed to dispersive nubby structure. Furthermore, subsequent T6 treatment resulted in diffusion layer thickness up to 200 μm and an obvious increase of the Vickers hardness for both 7050 and 6009 sides. The layered structure of the as-cast 6009/7050 bimetal is retained after hot rolling and T6 treatment.

Microstructure and mechanical properties of NZ30K alloy by semi-continuous direct chill and sand mould casting processes

The Mg-3.0Nd-0.2Zn-0.4Zr (NZ30K) alloys were prepared by direct-chill casting (DCC) and sand mould casting (SMC) processes,respectively and their microstructures and mechanical properties were investigated.The results indicate that casting method plays a remarkable influence on the microstructure and mechanical properties of as-cast NZ30K alloy.The grain size increases from 35-40μm in the billets made by the DCC to about 100-120μm in the billets by the SMC.The aggregation of Mg12Nd usually found at the triple joints of grain boundaries in the billets prepared by SMC while is not observable from the billets by DCC.The tensile strengths and elongations of the billets are 195.2 MPa and 15.5% by DCC,and 162.5 MPa and 3.2% by SMC,respectively.The tensile strength of the alloy by DCC is remarkably enhanced by T6 heat treatment,which reached 308.5 MPa.Fracture surfaces of NZ30K alloy have been characterized as intergranular fracture by SMC and quasi-cleavage fracture by DCC,respectively.

Numerical simulation for macrosegregation in direct-chill casting of 2024 aluminum alloy with an extended continuum mixture model

An extended continuum mixture model for macrosegregation is applied to predicting Cu and Mg segregation in large-size ingot of 2024 aluminum alloy during direct chill casting（DC）. A microsegregation model using the approximate phase diagram data was coupled with macroscopic transport equations for macrosegregation profiles. Then, the impacts of transport mechanisms on the formation of macrosegregation were discussed. It is found that copper and magnesium have a similar segregation configuration from the billet center to surface. Negative segregation is observed in the centerline and subsurface, whereas positive segregation is obtained in the surface and somewhat underestimated positive segregation in the middle radius. Further, the discrepancy between the predicted and experimental results was discussed in detail. The results show that the magnesium to some extent alleviates the copper segregation in ternary alloy, compared with that in binary alloy. The predicted results show good agreement with measured experimental data obtained from literatures.

Effect of casting speed on floating grains and macrosegregation ofdirect-chill cast 2024 alloy with intensive melt shearing

The ingot was prepared by direct-chill(DC)casting technology with different casting speeds under the influence of intensive melt shearing to explore the effect of casting speed and intensive melt shearing on the floating grains and negative centerline segregation.The results indicate that the application of intensive melt shearing in DC casting process can distribute the floating grains uniformly,reduce the area fraction of the floating grains,alleviate the negative centerline segregation,and improve the uniformity of temperature field in the sump.It is also suggested that under the influence of intensive melt shearing,the casting speed plays a crucial role in the amounts and distribution of floating grains.At low casting speed,the intensive melt shearing can significantly reduce the area fraction of the floating grains and distribute them uniformly throughout the ingot.However,this effect gradually disappears with the increase of casting speed.

Macro-physical field of large diameter magnesium alloy billet electromagnetic direct-chill casting:A comparative study

A comprehensive two-dimensional axisymmetric mathematical model that couples transient electromagnetic force with fluid flow,heat transfer,and solidification was established to describe the interaction of multiphysics field during DC casting.The melt flow,heat transfer,and solidification characteristics under differential phase pulse magnetic field and differential phase low-frequency electromagnetic field(DP-PMF and DP-LFEF)were numerically investigated by means of numerical simulation during electromagnetic direct-chill(DC)casting of AZ31 alloy at the same casting conditions.The effects of differential phase electromagnetic fields on Lorentz forces distributions,melt flow,heat transfer,and liquid sump shape were discussed systematically.Based on measured current waveform,the results were compared with those obtained without magnetic field(MF)and under conventional pulse magnetic field(PMF)and low-frequency electromagnetic field(LFEF)under the same conditions.The results show that the application of magnetic fields can significantly change the solidification process of DC casting.Differential phase magnetic fields(DP-LFEF and DP-PMF)can effectively reduce the temperature of the melt in the liquid sump,and the shallower liquid sump depth can be obtained under the differential phase magnetic fields.A large velocity vibration amplitude and a lower temperature are available simultaneously under DP-PMF,resulting in more uniform temperature distribution.

Effects of casting process on microstructures and flow stress behavior of Mg-9Gd-3Y-1.5Zn-0.8Zr semi-continuous casting billets

Mg-9Gd-3Y-1.5Zn-0.8Zr alloys own high strength,good heat and corrosion resistance.However,it is difficult for the fabrication of large-scale billets,due to the poor deformation ability and strong hot-crack tendency.This work investigated the casting process on the microstructures and flow stress behaviors of the semi-continuous casting billets for the fabrication of large-scale Mg-9Gd-3Y-1.5Zn-0.8Zr billets.The casting process(electromagnetic intensity and casting speed)shows outstanding effects on the microstructures and flow stress behavior of the billets.The billets with the specific casting process(I=68 A,V=65 mm/min)exhibit uniform microstructures and good deformation uniformity.

Deformation and heat treatment ability of three-layer 6009/7050/6009 Al alloy clad slab prepared by direct-chill casting

Three-layer6009/7050/6009aluminum alloy clad slab was fabricated by an innovative direct-chill casting process.To study the response of the clad slab to plastic deformation and heat treatments,homogenization annealing,hot rolling,solution and aging were successively performed on the as-cast6009/7050/6009clad samples.The results revealed that excellent metallurgical bonding between7050alloy layer and6009alloy layer was achieved under optimal parameters.The clad ratio obviously decreased when the annealed sample was rolled to55%hot reduction level,and then changed slightly with further rolling.Furthermore,the content of rodlike Zn-rich phases increased significantly in7050alloy layer in the homogenized clad samples after rolling at55%,65%and75%hot reduction levels,and the higher level of hot reduction resulted in narrower diffusion layer.Subsequent solution and aging significantly improved the hardness in7050alloy layer,interfaces and6009alloy layers of the rolled samples except for the thin side for the75%hot reduction sample.

Effect of high-intensity ultrasonic field on process of semi-continuous casting for AZ80 magnesium alloy billets

Under the high-intensity ultrasonic field,AZ80 magnesium alloy was semi-continuously cast.The effects of ultrasonic intensity on the as-cast microstructures and mechanical properties were investigated.The results show that the microstructures of the alloy cast under high-intensity ultrasonic field are fine and uniform,and the grains are equiaxed,rose-shaped or globular with an average size of 257μm.High-intensity field significantly decreases the grain size,changes the morphologies of theβ-Mg17Al12 phases and reduces their area fraction.It is also shown that a proper increase in ultrasonic intensity is helpful to obtain fine,uniform and equiaxed as-cast microstructures.The optimum ultrasonic parameters are that frequency is 20 kHz and ultrasonic intensity is 1 368 W.The mechanical tests show that the mechanical properties of the as-cast AZ80 magnesium alloy billets cast under ultrasonic field are greatly improved,and with increasing the ultrasonic intensity,the mechanical properties of the entire alloy billets are much higher and more uniform than those of the alloy without ultrasonic field.

Effects of heat treatment on microstructure and mechanical properties of Mg-8Gd-3Y-0.5Zr(wt.%)alloy fabricated by semi-continuous casting

The microstucture, mechanical properties and fracture behaviors of semi-continuous cast Mg-8Gd- 3Y-0.5Zr （wt.%, GW83K） alloy after different heat treatments were investigated. Almost all the eutectic compounds were dissolved into the matrix and there was no evident grain growth after optimum solution treatment at 500 ~C for 4 h. Further ageing at low temperatures led to significant precipitation hardening, which strengthened the alloy. Peak-aged at 200℃, the alloy had the highest ultimate tensile strength （UTS） and lowest elongation at 395 MPa and 2.8%, respectively. When aged at 225℃ for 15 h, the alloy exhibited prominent mechanical performance with UTS and elongation of 363 MPa and 5.8 %, respectively. With regard to microstructure and tensile properties, the processes of 500℃, 4 h ＋ 225℃, 15 h are selected as the optimal heat treatment conditions. The alloy under different conditions shows different fracture behaviors： in the as-cast alloy, a quasi-cleavage pattern is observed; after solution treatment, the alloy exhibits a trans-granular quasi-cleavage fracture; after being peak-aged at 200℃ and 225℃, the fracture mode is a mixed mode of trans-granular and inter-granular fracture, in which the inter-granular mode is dominant in the alloy peak-aged at 200℃.

Microstructure and mechanical properties of AZ31 alloy ingot fabricated by semi-continuous casting

The AZ31 alloy ingot with diameter of 110 mm and length of 3500 mm was fabricated successfully. The compositions and microstructure morphologies of the ingot at different locations were performed, which indicated that the chemical composition distributed homogeneously through the whole alloy ingot and the average grain size increased from the surface to the center. The results of the EDS and element face-scanning illustrated that the eutectic compounds mainly consisted of fl-Mg17Al12 and a small amount of fl-Mgl7（AlZn）12. Furthermore, slight improvements of the strength and ductility were observed from the center to the surface along the axial direction of the alloy ingot, while both the strength and elongation to failure of the samples along the radial direction are higher than that along the axial direction. The fine grain strengthening was the main contributors to the strength of the as-casted AZ31 alloy.

Thermal-stress Simulation of Direct-chill Casting of AZ31 Magnesium Alloy Billets

Two-dimensional （2D） transient coupled finite element model was developed to compute the temperature and stress field in cast billets, so as to predict the defects of the I-type billets made from AZ31 magnesium alloy and find the causes and solutions for surface cracks and shrinkages during direct-chill （DC） casting process. Method of equivalent specific heat was used in the heat conduction equation. The boundary and initial conditions used for primary and secondary cooling were elucidated on the basis of the heat transfer during the solidification of the billet. The temperature and the thermal-stress fields were simulated with the thermal-structural coupled module of ANSYS software. The influences of casting parameters on the distributions of temperature and stress were studied, which helped optimize the parameters （at pouring temperature of 680 ℃, casting speed of 2 min/s, heat-transfer coefficient of the second cooling equals to 5 000 W/m^2.℃^-1）. The simulation results of thermal stress and strain fields reveal the formation mechanism of some casting defects, which is favourable for optimizing the casting parameters and obtain high quality billets. Some measures of controlling processes were taken to prevent the defects for direct-chill casting billets.

Effect of Middle-frequency Electromagnetic Field on the Semi-continuous Casting for ZK60 Billets

The semi-continuous casting of ZK60 magnesium alloy under different middle frequency electromagnetic field conditions was examined.Effects of middle frequency electromagnetic field on microstructure,precipitations and tensile properties are investigated.The results show that the microstructures of ZK60 magnesium alloy are refined and distribution uniformity of precipitations is observed after applying the middle frequency electromagnetic field.And the tensile properties of the billets produced by middle frequency electromagnetic field are increased.

Effect of Cooling Intensity and Position on Solidification in Semi-Continuous Casting of Copper

Cooling heat flux effect in both primary and secondary cooling zone has been studied in semi-continuous casting of copper billet. Sufficient cooling is essential to reduce casting defects and to get high productivity, however low rate of solidification is aimed in order to get coarser grain size and softer metal for less losses in extrusion. A three-dimensional numerical model has been developed including solidification behavior of copper through mushy zone. At steady state and constant casting speed, solid shell thickness is monitored during the reduction of cooling rate at mould region to avoid breaking out. Heat flux intensity at mould plays important role not only in the formation of solid shell thickness. But, pool length and mushy zone thickness can be significantly increased by decreasing primary cooling intensity. Increase intensity of secondary cooling zone for two particular cases of primary cooling is tested. First case is tested at mould inlet water temperature of 38°C, and second case at water temperature of 63°C. Results showed that the combination of increasing secondary cooling intensity and reduction of primary cooling intensity can increase pool length and mushy zone thickness. Also, it is shown that, secondary cooling intensity can be magnified by up to 1.5 times for cooling water temperature of 63°C to get pool length close to that of water temperature of 38°C.

Effects of Ce on microstructure of semi-continuously cast Mg-1.5Zn-0.2Zr magnesium alloy ingots

Mg-1.5Zn-0.2Zr-xCe (x=0, 0.1, 0.3, 0.5, mass fraction, %) alloys were prepared by conventional semi-continuous casting. The effect of rare earth Ce on the microstructure of Mg-1.5Zn-0.2Zr-xCe alloys was studied and the distribution of Ce was analyzed by optical microscopy (OM), X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results indicate that Ce element exists in the form of Mg12Ce phase and has an obvious refining effect on the microstructure of test alloys. As the Ce content increases, the grain size reduces, the grain boundaries turn thinner, and the distribution of Mg12Ce precipitates becomes more and more dispersed. The Mg-1.5Zn-0.2Zr alloy with 0.3%Ce has the best refinement effect. From center to periphery of the ingot, the amount of granular precipitates in the grain reduces. In longitudinal section of the ingot, some relative long columnar grains appear.

Inhomogeneity of microstructure and mechanical properties of a 500 mm diameter heavy section semi-continuous cast AZ61 magnesium alloy ingot

For the large magnesium alloy ingot, there is a considerable difference in cooling rate of different parts in the ingot, which leads to non-uniform distribution of the secondary phases, solute segregation and tensile properties. In the present research, an heavy AZ61 alloy ingot with a diameter of 500 mm was made by semi-continuous casting. The microstructure and mechanical properties at different positions along the radial direction of the large ingot were investigated by using an optical microscope(OM), a scanning electron microscope(SEM), an energy dispersive spectroscope(EDS), and a micro-hardness tester. The results indicate that the microstructure of the AZ61 ingot is non-uniform in different locations. It changes from equiaxed to columnar grains from the center to the edge; the average grain size gradually reduces from 1,005 μm to 763 μm, the secondary dendrite arm spacing reduces from 78 μm to 50 μm, and the Mg17(Al,Zn)12 phase is also refined. The micro-hardness value increases from 55.4 HV at the center to 72.5 HV at the edge of the ingot due to the microstructure differences, and the distribution of micro-hardness at the edge of the ingot is more uniform than that in the center. The tensile properties at room temperature show little difference from the center to the edge of the ingot except that the elongation at the edge is only 3.5%, much lower than that at other areas. The fracture mechanism is ductile fracture at the center and cleavage fracture at the edge of the ingot, and at the 1/2 radius of the ingot, a mixture of ductile and cleavage fracture is present.

Effect of ultrasonic power and casting speed on solidification structure of 7050 aluminum alloy ingot in ultrasonic field

With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-continuous casting were researched, and the effects of casting speed on solidification structure in ultrasonic field were also analyzed. The experiment and simulation results show that the solidification structure of the ingot is homogeneously distributed, and its grain size is obviously refined at ultrasonic power of 240 W. The average grain sizes, which can be seen from the Leica microscope, are less than 100 μm. When the casting speed is 45-50 mm/min, the best grain refinement is obtained.

As-cast structure of DC casting 7075 aluminum alloy obtained under dual-frequency electromagnetic field

We have experimentally determined the as-cast structures of semi-continuous casting 7075 aluminum alloy obtained in the pres-ence of dual-frequency electromagnetic field. Results suggest that the use of dual-frequency electromagnetic field during the semi-continuous casting process of 7075 aluminum alloy ingots reduces the thickness of the surface segregation layer, increases the height of the melt menis-cus, enhances the surface quality of the ingot, and changes the surface morphology of the melt pool. Moreover, low-frequency electromag-netic field was found to show the most obvious influence on improving the as-cast structure because of its high permeability in conductors.

Microstructure and mechanical properties of large-scale Mg-Gd-Y-Zn-Mn alloys prepared through semi-continuous casting

Large-scale Mg-8Gd-4Y-1Zn-Mn(wt.%)alloy ingot with a diameter of 315 mm and a length of 2410 mm was prepared through semi-continuous casting.Chemical composition,microstructure and mechanical properties at different locations of the samples with as-cast,T4 and T6 heat-treated states,respectively,were investigated.No obvious macro segregation has been detected in the high-quality alloy ingot.The main eutectic structures at all different locations are composed ofα-Mg,Mg3RE-type,Mg5RE-type and LPSO phases.At the edge of ingot,the unusual casting twins including 10-12 extension twins and 10-11 compression twins were observed due to the intensive internal stress.In T4 heat-treated alloy,the micro segregation was eliminated.The remained phases wereα-Mg and LPSO phase.Combined with the remarkable age-hardening response,T6 samples exhibits improved mechanical properties at ambient temperature,which derives from the dense prismaticβ'precipitates and profuse basalγ'precipitates.