Cold Metal Transfer （CMT） welding technique is a new welding technique introduced by Fronins company. CMT welding of nickel-based alloy with stainless steel was carried out using CuSi3 filler wire in this paper. Eff...Cold Metal Transfer （CMT） welding technique is a new welding technique introduced by Fronins company. CMT welding of nickel-based alloy with stainless steel was carried out using CuSi3 filler wire in this paper. Effects of welding parameters, including welding current, welding speed, etc, on weld surface appearance were tested. Microstructure and mechanical properties of CMT weld were studied. The results shaw that the thickness of interface reaction layer of the nickel- based alloy is 14. 3 μm, which is only 4. 33% of base material. The weld is made up of two phases, α-copper and iron-based solid solution. Rupture occurs initially at the welded seam near the edge of stainless steel in shear test. The maximum shear strength of the CuSi3 welded joint is 184. 9 MPa.展开更多
To quantify the nonuniform micromechanical performance of welded joint,the load-displacement curves by nanoindentation test were introduced to examine different zones including base metal,coarse grained heat affected ...To quantify the nonuniform micromechanical performance of welded joint,the load-displacement curves by nanoindentation test were introduced to examine different zones including base metal,coarse grained heat affected zone,partially melted zone,weld metal near the fusion boundary and weld metal center.The results showed that the strengthening effect of weld metal was more obvious than that of heat affected zone for nickel based welded joint and especially in coarse grained heat affected zone,the hardening resulted from overheating was not apparent.Nickel based weld metal with high content of alloying elements which were often segregated at interdendritic regions or precipitated in grain interior under nonequilibrium solidification contributed to the characteristics that differ from conventional low alloy steel welded joint.展开更多
针对厚度6 mm N06200镍基合金和S32168不锈钢手工TIG焊接试板,采用三种热处理工艺对不同状态下焊接接头的微观组织、力学性能、断口形貌及耐腐蚀性能进行分析对比。结果表明:N06200镍基合金与S32168不锈钢TIG焊接接头组织为等轴晶奥氏...针对厚度6 mm N06200镍基合金和S32168不锈钢手工TIG焊接试板,采用三种热处理工艺对不同状态下焊接接头的微观组织、力学性能、断口形貌及耐腐蚀性能进行分析对比。结果表明:N06200镍基合金与S32168不锈钢TIG焊接接头组织为等轴晶奥氏体和垂直于熔合线方向生长的树枝晶组成;1 050℃热处理后焊接接头的抗拉强度最高为736 MPa,与N06200母材强度接近,较未热处理的焊接接头的抗拉强度(675 MPa)提高了9.05%;未热处理和1050℃热处理后的焊接接头断裂方式都为韧性断裂,1 150℃热处理后的焊接接头断裂方式为韧性+脆性混合型断裂,焊缝区域硬度高于其他区域;界面组织为靠近N06200镍基合金侧的IMCs为NiFe和Ni_(2)Cr,靠近S32168不锈钢侧的IMCs为FeCr和Ni_(3)Fe;NiFe相晶粒的主要织构为<011>丝织构,Ni_(3)Fe相晶粒的取向较明显,为强烈的<111>丝织构组成。展开更多
Future steam turbines will use hollow structures so that the turbine inlet temperature can be increased to improve the thermal efficiency. These hollow structures are made of the nickel-base alloy Nicrofer 6025 HT and...Future steam turbines will use hollow structures so that the turbine inlet temperature can be increased to improve the thermal efficiency. These hollow structures are made of the nickel-base alloy Nicrofer 6025 HT and consist of a wire mesh between two cover sheets. The cover sheets can be joined to the wire mesh by capacitor discharge welding due to its extremely short welding duration. The goal of this research is to investigate suitable welding parameters so that the weld spots form in an optimum way to increase the tensile shear strength and reduce spattering. Tensile shear tests, three-point bending tests, and micrographs were used to judge the joint quality of structures made with various welding parameters. The results show that the best welds are obtained with a transmission ratio of 1：200, welding energy of 70% to 95%, and electrode force of 7 to 9 MPa.展开更多
A ductility-dip-cracking(DDC)-concentrated zone(DCZ) in a width of about 3 mm was observed adjacent to the AISI 316 L/52 Mw fusion boundary(FB) in 52 Mw. The morphology, microstructure, mechanical and thermal properti...A ductility-dip-cracking(DDC)-concentrated zone(DCZ) in a width of about 3 mm was observed adjacent to the AISI 316 L/52 Mw fusion boundary(FB) in 52 Mw. The morphology, microstructure, mechanical and thermal properties and corrosion behavior in simulated primary water of DDC/DCZ were investigated by scanning electron microscopy(SEM), transmission electron microscopy(TEM), 3 D X-ray tomography(XRT), 3 D atom probe(3 DAP), slow strain rate tensile(SSRT) testing and thermal dilatometry. The results indicate that DDCs are random-shaped and disc-like cavities with corrugated structure of inner surface and are parallel in groups along straight high-angle boundaries of columnar grains, ranging from micrometers to millimeters in size. Large-size M_(23)C_6 carbides dominate on the grain boundaries rather than MC(M=Nb, Ti), and thus the bonding effect of carbides is absent for the straight grain boundaries.The impurity segregation of O is confirmed for the inner surfaces of DDC. The oxide film formed on the inner surface of DDC(about 50 nm) is approximately twice as thick as that on the matrix(about 25 nm)in simulated primary water. The yield strength, tensile strength and elongation to fracture of 52 MwDCZ(400 MPa, 450 MPa and 20 %, respectively) are lower than those of 52 Mw-MZ(460 MPa, 550 MPa and 28 %, respectively). The intrinsic high-restraint weld structure, the additional stress/strain caused by the thermal expansion difference between AISI 316 L and 52 Mw as well as the detrimental carbide precipitation and the resulting grain boundary structure all add up to cause the occurrence of DCZ in the dissimilar metal weld.展开更多
文摘Cold Metal Transfer （CMT） welding technique is a new welding technique introduced by Fronins company. CMT welding of nickel-based alloy with stainless steel was carried out using CuSi3 filler wire in this paper. Effects of welding parameters, including welding current, welding speed, etc, on weld surface appearance were tested. Microstructure and mechanical properties of CMT weld were studied. The results shaw that the thickness of interface reaction layer of the nickel- based alloy is 14. 3 μm, which is only 4. 33% of base material. The weld is made up of two phases, α-copper and iron-based solid solution. Rupture occurs initially at the welded seam near the edge of stainless steel in shear test. The maximum shear strength of the CuSi3 welded joint is 184. 9 MPa.
基金supported by the Primary Research&Developement Plan of Jiangsu Province(BE2017168)
文摘To quantify the nonuniform micromechanical performance of welded joint,the load-displacement curves by nanoindentation test were introduced to examine different zones including base metal,coarse grained heat affected zone,partially melted zone,weld metal near the fusion boundary and weld metal center.The results showed that the strengthening effect of weld metal was more obvious than that of heat affected zone for nickel based welded joint and especially in coarse grained heat affected zone,the hardening resulted from overheating was not apparent.Nickel based weld metal with high content of alloying elements which were often segregated at interdendritic regions or precipitated in grain interior under nonequilibrium solidification contributed to the characteristics that differ from conventional low alloy steel welded joint.
基金Supported by the DAAD (German Academic Exchange Service) CSC (China Scholarship Council) on Tsinghua University/ RWTH Aachen Joint Master Program
文摘Future steam turbines will use hollow structures so that the turbine inlet temperature can be increased to improve the thermal efficiency. These hollow structures are made of the nickel-base alloy Nicrofer 6025 HT and consist of a wire mesh between two cover sheets. The cover sheets can be joined to the wire mesh by capacitor discharge welding due to its extremely short welding duration. The goal of this research is to investigate suitable welding parameters so that the weld spots form in an optimum way to increase the tensile shear strength and reduce spattering. Tensile shear tests, three-point bending tests, and micrographs were used to judge the joint quality of structures made with various welding parameters. The results show that the best welds are obtained with a transmission ratio of 1：200, welding energy of 70% to 95%, and electrode force of 7 to 9 MPa.
基金financially supported by the National Key Research and Development Program of China (2016YFE0105200)Key Research Program of Frontier Sciences,Chinese Academy of Sciences (QYZDY-SSW-JSC012)
文摘A ductility-dip-cracking(DDC)-concentrated zone(DCZ) in a width of about 3 mm was observed adjacent to the AISI 316 L/52 Mw fusion boundary(FB) in 52 Mw. The morphology, microstructure, mechanical and thermal properties and corrosion behavior in simulated primary water of DDC/DCZ were investigated by scanning electron microscopy(SEM), transmission electron microscopy(TEM), 3 D X-ray tomography(XRT), 3 D atom probe(3 DAP), slow strain rate tensile(SSRT) testing and thermal dilatometry. The results indicate that DDCs are random-shaped and disc-like cavities with corrugated structure of inner surface and are parallel in groups along straight high-angle boundaries of columnar grains, ranging from micrometers to millimeters in size. Large-size M_(23)C_6 carbides dominate on the grain boundaries rather than MC(M=Nb, Ti), and thus the bonding effect of carbides is absent for the straight grain boundaries.The impurity segregation of O is confirmed for the inner surfaces of DDC. The oxide film formed on the inner surface of DDC(about 50 nm) is approximately twice as thick as that on the matrix(about 25 nm)in simulated primary water. The yield strength, tensile strength and elongation to fracture of 52 MwDCZ(400 MPa, 450 MPa and 20 %, respectively) are lower than those of 52 Mw-MZ(460 MPa, 550 MPa and 28 %, respectively). The intrinsic high-restraint weld structure, the additional stress/strain caused by the thermal expansion difference between AISI 316 L and 52 Mw as well as the detrimental carbide precipitation and the resulting grain boundary structure all add up to cause the occurrence of DCZ in the dissimilar metal weld.