Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparin...Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparing the orientation distribution function （ODF） of the double rolled sample with that of the single rolled one. The double cold rolling texture is characterized by a higher γ-texture and a lower α-texture, and the { 111}〈112〉 component is improved remarkably. Based on the TEM observation and mechanical properties test, it is found that the reduction ratio assignment significantly affects the texture variation, as-annealing microstructures, and properties of the double cold rolled samples. These results may provide a theoretical guide for the industrial production of double cold rolled IF steel.展开更多
Two kinds of cold rolling experiments, single cold rolling and double cold rolling, were carried out on one titanium stabilized interstitial free (IF) steel that has been warm rolled at ferrite temperature. The main a...Two kinds of cold rolling experiments, single cold rolling and double cold rolling, were carried out on one titanium stabilized interstitial free (IF) steel that has been warm rolled at ferrite temperature. The main aim was to investigate the evolution of rolling and annealing textures from the well known behavior observed under single cold rolling condition to the less understood double cold rolling by using orientation distribution function (ODF). In the twice cold rolled samples, the annealing texture comprises only single {111}(110-112) r-fibre texture when it subjected to moderate reduction in the first round of rolling. Accordingly both the once cold rolled sample and the twice cold rolled sample with heavy reduction in the first round of rolling have much complex texture components. They are related to the formation of initial {111} subgrain and the priority growth of stable {111} nucleus.展开更多
The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. Wit...The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. With the aid of orientation distribution function (ODF) analysis, it was found that he main reason for good property is the counterbalance in intensity of the ideal texture component {111} < 011 > and {111} < 112 >.展开更多
文摘Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparing the orientation distribution function （ODF） of the double rolled sample with that of the single rolled one. The double cold rolling texture is characterized by a higher γ-texture and a lower α-texture, and the { 111}〈112〉 component is improved remarkably. Based on the TEM observation and mechanical properties test, it is found that the reduction ratio assignment significantly affects the texture variation, as-annealing microstructures, and properties of the double cold rolled samples. These results may provide a theoretical guide for the industrial production of double cold rolled IF steel.
文摘Two kinds of cold rolling experiments, single cold rolling and double cold rolling, were carried out on one titanium stabilized interstitial free (IF) steel that has been warm rolled at ferrite temperature. The main aim was to investigate the evolution of rolling and annealing textures from the well known behavior observed under single cold rolling condition to the less understood double cold rolling by using orientation distribution function (ODF). In the twice cold rolled samples, the annealing texture comprises only single {111}(110-112) r-fibre texture when it subjected to moderate reduction in the first round of rolling. Accordingly both the once cold rolled sample and the twice cold rolled sample with heavy reduction in the first round of rolling have much complex texture components. They are related to the formation of initial {111} subgrain and the priority growth of stable {111} nucleus.
基金This work was supported by the National Natural Science Foundation of China under Grant No.59995440 and by the State Ministry of Science and Technology of China, the High Technology Development Plan (863) Project No.2001AA332020.
文摘The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. With the aid of orientation distribution function (ODF) analysis, it was found that he main reason for good property is the counterbalance in intensity of the ideal texture component {111} < 011 > and {111} < 112 >.