We prepare a new type of patented biodegradable biomedical Mg-Nd-Zn-Zr(JDBM)alloy system and impose double continuously extrusion(DCE)processing.The lowest processing temperature is 250℃for JDBM-2.1Nd and 310℃for JD...We prepare a new type of patented biodegradable biomedical Mg-Nd-Zn-Zr(JDBM)alloy system and impose double continuously extrusion(DCE)processing.The lowest processing temperature is 250℃for JDBM-2.1Nd and 310℃for JDBM-2.8Nd,which increases with the Nd concentration.The highest yield strength of 541 MPa is achieved in JDBM-2.1 Nd samples when extruded at 250℃and the elongation is about 3.7%.Moreover,the alloy with a lower alloying element content can reach a higher yield strength while that with a higher alloying element content can reach a larger elongation after DCE processing.However,when extruded under the same conditions,the alloy with a higher alloying contents exhibits better tensile properties.展开更多
AZ31B magnesium alloy chips were recycled by three solid-state recycling processes including cold-pressing,hot-pressing followed by hot extrusion and double extrusion.Microstructure and mechanical properties of the re...AZ31B magnesium alloy chips were recycled by three solid-state recycling processes including cold-pressing,hot-pressing followed by hot extrusion and double extrusion.Microstructure and mechanical properties of the recycled specimens and reference specimens were compared.For the recycled specimen by cold-pressing,the grains are refined to a large extent during hot extrusion due to the presence of twins and high density dislocation.The recycled specimens by hot-pressing and double extrusion do not exhibit finer grain than that the recycled specimen by cold-pressing.Consequently,higher ultimate tensile strength of the recycled specimen by hot-pressing and double extrusion is not achieved.For hot pressing process,more compact billet lowers the porosity in recycled material,so elongation to failure of the recycled specimen increases.The recycled specimen fabricated by double extrusion process shows slightly higher elongation than the reference specimen.The second extrusion makes the oxides further crush and distribute more dispersedly,and minimizes porosity,which is responsible for the improved ductility.展开更多
基金support by the national key research and development plan(No.2016YFC1102100)the National Natural Science Founda-tion of China(Nos.51501110,51728202,11332013 and 51501115)+1 种基金the Natural Science Foundation of Shang-hai(15ZR1422600)the Shanghai Jiao Tong University Medical-engineering Cross Fund(No.YG2015MS66 and No.YG2014MS62).
文摘We prepare a new type of patented biodegradable biomedical Mg-Nd-Zn-Zr(JDBM)alloy system and impose double continuously extrusion(DCE)processing.The lowest processing temperature is 250℃for JDBM-2.1Nd and 310℃for JDBM-2.8Nd,which increases with the Nd concentration.The highest yield strength of 541 MPa is achieved in JDBM-2.1 Nd samples when extruded at 250℃and the elongation is about 3.7%.Moreover,the alloy with a lower alloying element content can reach a higher yield strength while that with a higher alloying element content can reach a larger elongation after DCE processing.However,when extruded under the same conditions,the alloy with a higher alloying contents exhibits better tensile properties.
基金Projects(50674038,50974048) supported by the National Natural Science Foundation of ChinaProject(11541347) supported by the Educational Office of Heilongjiang Province,China
文摘AZ31B magnesium alloy chips were recycled by three solid-state recycling processes including cold-pressing,hot-pressing followed by hot extrusion and double extrusion.Microstructure and mechanical properties of the recycled specimens and reference specimens were compared.For the recycled specimen by cold-pressing,the grains are refined to a large extent during hot extrusion due to the presence of twins and high density dislocation.The recycled specimens by hot-pressing and double extrusion do not exhibit finer grain than that the recycled specimen by cold-pressing.Consequently,higher ultimate tensile strength of the recycled specimen by hot-pressing and double extrusion is not achieved.For hot pressing process,more compact billet lowers the porosity in recycled material,so elongation to failure of the recycled specimen increases.The recycled specimen fabricated by double extrusion process shows slightly higher elongation than the reference specimen.The second extrusion makes the oxides further crush and distribute more dispersedly,and minimizes porosity,which is responsible for the improved ductility.