Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were ...Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were carried out after the thermal test. Thermally cycled microstructure and fracture surfaces were observed too. The results indicate that impact toughness of heat-affected zone （HAZ） at -50 ℃ is lower than that of parent metal with different wire spacing and welding speed. The microstracture of coarse-grains heat-affected zone （ CGHAZ ） is mainly made up of lath bainite with serious brittleness. The study also shows that a smaller energy input could be adopted to ensure the toughness of welded joints at the welding process in a common molten pool, while a higher energy input could be exerted to enhance welding efficieney at the welding process in two separate molten pools.展开更多
New transmission line equations are deduced applying Maxwell's equations in this paper. The conditions of the classical transmission line equations have been discussed, which is important to solve the EM problems ...New transmission line equations are deduced applying Maxwell's equations in this paper. The conditions of the classical transmission line equations have been discussed, which is important to solve the EM problems in high frequency case.展开更多
文摘Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were carried out after the thermal test. Thermally cycled microstructure and fracture surfaces were observed too. The results indicate that impact toughness of heat-affected zone （HAZ） at -50 ℃ is lower than that of parent metal with different wire spacing and welding speed. The microstracture of coarse-grains heat-affected zone （ CGHAZ ） is mainly made up of lath bainite with serious brittleness. The study also shows that a smaller energy input could be adopted to ensure the toughness of welded joints at the welding process in a common molten pool, while a higher energy input could be exerted to enhance welding efficieney at the welding process in two separate molten pools.
文摘New transmission line equations are deduced applying Maxwell's equations in this paper. The conditions of the classical transmission line equations have been discussed, which is important to solve the EM problems in high frequency case.