Cold metal transfer （CMT） welding of nickel-coated Q235 steel studs with 606l Al alloy was carried out using ER4043 as filler metal. The welding process was stable, and appearance of weld formed well without surface...Cold metal transfer （CMT） welding of nickel-coated Q235 steel studs with 606l Al alloy was carried out using ER4043 as filler metal. The welding process was stable, and appearance of weld formed well without surface defect under the parameters of welding current 121 A, welding voltage 15.4 V and welding speed 6 r/min. The microstructure of fiUer metal was analyzed by means of scanning electron microscopy. The filler metal and 6061 Al alloy were fused to form fusion welding interface, the fusion zone had a good bonding without any micro defect. The steel stud did not melt and brazing interface was formed between the filler metal and steel stud. Two different reaction layers existed in the brazing interface, the Fe2Al5 layer about 10 -12 p^m formed near the steel stud side, and the other layer was mainly composed of FeAl3. Nickel-rich zone was formed in the root toe area of the fillet weld, which was mainly composed of Al3Ni2. The tensile tests showed that the maximum shearing strength of the joints was 129 MPa. The joint was brittle fractured in the intermetallic compound layer where plenty of FeAl3 were distributed continuously.展开更多
Through the investigation on traditional arc stud welding process, a new welding gun and its control system were developed in this paper. The stepping arc stud welding gun was mainly made by a stepping motor as actuat...Through the investigation on traditional arc stud welding process, a new welding gun and its control system were developed in this paper. The stepping arc stud welding gun was mainly made by a stepping motor as actuating unit and a screw-driven device as moving unit. A control system with a MCS-51 single-chip microcomputer as main control component was used to realize the new stud welding procedure. This new welding process with stepping stud welding gun is named as stepping arc stud welding. In the new welding process, the stud action can be looked as constituted by some micro steps. The setting and adjusting of the stepping arc welding gun behavior parameters are accomplished independently. It is indicated from the results of process tests and bending test that the stepping arc stud welding process is practicable.展开更多
The support plates including all of the inner hulls such as E grade steel, weld seams and SUS304L were considered to establish the optimal stud welding condition in LNG ship building. The stainless steel plate was esp...The support plates including all of the inner hulls such as E grade steel, weld seams and SUS304L were considered to establish the optimal stud welding condition in LNG ship building. The stainless steel plate was especially applied to the bracket on the liquid dome. The polished and etched surfaces of the welded stud and support plate were examined if the bead was properly formed. With the micrographic examination, the fusion boundary of metal weld zone formed by stud welding was analyzed to optimize the welding parameters. And also the analysis of the unacceptable welding faults such as cold and hot weld were performed. The mechanical tests such as tensile tests and bending tests were carried out to reveal any abnormal variation in the relationship of process parameters and the strength.展开更多
The applied conditions of stud welding on body of automobile, and the current waveforms and sequence control techniques which are set to meet the quality of stud welding in the car body, are introduced in this paper. ...The applied conditions of stud welding on body of automobile, and the current waveforms and sequence control techniques which are set to meet the quality of stud welding in the car body, are introduced in this paper. The realizing method of current waveforms and sequence control based on microprocessor are also discussed in detail. The waveforms of output welding current and voltage are measured. It is proved that the techniques including current waveforms & sequence control can successfully meet the demand of automobile stud welding.展开更多
基金supported by the Natural Science Foundation of Jiangsu Province(No.BK20131261)
文摘Cold metal transfer （CMT） welding of nickel-coated Q235 steel studs with 606l Al alloy was carried out using ER4043 as filler metal. The welding process was stable, and appearance of weld formed well without surface defect under the parameters of welding current 121 A, welding voltage 15.4 V and welding speed 6 r/min. The microstructure of fiUer metal was analyzed by means of scanning electron microscopy. The filler metal and 6061 Al alloy were fused to form fusion welding interface, the fusion zone had a good bonding without any micro defect. The steel stud did not melt and brazing interface was formed between the filler metal and steel stud. Two different reaction layers existed in the brazing interface, the Fe2Al5 layer about 10 -12 p^m formed near the steel stud side, and the other layer was mainly composed of FeAl3. Nickel-rich zone was formed in the root toe area of the fillet weld, which was mainly composed of Al3Ni2. The tensile tests showed that the maximum shearing strength of the joints was 129 MPa. The joint was brittle fractured in the intermetallic compound layer where plenty of FeAl3 were distributed continuously.
文摘Through the investigation on traditional arc stud welding process, a new welding gun and its control system were developed in this paper. The stepping arc stud welding gun was mainly made by a stepping motor as actuating unit and a screw-driven device as moving unit. A control system with a MCS-51 single-chip microcomputer as main control component was used to realize the new stud welding procedure. This new welding process with stepping stud welding gun is named as stepping arc stud welding. In the new welding process, the stud action can be looked as constituted by some micro steps. The setting and adjusting of the stepping arc welding gun behavior parameters are accomplished independently. It is indicated from the results of process tests and bending test that the stepping arc stud welding process is practicable.
文摘The support plates including all of the inner hulls such as E grade steel, weld seams and SUS304L were considered to establish the optimal stud welding condition in LNG ship building. The stainless steel plate was especially applied to the bracket on the liquid dome. The polished and etched surfaces of the welded stud and support plate were examined if the bead was properly formed. With the micrographic examination, the fusion boundary of metal weld zone formed by stud welding was analyzed to optimize the welding parameters. And also the analysis of the unacceptable welding faults such as cold and hot weld were performed. The mechanical tests such as tensile tests and bending tests were carried out to reveal any abnormal variation in the relationship of process parameters and the strength.
文摘The applied conditions of stud welding on body of automobile, and the current waveforms and sequence control techniques which are set to meet the quality of stud welding in the car body, are introduced in this paper. The realizing method of current waveforms and sequence control based on microprocessor are also discussed in detail. The waveforms of output welding current and voltage are measured. It is proved that the techniques including current waveforms & sequence control can successfully meet the demand of automobile stud welding.