In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,Si...In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.展开更多
The mechanical force borne by the lintel and“brackets”in the inclined channel area of CDQ and the thermal stress generated by the top-down temperature gradient were simulated by ANSYS software.The following conclusi...The mechanical force borne by the lintel and“brackets”in the inclined channel area of CDQ and the thermal stress generated by the top-down temperature gradient were simulated by ANSYS software.The following conclusions are drawn.(1)The mechanical force has very mild effect on the damage of the“brackets”.(2)The temperature gradient caused by the uneven temperature distribution of CDQ oven is the key factor affecting the“bracket”damage.The different expansion of refractory materials in various parts results in the thermal stress concentration which tears the“brackets”.(3)The structure adjustment of the“brackets”has very little effect on the thermal stress distribution.(4)The multi-phase nitride bonded silicon carbide for CDQ can effectively alleviate the stress concentration at the“brackets”,realizing the long-life and stable operation.展开更多
文摘In order to prolong the service life of the cooling zone of large scale coke dry quenching ovens,six kinds possible refractories for the cooling zone of large scale coke dry quenching ovens： SiC containing brick A,SiC containing brick B,mullite-andalusite brick,spinel containing brick,zirconia containing brick,corundum-mullite brick and grade B mullite brick,were analyzed in properties. It is found that the cooling zone lining adopting SiC containing bricks or mullite-andalusite bricks has much longer service life. Based on this,a new type of wear resistant brick was developed. The brick has a compressive strength of 135 MPa,a wear loss of 2. 10cm^3（only a quarter of that of the grade B mullite brick）,and a higher bulk density than the grade B mullite brick. The application of the brick in a 140t·h^（-1）coke dry quenching oven showed that it performed better than the grade B mullite brick. The cooling zone adopting the new bricks has a lower coke discharging temperature,which is beneficial to the enhancement of heat recovery efficiency and steam power generation.
文摘The mechanical force borne by the lintel and“brackets”in the inclined channel area of CDQ and the thermal stress generated by the top-down temperature gradient were simulated by ANSYS software.The following conclusions are drawn.(1)The mechanical force has very mild effect on the damage of the“brackets”.(2)The temperature gradient caused by the uneven temperature distribution of CDQ oven is the key factor affecting the“bracket”damage.The different expansion of refractory materials in various parts results in the thermal stress concentration which tears the“brackets”.(3)The structure adjustment of the“brackets”has very little effect on the thermal stress distribution.(4)The multi-phase nitride bonded silicon carbide for CDQ can effectively alleviate the stress concentration at the“brackets”,realizing the long-life and stable operation.
